A method for preparing curing agent using gas-making slag-slag as raw material

A curing agent and gas-making technology, which is applied in cement production and other directions, can solve the problems of low material strength and cracking of building material products, and achieve the effects of improving mechanical strength, low production cost, resource utilization and environmental protection

Active Publication Date: 2021-11-12
HEBEI UNIVERSITY OF SCIENCE AND TECHNOLOGY
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The content of free calcium in gas-making slag is high, and the strength of the material is low when directly preparing building materials, and even the building materials may crack due to the hydration and expansion of free calcium oxide. Therefore, it is necessary to study the safe and efficient utilization method of gas-making slag Very necessary

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing curing agent using gas-making slag-slag as raw material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] 1) Mix 20 parts of gas-forming slag, 2 parts of carbide slag, 0.03 part of borax and 5 parts of water evenly to make a mixture, and activate the mixture at 40°C for 3 hours;

[0023] 2) After the activated mixture is dried, it is mixed evenly with 55 parts of dry slag, 10 parts of modified gypsum, 3 parts of clinker and 1 part of polysilicon waste residue to obtain a curing agent with a specific surface area of ​​544 m 2 / kg.

[0024] The strength of the curing agent is tested according to GB / T17671-1999 "Cement Mortar Strength Test Method (ISO Method)".

Embodiment 2

[0026] 1) Mix 25 parts of gas-forming slag, 3.5 parts of carbide slag, 0.06 part of borax and 5 parts of water evenly to make a mixture, and activate the mixture at 50°C for 2 hours;

[0027] 2) After the activated mixture is dried, it is mixed evenly with 40 parts of dry slag, 7 parts of modified gypsum, 5 parts of clinker and 10 parts of polysilicon waste residue to obtain a curing agent with a specific surface area of ​​462 m 2 / kg.

[0028] The strength of the curing agent is tested according to GB / T17671-1999 "Cement Mortar Strength Test Method (ISO Method)".

Embodiment 3

[0030] 1) Mix 30 parts of gas-forming slag, 5 parts of carbide slag, 0.08 part of borax and 5 parts of water evenly to make a mixture, and activate the mixture at 60°C for 1 hour;

[0031] 2) After the activated mixture is dried, it is evenly mixed with 48 parts of dry slag, 5 parts of modified gypsum, 1 part of clinker and 6 parts of polysilicon waste residue to obtain a curing agent with a specific surface area of ​​416 m 2 / kg.

[0032] The strength of the curing agent is tested according to GB / T17671-1999 "Cement Mortar Strength Test Method (ISO Method)".

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing a solidifying agent using gas-making slag-slag as a raw material, specifically: 1) Grinding gas-making slag, carbide slag and borax to 400m 2 / kg~450m 2 / kg, add water and mix evenly to make a mixture, activate the mixture at 40°C-60°C for 1h-3h; Grinding after mixing to obtain a curing agent. According to the characteristics of different materials, the invention prepares a higher-strength curing agent through the synergistic action of multiple materials, which can replace the application of underground mine filling and urban garbage curing. The method has the characteristics of simple process, low energy consumption, wide source of raw materials, high content of waste residue and low production cost, and has positive social and economic benefits for resource utilization of solid waste and environmental protection.

Description

technical field [0001] The invention relates to a method for preparing a curing agent, in particular to a method for preparing a curing agent by using gas-making slag-slag as a raw material. Background technique [0002] In recent years, with the country's structural adjustment of the cement industry's production capacity and the implementation of the production restriction policy, the price of cement products has continued to rise. In 2019, 32.5# cement reached 400 yuan / ton, and 42.5# cement exceeded 500 yuan / ton. The rise in cement prices has directly increased the production costs of related application companies, causing certain difficulties in production and operation, and has a greater impact on companies in low value-added fields such as underground mine backfilling and sludge solidification. [0003] Gas-making slag is a mixture of 25% lime powder and 75% anthracite coal powder mixed into balls in the production process of chemical companies, especially chemical fer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B7/24C04B7/21
CPCC04B7/21C04B7/24Y02P40/10
Inventor 王荣耕马田宇王霄汉潘鹏聪刘进丽苗俊仟马文文王丹王晓虹苏光亮孙雨
Owner HEBEI UNIVERSITY OF SCIENCE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com