Preparation method for fast producing copper-chromium contact material

A copper-chromium contact, fast technology, applied in the direction of metal processing equipment, electrical components, circuits, etc., can solve the problems of complicated procedures, multiple equipment, long cycle, etc., and achieve simplified preparation process, short sintering time and high density Effect

Inactive Publication Date: 2020-05-12
四川中坚环境监测服务有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can be seen from the process of preparing the copper-chromium contact material that after the powder mixing is completed, the steps of cold isostatic pressing, vacuum sheathing, heating, and hot extrusion are required to obtain the copper-chromium contact material, and , each of the above-mentioned steps includes complicated procedures. Such a production process not only has a long cycle and consumes a lot of energy, but also requires a variety of equipment and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The preparation method of quick production copper-chromium contact material of the present invention, it comprises the following concrete steps:

[0020] 1) Powder mixing: Add binder to the mixed powder of chromium powder and copper powder and mix evenly; the particle size of the chromium powder is 10-30 μm, and the particle size of the copper powder is 0.8-10 μm;

[0021] 2) Sieve and disperse: sieve the mixed powder processed in step 1 through a sieve and put it in a container to disperse and dry;

[0022] 3) Pre-sintering: Pour the mixed powder obtained in step 2 into a graphite mold, and mold it under a pressure of 3 tons / cm2, and set the temperature at 700°C during molding to obtain a molded product, which is placed in a spark plasma sintering furnace to vacuumize And pressurize, when the pressure reaches 20MPa, a pulsed direct current is applied and the temperature is raised to 1000°C, and after holding for 2.5 minutes, the pre-sintered porous sintered product is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method for fast producing a copper-chromium contact material. The method comprises the following specific steps that 1) powder mixing is performed, specifically,an adhesive agent is added into mixed powder of chromium powder and copper powder and mixed uniformly; 2) sieving and dispersing are performed, specifically, mixed powder obtained through treatment inthe first step is arranged in a container for dispersing and airing after being sieved by means of a sieving net; 3) presintering is performed, specifically, mixed powder obtained in the second stepis poured into a graphite die, and die pressing is performed under the pressure of 1-3.8 ton / cm2; 4) secondary sintering is performed, specifically, a porous sintering product obtained in the third step is continuously placed in a discharge plasma sintering furnace for vaccumizing and pressurizing; and 5) heat aftertreatment is performed, specifically, heat preservation is performed in vacuum or inert gas protection. According to the preparation method provided by the invention, the chromium powder and the copper powder are directly sintered after being mixed, and accordingly, the copper-chromium contact material is obtained; and compared with a copper-chromium contact material manufactured through the steps of powder mixing, isostatic cool pressing, vacuum bagging, heating and hot extrusion in the prior art, the preparation method provided by the invention involves effective simplifying of a preparation process, and the preparation process is completed without excessive equipment andcomplex technologies.

Description

technical field [0001] The invention relates to the technical field of material preparation, in particular to a preparation method for rapidly producing copper-chromium contact materials. Background technique [0002] Contact materials are widely used in automatic switches, large-capacity circuit breakers, molded case circuit breakers and other switches. The preparation method of the existing high-performance copper-chromium contact material usually includes the following steps: 1) raw material selection: select 50-300 micron electrolytic chromium powder or thermite reduced chromium powder and 300 micron electrolytic copper powder or atomized Copper powder; 2) Powder mixing: according to the weight ratio of Cu powder: Cr powder = 9:1 ~ 5:5, and ball milling according to the weight ratio of Cu powder and Cr powder: copper ball = 1:1 Mix the powder for 3-10 hours; 3) Cold isostatic pressing: Put the mixed powder into the rubber sleeve and cold isostatic press it into a bar, t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F3/105B22F1/00B22F3/24C22C1/04C22C9/00H01H11/04
CPCB22F3/105B22F3/1017B22F3/24C22C1/0425C22C9/00H01H11/048B22F2003/248B22F1/10
Inventor 符小平
Owner 四川中坚环境监测服务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products