Production method of high-cleanliness high-titanium low-carbon steel

A technology with high cleanliness and production methods, which is applied in the field of iron and steel metallurgy, can solve the problems of poor steel quality, low cleanliness, and low product quality, and achieve the effects of reducing burning loss, high cleanliness of molten steel, and good quality of cast slabs

Active Publication Date: 2020-08-07
CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD +1
View PDF21 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem solved by the invention is that when the titanium content is high, the steel quality becomes poor, the cleanliness is low, and the final product quality is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Converter into the furnace [S] 0.008%, converter tapping temperature 1670 ℃, end point carbon 0.05%, online argon blowing during tapping, tapping time 5.2 minutes, slag thickness 50mm, ladle headroom height 350mm, tapping 4 / 5 Start to add high-titanium and low-carbon steel refining slag 3.2kg / ton of steel into the ladle, blow argon to the ladle after tapping, the argon blowing flow rate is 80NL / min, and the argon blowing time is 6min. The composition is (CaO+BaO+SrO): 50%, MgO: 6%, SiO 2 : 3%, Al 2 o 3 : 25%, F - : 2%, TiO 2 : 12%

[0036] When 1 / 4 of the steel is tapped from the converter, high-carbon ferromanganese and aluminum ferromanganese are added to alloy the manganese, aluminum and other elements in the steel, and they are controlled to the composition of the finished product. When the RH treatment starts, 40TiFe is added at one time to make the titanium in the steel Control the composition of the finished product, and the vacuum cycle time after adding th...

Embodiment 2

[0043] Converter into furnace [S] 0.004%, converter tapping temperature 1690°C, end point carbon 0.08%, argon blowing on-line during tapping, tapping time 6.3 minutes, slag thickness 80mm, ladle headroom height 500mm, tapping 4 / 5 Start to add high-titanium and low-carbon steel refining slag 7kg / ton of steel into the ladle. After tapping, the ladle is blown with argon. For, (CaO+BaO+SrO): 42%, MgO: 5%, SiO 2 : 5%, Al 2 o 3 : 20%, F - : 3%, TiO 2 :twenty two%;

[0044] Low-carbon ferromanganese and aluminum shot were added to alloy the manganese, aluminum and other elements in the steel when the converter was tapping 2 / 3 of the steel, and controlled to the finished product composition; after RH treatment for 2 minutes, 80TiFe was added at one time to make the steel The medium titanium is controlled in the composition of the finished product, and the vacuum cycle time after adding the alloy is 15 minutes;

[0045] After the RH treatment, the molten steel is refined by argon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production method of high-cleanliness high-titanium low-carbon steel, and belongs to the technical field of ferrous metallurgy. The invention aims to solve the technical problems of poor steel quality, low cleanliness and low quality of a finally produced product when the titanium content is high. The invention provides a production method of high-cleanliness high-titanium low-carbon steel, and the production method comprises the following steps of carrying out converter-RH-argon blowing-slab continuous casting process flow production, carrying out converter end point control, carrying out converter tapping and carrying out RH step-by-step deoxidation alloying on molten steel; and high-titanium low-carbon steel refining slag is added into a steel ladle for slagging in the converter tapping process, the components of the steel ladle slag are controlled, casting powder is adopted in the pouring process, and the titanium content in the steel is 0.15%-0.8% by mass. According to the production method, smooth pouring of the high-titanium low-carbon steel can be achieved, auxiliary materials such as the steel ladle slag, a tundish covering agent and the castingpowder have the good capacity of absorbing nonmetallic inclusions, the performance can still be kept stable after a large number of inclusions are absorbed, the cleanliness of molten steel is high, and the quality of a poured casting blank is good.

Description

technical field [0001] The invention belongs to the technical field of iron and steel metallurgy, and in particular relates to a production method of high-cleanliness high-titanium low-carbon steel. Background technique [0002] Titanium is a good deoxidizer and an effective element for fixing nitrogen and carbon in steel. The application of titanium in steel is mainly based on microalloying. Adding a certain amount of titanium (0.01% to 0.03%) in steel can refine the structure of steel, improve the strength of steel, and improve the plasticity and impact toughness of steel. And so on. With the increase of titanium content in steel, the toughness, processability and wear resistance of the product are greatly improved, especially when Ti≥0.15% in steel, a large amount of micron-sized (1-5μm) TiC (≥80% ) and a small amount of TiN, the wear resistance of the product is more than 10 times that of titanium microalloyed steel, and the service life of the product is significantly...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C33/04C21C7/00C21C7/06C21C7/10B22D11/111B22D11/22B22D11/16C22C38/02C22C38/04C22C38/06C22C38/14
CPCC22C33/04C21C7/0006C21C7/06C21C7/10B22D11/111B22D11/225B22D11/16C22C38/02C22C38/04C22C38/06C22C38/002C22C38/14
Inventor 张敏曾建华尹晶晶吴国荣
Owner CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com