Isolation material, preparation method and applications thereof

A technology of isolation materials and isolation agents, which is applied in the direction of synthetic cellulose/non-cellulose material pulp/paper, textiles and papermaking, and fiber raw material processing, which can solve the problems of not producing a large amount of gas, achieve good isolation effect, and evenly distribute , the effect of high content of release agent

Active Publication Date: 2020-05-12
CHINA NAT PULP & PAPER RES INST CO LTD +1
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the release agent mixed in the stainless steel layer cannot produce a large amount of gas, especially oxygen, when it is hot-rolled and pyrolyzed. It is necessary to limit the content of additives in the composite insulation material, which sets a limit for the production of insulation materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Isolation material, preparation method and applications thereof
  • Isolation material, preparation method and applications thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0046] The present invention also provides a preparation method for the isolation material of the above-mentioned technical solution, comprising the following steps:

[0047] Provide mixed fiber dissolving liquid;

[0048] Mixing the mixed fiber disentangling liquid, release agent and latex to obtain the first mixture;

[0049] mixing the first mixture, flocculant and defoamer to obtain a second mixture;

[0050] diluting the second mixture to obtain a slurry;

[0051] Papermaking is performed on the slurry to obtain the insulating material.

[0052] In the present invention, the components in the preparation method are consistent with the components of the isolation material in the above technical solution, and will not be repeated here.

[0053] The invention provides a mixed fiber dissolving liquid. In the present invention, the mass concentration of the mixed fiber disintegrating liquid is preferably 0.5-2%, more preferably 0.7-1.7%, and still more preferably 1-1.5%. In...

Embodiment 1

[0061] In terms of parts by mass, the isolation material components are:

[0062] 78.1 parts of release agent, obtained by mixing 325 mesh magnesium oxide and 800 mesh magnesium oxide according to the mass ratio of 1:2;

[0063] 6.3 parts of mixed fiber, obtained by mixing coniferous wood fiber and glass wool at a mass ratio of 7:5;

[0064] 14.7 parts of latex, obtained by mixing styrene-butadiene latex and nitrile latex at a mass ratio of 4:3;

[0065] 0.1 part of flocculant, obtained by mixing polyaluminum chloride (PAC) and cationic polyacrylamide (CPAM) at a mass ratio of 1:1;

[0066] 0.05 part of defoamer, JF-05B type silicone defoamer, purchased from Beijing Shi Aode Rui Technology Co., Ltd.

[0067] The preparation method of the isolation material is:

[0068] Using water as the diluent, dilute the latex to a mass concentration of 10%, dilute the flocculant to a mass concentration of 1%, and dilute the defoamer to a mass concentration of 1%, and set aside;

[0069...

Embodiment 2

[0076] In terms of parts by mass, the isolation material components are:

[0077] 76.6 parts of release agent, obtained by mixing 325 mesh magnesia and 800 mesh alumina according to the mass ratio of 1:2;

[0078] 7.5 parts of mixed fiber, obtained by mixing coniferous wood fiber and glass wool at a mass ratio of 1:1;

[0079] 15.3 parts of latex, obtained by mixing styrene-butadiene latex and nitrile latex at a mass ratio of 1:1;

[0080] 0.1 part of flocculant, obtained by mixing polyaluminum chloride (PAC) and cationic polyacrylamide (CPAM) according to the mass ratio of 2:1;

[0081] 0.05 part of defoamer, JF-05B type silicone defoamer, purchased from Beijing Shi Aode Rui Technology Co., Ltd.

[0082] The preparation method of the isolation material is:

[0083] Using water as the diluent, dilute the latex to a mass concentration of 10%, dilute the flocculant to a mass concentration of 1%, and dilute the defoamer to a mass concentration of 1%, and set aside;

[0084] A...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of composite materials, particularly relates to an isolation material, a preparation method and applications thereof, and provides an isolation material, which comprises the following components in parts by mass: 60-80 parts of an isolating agent, 6-15 parts of mixed fiber, 14-20 parts of latex, 0.02-0.1 part of a flocculating agent, and 0.01-0.1 part of an antifoaming agent. According to the invention, through the combined action of all the components, the isolation material is designed into a paper-based material, and the isolating agent is uniformly distributed in the isolation material, so that the uniform distribution of the isolating agent is met, and secondary pollution caused by the isolating agent in a dust form is fundamentally avoided; the experimental results show that the content of the isolating agent in the isolation material provided by the invention can reach 80 wt.%, so that the content of the isolating agent is high; and when the isolation material is directly spread between stainless steel, the isolation material is uniformly distributed, has no skin cracking phenomenon and has a good isolation effect.

Description

technical field [0001] The invention belongs to the technical field of composite materials, and in particular relates to an insulating material and its preparation method and application. Background technique [0002] Stainless steel-carbon steel clad plate (hereinafter collectively referred to as stainless steel clad plate) is a metal composite material with special properties that is made of stainless steel and carbon steel in a certain way. In the production process of stainless steel clad plate, it is necessary to follow the sequence of carbon steel-stainless steel-stainless steel-carbon steel, superimposed and welded together from top to bottom to form a composite billet before entering the hot rolling section. At high temperature, the contact surface of the stainless steel layer will be mutually Adhesion, subsequent inseparability. Therefore, it is necessary to add a release agent between the contact surfaces of the stainless steel layer of the composite billet. The ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21H11/00D21H13/40D21H17/67D21H17/37D21H21/02D21H21/12D21F11/02
CPCD21H11/00D21H13/40D21H17/675D21H17/37D21H21/12D21H21/02D21F11/02
Inventor 江骁雅王建国刘文杨春政陈雪峰毛宗久周德光王普孙启昆王华鹏孔艳荣王根矶徐永先杨冀王志勇郜丙兴袁立勇焦晓磊郭延爽郑同雷贾啸林王东董博伟曾玉杰王莹
Owner CHINA NAT PULP & PAPER RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com