A quantum dot film with high luminous efficiency and its preparation process

A high luminous efficiency, quantum dot film technology, applied in the direction of non-polymer adhesive additives, adhesive types, chemical instruments and methods, etc., can solve the problems of low yield rate, poor stability of quantum dot film, etc., to achieve improved Stability, optimize the effect of curing process

Active Publication Date: 2022-02-22
武汉华彩光电有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the above-mentioned technical deficiencies, propose a quantum dot film with high luminous efficiency and its preparation process, and solve the technical problems of poor stability and low yield of the quantum dot film in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A quantum dot film with high luminous efficiency and its preparation process
  • A quantum dot film with high luminous efficiency and its preparation process
  • A quantum dot film with high luminous efficiency and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] (1) Mix 100 parts by weight of adhesive, 2.5 parts by weight of titanium dioxide particles, 0.5 parts by weight of benzophenone, 0.25 parts by weight of red quantum dot solution, and 1.75 parts by weight of green quantum dot solution to form quantum dots Adhesive coating solution.

[0044] (2) A first barrier film and a second barrier film are provided, and the quantum dot adhesive layer coating liquid is coated between the first barrier film and the second barrier film to obtain a quantum dot film pre-product.

[0045] (3) The quantum dot film pre-product is subjected to the first-stage curing treatment, the second-stage curing treatment and the third-stage curing treatment in sequence to obtain the quantum dot film.

Embodiment 2

[0047] Except that the above-mentioned quantum dot film pre-product is subjected to the first-stage curing treatment and the second-stage curing treatment in sequence, the rest is the same as that of Example 1.

Embodiment 3

[0049] (1) 100 parts by weight of adhesive, 2.5 parts by weight of titanium dioxide particles, 0.5 parts by weight of benzophenone, 0.8 parts by weight of 1-hydroxycyclohexyl phenyl ketone, 0.25 parts by weight of red quantum dot solution 1.75 parts by weight of the green quantum dot solution are mixed and configured to form a quantum dot glue layer coating solution.

[0050] (2) A first barrier film and a second barrier film are provided, and the quantum dot adhesive layer coating liquid is coated between the first barrier film and the second barrier film to obtain a quantum dot film pre-product.

[0051] (3) The quantum dot film pre-product is subjected to the first-stage curing treatment, the second-stage curing treatment and the third-stage curing treatment in sequence to obtain the quantum dot film.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
wavelengthaaaaaaaaaa
wavelengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a quantum dot film with high luminous efficiency and a preparation process thereof. The preparation process of the quantum dot film with high luminous efficiency comprises the following steps: in parts by weight, providing 80-150 parts of adhesive, 1-10 parts of inorganic particles, 1-10 parts of quantum dot concentrate and 0.1-5 parts of photoinitiator Parts, mixed and configured as a quantum dot layer coating solution; the first barrier film and the second barrier film are provided, and the quantum dot layer coating solution is coated between the first barrier film and the second barrier film to obtain a quantum dot film Preform: performing multi-stage curing treatment on the quantum dot film preform to obtain the quantum dot film. The present invention adopts the matching method of photoinitiator and multi-stage curing process, optimizes the curing process of quantum dot film, improves the curing efficiency and reduces the impact on quantum dots, and finally improves the stability of the optical properties of the quantum dot film and the stability of the product production process. yield.

Description

technical field [0001] The invention relates to the technical field of quantum dot film preparation, in particular to a quantum dot film with high luminous efficiency and a preparation process thereof. Background technique [0002] With the development of semiconductor technology, various new materials are developing rapidly in various fields. As a typical existence of new nanomaterials, quantum dots play an increasingly important role in the field of optics and develop faster and faster [0003] Conventional LCD devices are equipped with a backlight unit that together converts the white backlight into the desired target display color. The colored light emitted by this traditional light-emitting device has limited performance and low luminous efficiency; while the traditional LCD device is equipped with a quantum dot film and combined with a blue light source, a display with high purity, high luminous efficiency, and high color gamut can be obtained. Improve the color disp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J175/04C09J163/00C09J133/12C09J125/06C09J11/04C09J11/06B32B7/12B32B37/12
CPCC09J175/04C09J163/00C09J133/12C09J125/06C09J11/04C09J11/06B32B7/12B32B37/1284C08K2003/2241B32B2037/1269
Inventor 肖蔓达黄瑜刘亮
Owner 武汉华彩光电有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com