Environmental-friendly, antibacterial and bactericidal bed sheet and quilt cover capable of releasing negative oxygen ions

A technology of negative oxygen ions and negative oxygen ion powder, which is applied in the fields of bed sheets, textiles, papermaking, fiber treatment, etc., can solve the problems such as the lack of antibacterial and sterilizing functions of bed sheets and quilts, and achieve the effect of improving practical performance and improving technical effects

Pending Publication Date: 2020-05-19
IDEAL NEW MATERIAL TECH HONGKONG LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0011] The invention provides a green antibacterial and sterilizing bed sheet quilt cover that releases negative oxygen ions, which solves the technical problem that the bed sheet quilt cover lacks antibacterial and sterilizing functions in the prior art, and realizes that the bed sheet quilt cover can release negative oxygen for a long time while having the antibacterial and sterilizing function. Ions, the technical effect of improving practical performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environmental-friendly, antibacterial and bactericidal bed sheet and quilt cover capable of releasing negative oxygen ions
  • Environmental-friendly, antibacterial and bactericidal bed sheet and quilt cover capable of releasing negative oxygen ions

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047]S1: Place 28 parts of nano-zinc oxide powder, 1 part of selenium dioxide, 4 parts of potassium octatitanate, 0.6 part of gallium arsenide, and 1.5 parts of vermiculite powder in a stainless steel stirring tank for first-stage stirring to obtain a first intermediate product ; The time control of the first stage stirring is 30 minutes;

[0048] S2: place the first intermediate product in a high-temperature furnace for calcination to obtain a second intermediate product; the calcining time is controlled to be 8 hours;

[0049] S3: After the second intermediate product is cooled, the second intermediate product is placed in a stainless steel stirring tank, and then 19 parts of chlorophyll, 20 parts of catechins, and 10 parts of tea polyphenols are added to the stainless steel stirring tank for second-stage stirring ; The second stage stirring time is controlled at 35 minutes;

[0050] S4: adding 8 parts of the nano aerogel powder into the stainless steel stirring tank for t...

Embodiment 2

[0055] S1: Place 30 parts of nano-zinc oxide powder, 1 part of selenium dioxide, 5 parts of potassium octatitanate, 1 part of gallium arsenide, and 3 parts of vermiculite powder in a stainless steel stirring tank for first-stage stirring to obtain a first intermediate product ; The time control of the first stage stirring is 30 minutes;

[0056] S2: place the first intermediate product in a high-temperature furnace for calcination to obtain a second intermediate product; the calcining time is controlled to be 8 hours;

[0057] S3: After the second intermediate product is cooled, place the second intermediate product in a stainless steel stirring tank, and then add 20 parts of chlorophyll, 20 parts of catechin, and 10 parts of tea polyphenols into the stainless steel stirring tank for the second stage stirring ; The second stage stirring time is controlled at 30 minutes;

[0058] S4: adding 10 parts of the nano aerogel powder into the stainless steel stirring tank for the thir...

Embodiment 3

[0063] S1: Place 35 parts of nano-zinc oxide powder, 1.3 parts of selenium dioxide, 5.5 parts of potassium octatitanate, 1.5 parts of gallium arsenide, and 3.5 parts of vermiculite powder in a stainless steel stirring tank for first-stage stirring to obtain a first intermediate product ; The time control of the first stage stirring is 40 minutes;

[0064] S2: place the first intermediate product in a high-temperature furnace for calcination to obtain a second intermediate product; the calcining time is controlled to be 9 hours;

[0065] S3: After the second intermediate product is cooled, place the second intermediate product in a stainless steel stirring tank, and then add 21 parts of chlorophyll, 22 parts of catechin, and 11 parts of tea polyphenols into the stainless steel stirring tank for the second stage stirring ; The second stage stirring time is controlled at 35 minutes;

[0066] S4: adding 13 parts of the nano aerogel powder into the stainless steel stirring tank fo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an environmental-friendly, antibacterial and bactericidal bed sheet and quilt cover capable of releasing negative oxygen ions. The bed sheet and quilt cover is formed by dip-dyeing and drying modified dye. The modified dye consists of, by weight, 96-98.5 parts of water-based dye and 1.5-4 parts of negative oxygen ion powder, wherein the negative oxygen ion powder comprises, by weight, 15-28 parts of chlorophyll, 19-25 parts of catechin, 10-15 parts of tea polyphenol, 20-50 parts of nano zinc oxide powder, 0.6-2.5 parts of selenium dioxide, 3-10 parts of potassium octatitanate, 0.5-4 parts of gallium arsenide, 1-6 parts of vermiculite powder and 5-20 parts of nano aerogel powder. The environmental-friendly, antibacterial and bactericidal bed sheet and quilt cover capable of releasing the negative oxygen ions has the antibacterial and bactericidal functions and can release the negative oxygen ions for a long time, and the practical performance is improved.

Description

technical field [0001] The invention relates to the technical field of home textile products, in particular to a green antibacterial, sterilizing and releasing negative oxygen ion bed sheet and quilt cover. Background technique [0002] Negative oxygen ions are also known as air vitamins, vitamins, and longevity elements. Generally, the concentration of negative ions in the air in a closed room is 50-100 / cm 3 ;The general content is 700 / cm 3 The above (such as wilderness or park) can make people feel fresh and healthy. Therefore, negative ions are known as "air vitamins". Medical experts at home and abroad have clinically verified that moderate amounts of natural negative ions in the air have the following functions: [0003] (1), improve the oxygen conversion ability of the human body, accelerate the metabolism, make people feel comfortable and have a physiotherapy healing effect. Negative ions can activate various enzymes in the body; increase oxygen intake by 20% and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M13/503D06M13/152D06M11/44D06M11/52D06M11/46D06M11/00D06M11/79A47G9/02
CPCA47G9/02A47G9/0238A47G9/0261D06M11/00D06M11/44D06M11/46D06M11/52D06M11/79D06M13/152D06M13/503D06M16/00
Inventor 何新桥
Owner IDEAL NEW MATERIAL TECH HONGKONG LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com