Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Forming process and device of a complex curved surface bulletproof insert

A bullet-proof insert and forming process technology, which is applied to the structure of armor plates, manufacturing tools, ceramic molding machines, etc., can solve the problems of uneven temperature distribution and difficulty in the production and control of bullet-proof inserts.

Active Publication Date: 2021-09-14
浙江吉成新材股份有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the pressureless sintering process of boron carbide ceramics, due to the need to meet the densification requirements, the product is placed on the sintering plate, which is placed inside the high-temperature sintering furnace for sintering deformation. There will be a process of volume shrinkage of about 20%, and the volume shrinkage will cause the shape of the curved surface of the product to change, and the process of shrinkage and shape change is all completed above 2200°C. In this ultra-high temperature environment, thermoelectric The measuring part of the pair will be damaged due to excessive temperature. At the same time, during the deformation process of the product, because the bulletproof plate is a complex curved shape, and the internal temperature of the sintering furnace is controlled by heating, heat preservation, cooling and cooling. Therefore, it often occurs that the temperature distribution in the airflow in contact between the bulletproof plate and the setter plate is uneven, which makes the production and control of the bulletproof plate very difficult. For this reason, we propose a complex curved surface Forming Technology and Device of Bulletproof Insert

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forming process and device of a complex curved surface bulletproof insert
  • Forming process and device of a complex curved surface bulletproof insert
  • Forming process and device of a complex curved surface bulletproof insert

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0029] see Figure 1-7 , the present invention provides a technical solution: a forming process and device for bulletproof inserts with complex curved surfaces, a forming process for bulletproof inserts with complex curved surfaces, comprising the following steps:

[0030] Step 1: After the boron carbide powder is granulated by pulping and spray drying, the surface of the powder particles is modified and a sintering aid is added to promote the activity between...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a forming process and device for bulletproof inserts with complex curved surfaces, which includes the following steps: Step 1: After boron carbide powder is granulated through pulping and spray drying, the surface of the powder particles is modified and a sintering aid is added, Promote the activity between boron carbide particles during the sintering process, and press it into a green body with a steel mold; Step 2: Put the prepared green body into the sintering furnace, vacuum sinter to 2200 degrees, and then keep it warm for 60 minutes, and then cool after sintering The forming process and device of the complex curved bulletproof inserts are based on the setter plate installed inside the sintering furnace, and the setter not only maintains a relatively uniform temperature of the airflow directly in contact with the complex curved bulletproof inserts and setters, At the same time, it can play the role of stably supporting the bulletproof insert with complex curved surface, and further improve the stability of the bulletproof insert when sintering inside the sintering furnace body.

Description

technical field [0001] The invention relates to the technical field of bulletproof board processing, in particular to a forming process and device for bulletproof boards with complex curved surfaces. Background technique [0002] The multi-curved bulletproof insert is a continuous and gradual complex curved surface. The product is composed of circular arcs with different curvatures at each position. The blanks in the compression molding stage in the pressureless sintering process require that the density of the blanks at each position should be basically equal. This requires that the weight of the powder distributed in each unit volume of the blank should be substantially equal before compression molding. [0003] In the actual application of the bulletproof board, in order to ensure the comfort of the user, its shape is composed of an ergonomically designed, continuous and gradually changing complex curved surface. In order to ensure the curved surface structure of the bull...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): F27B17/00F27D5/00F27D7/04B28B3/00B28B11/24F41H5/02
CPCB28B3/00B28B11/243F27B17/005F27D5/00F27D7/04F27D2007/045F27M2001/1504F27M2003/04F41H5/02
Inventor 尹邦进沈庚寿潘虎成
Owner 浙江吉成新材股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products