A kind of preparation method of environmental protection brick

An environmentally friendly brick and a certain amount of technology, applied in the field of environmentally friendly building materials, can solve the problems of high density, waste gas pollution, and can not fully meet the requirements of energy saving and environmental protection, and achieve the effect of light weight and high strength

Active Publication Date: 2021-11-30
张勇
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The reuse of waste resources is an effective way of green environmental protection, energy saving and emission reduction. With the increasingly severe pressure of national environmental protection, a lot of solid wastes such as biochemical sludge, Fenton oxidation sludge and fly ash have been produced. These solid wastes are often used to make bricks by sintering process. Although they have been reused, they have caused new exhaust gas pollution problems such as sulfur oxides and nitrogen oxides, and the single sludge made of bricks has caused the density of bricks to increase. Too large, can not fully meet the requirements of energy saving and environmental protection
On the other hand, some original ecological wastes, such as rice husks, sawdust, etc., are commonly disposed of by landfill, incineration, etc., and the resources are not fully utilized.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: A kind of environment-friendly brick is prepared according to the following steps.

[0016] Step 1: Pour 10g of rice husk, 5g of sawdust and 20g of rubber particles with a particle size of 1mm into 1000mL of sewage, add 150g of sludge produced by Fenton oxidation, 295g of biochemical sludge and 520g of fly ash, and stir for 8 hours. Obtain the mixture A of rice husk, sawdust, rubber particles, sludge produced by Fenton oxidation, biochemical sludge and fly ash;

[0017] Step 2: Transfer the mixture A to the hydrothermal reaction kettle, control the temperature at 140 o C, after reacting for 24 hours, cool naturally, filter off part of the supernatant, and obtain mixture B;

[0018] Step 3: Weigh 700g of mixture B, add 300mL of supernatant, and add 30g of polypropylene fiber and 270g of cement to it, stir and filter to obtain mixture C;

[0019] Step 4: Transfer the mixture C to the brick mold, press molding, steam 105 o C curing for 36 hours to produce ...

Embodiment 2

[0020] Embodiment 2: A kind of environmental protection brick is prepared according to the following steps.

[0021] Step 1: Pour 20g of rice husk, 10g of sawdust and 30g of rubber particles with a particle size of 2mm into 1000mL of sewage, add 200g of sludge produced by Fenton oxidation, 260g of biochemical sludge and 480g of fly ash, and stir for 12 hours. Obtain the mixture A of rice husk, sawdust, rubber particles, sludge produced by Fenton oxidation, biochemical sludge and fly ash;

[0022] Step 2: Transfer the mixture A to the hydrothermal reactor, control the temperature at 170 o C, after reacting for 48 hours, cool naturally, filter off part of the supernatant, and obtain mixture B;

[0023] Step 3: Weigh 600g of mixture B, add 400mL of supernatant, and add 50g of polypropylene fiber and 350g of cement to it, stir and filter to obtain mixture C;

[0024] Step 4: Transfer the mixture C to the brick mold, press molding, steam 120 o C curing for 48 hours, and an envir...

Embodiment 3

[0025] Embodiment 3: A kind of environmental protection brick is prepared according to the following steps.

[0026] Step 1: Pour 15g of rice husk, 7.5g of sawdust and 25g of rubber particles into 1000mL of sewage, add 175g of sludge produced by Fenton oxidation, 277.5g of biochemical sludge and 500g of fly ash, and stir for 10 hours to obtain rice husk A mixture of wood chips, rubber particles, sludge produced by Fenton oxidation, biochemical sludge and fly ash;

[0027] Step 2: Transfer the mixture A to the hydrothermal reaction kettle, control the temperature at 150 o C, after reacting for 36 hours, cool naturally, filter off part of the supernatant, and obtain mixture B;

[0028] Step 3: Weigh 650g of mixture B, add 350mL of supernatant, and add 40g of polypropylene fiber and 310g of cement to it, stir and filter to obtain mixture C;

[0029] Step 4: Transfer the mixture C to a brick mold, press molding, steam 110 o C curing for 42 hours to produce an environmentally fr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing an environmentally friendly brick. The technical proposal includes: pouring a certain amount of rice husk, sawdust and rubber particles into a certain amount of sewage, adding sludge produced by Fenton oxidation, biochemical sludge and powder Coal ash, stirring to obtain a mixture A of rice husk, sawdust, rubber particles, sludge produced by Fenton oxidation, biochemical sludge and fly ash, transfer the mixture A to a hydrothermal reactor, control the reaction temperature and time, and naturally Cool, filter off the supernatant to obtain mixture B and supernatant; weigh a certain amount of mixture B, add a certain amount of supernatant, and add polypropylene fiber and cement to it, stir and filter to obtain mixture C; The mixture C is transferred to a brick-making mould, which is subjected to compression molding and steam curing to obtain an environmentally friendly brick. The environmentally friendly brick includes porous carbide, iron oxide, harmless sludge, fly ash polypropylene fiber, and cement. It has the advantages of light weight and high strength, reaching MU25 grade.

Description

technical field [0001] The invention relates to the field of environment-friendly building materials, in particular to a preparation method of environment-friendly bricks. Background technique [0002] As a typical way of utilizing solid waste, environmentally friendly bricks have gained widespread attention. The reuse of waste resources is an effective way of green environmental protection, energy saving and emission reduction. With the increasingly severe pressure of national environmental protection, a lot of solid wastes such as biochemical sludge, Fenton oxidation sludge and fly ash have been produced. These solid wastes are often used to make bricks by sintering process. Although they have been reused, they have caused new exhaust gas pollution problems such as sulfur oxides and nitrogen oxides, and the single sludge made of bricks has caused the density of bricks to increase. If it is too large, it cannot fully meet the requirements of energy conservation and environ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/02
CPCC04B28/02C04B2111/00017C04B2201/50C04B18/248C04B18/26C04B18/22C04B18/0418C04B18/08C04B16/0633C04B40/024
Inventor 张勇张栋宁齐媛媛孙文鹏龚娟
Owner 张勇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products