A continuous casting mold and simulation test technology, applied in the direction of measuring devices, instruments, scientific instruments, etc., can solve the problems of weakening and difficulty in the degree of slag-gold reaction, and achieve the effect of reducing test losses and wide applicability of the process

Active Publication Date: 2020-05-29
宝武特种冶金有限公司
View PDF17 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the static test state, TiN floats up, TiN in the steel decreases in the later stage, and the degree of slag-gold reaction is weakened. However, in the actual continuous casting state, TiN in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Slag-metal reaction simulation test device and method for continuous casting crystallizer covering slag
  • Slag-metal reaction simulation test device and method for continuous casting crystallizer covering slag

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0050] Example 1

[0051] IF induction furnace layout as attached figure 1 , Use the graphite crucible 3 with a hole at the bottom, the molten steel capacity is 150kg; install the bottom gun 1, the selected bottom gun 1 has a diameter of 30mm, and is connected to Ar gas or nitrogen, argon and nitrogen can be switched freely; the top of the crucible covers the furnace top cover , The outer protective gas blowing pipe 15 of the cover plate, through the internal blowing hole slot, blows Ar gas into the furnace to form a protective atmosphere in the furnace;

[0052] According to the quality of smelting molten steel, steel blocks of appropriate size are added into graphite crucible 3 in batches. The steel block is energized to melt, the top cover and bottom gun 1 are injected with argon gas, and the induction furnace is turned on to increase the power to melt the steel block quickly;

[0053] After the molten steel is melted, take the original steel sample with a sample spoon. After s...

Example Embodiment

[0057] Example 2

[0058] IF induction furnace layout as attached figure 1 , Use the graphite crucible 3 with a hole at the bottom, the molten steel capacity is 200kg; install the bottom gun 1, the selected bottom gun 1 has a diameter of 40mm, and connects to Ar gas or nitrogen, argon and nitrogen can be switched freely; the top of the crucible covers the furnace top cover , The outer protective gas blowing pipe 15 of the cover plate, through the internal blowing hole slot, blows Ar gas into the furnace to form a protective atmosphere in the furnace;

[0059] According to the quality of molten steel, steel blocks of appropriate size are added to the crucible in batches. The steel block is energized to melt, the top cover and bottom gun 1 are injected with argon gas, and the induction furnace is turned on to increase the power to melt the steel block quickly;

[0060] After the molten steel is melted, take the original steel sample with a sample spoon. After sampling and temperatur...

Example Embodiment

[0064] Example 3

[0065] IF induction furnace layout as attached figure 1 , Use the graphite crucible 3 with the bottom hole, the molten steel capacity is 300kg; install the bottom gun 1, the selected bottom gun 1 has a diameter of 60mm, and is connected to Ar gas or nitrogen, argon and nitrogen can be switched freely; the top of the crucible covers the furnace top cover , The outer protective gas blowing pipe 15 of the cover plate, through the internal blowing hole slot, blows Ar gas into the furnace to form a protective atmosphere in the furnace;

[0066] According to the quality of molten steel, steel blocks of appropriate size are added to the crucible in batches. The steel block is energized to melt, the top cover and bottom gun 1 are injected with argon gas, and the induction furnace is turned on to increase the power to melt the steel block quickly;

[0067] After the molten steel is melted, take the original steel sample with a sample spoon. After sampling and temperature...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a slag-metal reaction simulation test device for continuous casting crystallizer covering slag. The device comprises a medium-frequency induction furnace and a bottom blowing device. The medium-frequency induction furnace comprises a graphite crucible, a furnace shell, an induction coil and a furnace cover. The furnace shell is arranged outside the graphite crucible, the induction coil is arranged between the graphite crucible and the furnace shell and arranged on the graphite crucible in a sleeving mode, and a feeding port is formed in the furnace cover and covers thetop of the graphite crucible; the bottom blowing device comprises a bottom gun and a protective gas source which are introduced into the bottom of the graphite crucible, and the bottom gun is externally connected to the protective gas source through a protective gas blowing pipe. The invention also discloses a simulation test method which can provide dynamic slag-metal reaction and can simulate continuous TiN precipitation and simulate the slag-metal reaction degree in production under the condition of continuous steel casting by switching a bottom blowing N method, thereby more accurately judging whether the crystallizer casting powder is applicable or not.

Description

technical field [0001] The invention relates to a slag-gold reaction simulation technology, and more specifically refers to a slag-gold reaction simulation test device and method for continuous casting mold flux, and is especially suitable for Al- and Ti-containing steel types. Background technique [0002] In the continuous casting process of molten steel, the continuous casting mold is an important part used to solidify and form the initial billet shell, and it is also the "heart" of the continuous casting process. In order to prevent the exposure and oxidation of the molten steel surface during continuous casting, the molten steel surface in the mold needs to be covered with mold slag. After the mold slag is added to the crystallizer, it absorbs the heat provided by the high-temperature molten steel, and quickly forms a liquid slag layer on the molten steel surface. When the mold slag near the liquid slag layer has not reached the melting temperature, it has been sintered...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N33/00G01N33/205
CPCG01N33/00
Inventor 陈家昶王大智张晨卢耀华
Owner 宝武特种冶金有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap