A kind of curing agent for solid waste treatment and its application

A technology of solid waste and curing agent, applied in application, fertilizer mixture, other chemical processes, etc., can solve the problems of difficult secondary curing, low curing rate, poor plasticity of cuttings, etc., and achieve energy saving and environmental protection Effect

Active Publication Date: 2022-03-08
新疆盛洁环境技术有限责任公司
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the high salinity of cuttings in the prior art, high COD value (chemical oxygen demand), low solidification rate, and long-term exposure of cuttings to pollute the environment, the plasticity of cuttings cured by existing cement is poor, and it is difficult to recycle The technical problem of secondary solidification, the present invention provides a curing agent for solid waste treatment and its use method. The separated rock debris and other wastes are added to the solid waste treatment developed in a targeted manner to realize on-site Harmless and resourceful, it has wide applicability in the field of petroleum solid waste treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of curing agent for solid waste treatment and its application
  • A kind of curing agent for solid waste treatment and its application
  • A kind of curing agent for solid waste treatment and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Embodiment 1: Preparation method of curing agent for solid waste treatment of the present invention

[0037] The preparation method of the curing agent for solid waste treatment provided by the present invention comprises the following steps: (1) accurately weighing each material used; (2) transporting the accurately weighed material to a sealed mixer; (3) mixing in a sealed Stirring in the machine; (4) forming the solid waste treatment solidifying agent and packing the finished product for later use.

[0038] In the present invention, stir in a sealed mixer for 2h-3h.

[0039] The preparation method of the curing agent for solid waste treatment of the present invention comprises weighing materials, adding materials, adding 10% water, and then mixing.

Embodiment 2

[0040] Embodiment 2: The method of using the curing agent for solid waste treatment of the present invention

[0041] The method for using the curing agent for solid waste treatment provided by the present invention comprises the following steps: (1) injecting waste cuttings into a pool and stirring evenly; (2) adding the solid waste treatment solidifying agent into the pool in the first step (1) ; (3) stirring the waste cuttings after adding the curing agent for solid waste treatment; (4) drying the stirred mixture to obtain a solidified product.

Embodiment 3

[0042] Embodiment 3: Solid waste treatment solidifying agent of the present invention

[0043] The invention provides a curing agent for solid waste treatment, comprising the following components: 75 tons of high-calcium fly ash; 10 tons of desulfurized gypsum; 7 tons of volcanic ash; 3 tons of bentonite; 3 tons of calcium chloride; 2 tons of sodium sulfate .

[0044] In the present invention, bentonite is nano-scale bentonite.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a curing agent for solid waste treatment, which comprises the following components in parts by mass: 60-90 parts of high-calcium fly ash; 6-14 parts of desulfurized gypsum; 5-9 parts of volcanic ash; bentonite 1-5 parts; calcium chloride 1-5 parts; sodium sulfate 1-3 parts. The curing agent for solid waste treatment provided by the present invention has strong water absorption, and can achieve the effect of solidifying oilfield cuttings at low cost, convenience and high efficiency when applied in practice; it not only effectively utilizes solid waste as a resource, Moreover, it also solves the problem of difficult solid waste treatment in major enterprises; the curing agent of the present invention can realize rapid solidification of mud, and can reduce large-capacity mud storage pools; plant heavy metal-absorbing vegetation and complete vegetation growth experiments, especially can be used in Anti-drought, restoration of severe saline-alkali land, etc.; it not only protects the ecological balance, improves the living environment, but also plays an effective role in promoting the government to achieve sustainable development goals.

Description

technical field [0001] The invention belongs to the field of solid waste treatment, in particular to water-based drilling waste cuttings. Background technique [0002] After the implementation of the new "Environmental Protection Law" in 2015, the treatment of drilling water-based solid-liquid waste has been put on the agenda. Oilfields have begun to test the technology of drilling water-based solid-liquid waste without landing. Government departments are also formulating relevant management measures to guide the drilling water Solid and liquid waste treatment reduction, emission reduction, harmless and resource utilization, to promote clean production in oilfields. Mud non-landing treatment and recycling technology collects waste drilling mud and cuttings while drilling on site, regenerates the separated waste mud, and reuses it for drilling to realize mud recycling. In the early stage, all drilling companies used traditional cement solidification method, the last thing pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09K17/08B09B3/25B09C1/08C09K101/00C09K109/00
CPCC09K17/08B09C1/08C09K2109/00C09K2101/00B09B3/25
Inventor 张宜敬屈艳夏瑞东聂春娇
Owner 新疆盛洁环境技术有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products