A hyperbranched polymer and reaction technology, which is applied in the field of petroleum additives, can solve the problems that the demulsification efficiency needs to be improved, and achieve the effects of efficient demulsification, improved demulsification efficiency, and mild reaction conditions

Active Publication Date: 2020-05-19
湖北鑫城普瑞化学科技有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although the demulsifiers provided by the above methods have good demulsification efficiency, the demulsification of diesel oil emulsion by the above methods needs to be carried out at a relatively high temperature, and the demulsification efficiency still needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hyperbranched polymer as well as preparation method and application thereof
  • Hyperbranched polymer as well as preparation method and application thereof
  • Hyperbranched polymer as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0023] The concrete preparation method of this hyperbranched polymer comprises the steps:

[0024] (1) dissolving trimethyl citrate in a solvent, adding ethylenediamine thereto, and reacting at normal temperature to obtain intermediate 1;

[0025] (2) Add methyl acrylate and ethylenediamine to intermediate 1, react at room temperature, and then remove the solvent by distillation under reduced pressure to obtain intermediate 2;

[0026] (3) Under reduced pressure, the intermediate 2 was reacted with a gradient from 60 to 120° C. for 8 to 10 hours to obtain a reaction product. The reaction product was separated and dried to obtain the target product.

[0027] In some preferred embodiments of the present invention, the molar ratio of trimethyl citrate to ethylenediamine in step (1) is 1:3.

[0028] In some preferred embodiments of the present invention, the solvent used in step (1) is methanol.

[0029] In some preferred embodiments of the present invention, in step (1), trimet...

Embodiment 1

[0041]Embodiment 1 of the present invention provides a kind of preparation method of hyperbranched polymer, comprises the steps:

[0042] (1) 2.34g (0.01mol) of trimethyl citrate was dissolved in 30ml of methanol, then 1.8g (0.03mol) of ethylenediamine was added dropwise thereto, after mixing evenly, the mixed solution was placed at room temperature (25 °C) Stir the reaction at a rate of 300r / min for 24h to obtain intermediate 1;

[0043] (2) Add 9.02g (0.15mol) of ethylenediamine and 15.50g (0.18mol) of methyl acrylate to the intermediate 1 prepared in step (1), and continue stirring at a rate of 300r / min at room temperature Reaction for 24h, and then the solvent methanol was removed under reduced pressure to obtain intermediate 2;

[0044] (3) Under reduced pressure, react intermediate 2 at 60°C for 1h, 80°C for 1h, 100°C for 2h, and 120°C for 2h, naturally cool the obtained reaction product to room temperature, and add ether to the reaction product After stirring and prec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
demulsification efficiencyaaaaaaaaaa
transmittivityaaaaaaaaaa
demulsification efficiencyaaaaaaaaaa
Login to view more

Abstract

The invention discloses a hyperbranched polymer which is prepared taking trimethyl citrate as a center and an amino group as an end group. The weight-average molecular weight Mw of the hyperbranched polymer is 10757, and the PDI of the hyperbranched polymer is 5.09. The hyperbranched polymer is prepared by taking trimethyl citrate as the center, and amino group as the terminal group, contains a large number of hydrophilic groups, can remarkably reduce oil-water interfacial tension and improve demulsification efficiency, can be taken as a demulsifier to achieve efficient demulsification of oil-in-water emulsion at normal temperature condition; the demulsification efficiency of 50 mg / L of the hyperbranched polymer on diesel oil emulsion can reach 99.7% at normal temperature, the dosage of the hyperbranched polymer is small, and the demulsification efficiency is high. The invention also provides a preparation method of the hyperbranched polymer and application of the hyperbranched polymeras a demulsifier.

Description

technical field [0001] The invention belongs to the technical field of petroleum additives, and in particular relates to a hyperbranched polymer and its preparation method and application. Background technique [0002] The demulsification and dehydration of crude oil emulsion is an important link in the process of oil exploitation, gathering and transportation, and refining. The oil-water emulsion system is more complicated. Therefore, the demulsification research of oil-water emulsion is of great significance. Chemical demulsification is to achieve the purpose of demulsification by adding a certain amount of chemical agents to the emulsion. Demulsifiers can be classified into cationic, anionic and nonionic. Compared with ionic demulsifiers, nonionic demulsifiers are not easily affected by electrolytes because of their amphiphilic structure. Chemical demulsifier is the key to chemical demulsification. Traditional demulsifiers have problems such as low demulsification eff...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G83/00C10G33/04
CPCC08G83/005C10G33/04
Inventor 米远祝匡家哲叶泛张泽俊罗跃袁怀奎
Owner 湖北鑫城普瑞化学科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap