Antibacterial barrier BOPET film and preparation method thereof
A barrier and film technology, applied in the field of antibacterial barrier BOPET film and its preparation, can solve the problems of poor optical performance, large film haze, low production efficiency, etc., and achieve excellent antibacterial effect, reduce haze, and improve barrier performance. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] Example 1
[0026] An antibacterial barrier BOPET film is composed of an upper surface layer, a core layer and a lower layer; its thickness is 15 μm, and the thickness of the upper and lower layers each account for 12% of the total thickness of the film.
[0027] The upper and lower layers are antibacterial layers, which are made of the following weight percentages of raw materials: 1.0% silver-loaded carbon nanotubes, 0.3% glass beads, and the balance is polyester chips; the average particle size of the glass beads is 1.5μm .
[0028] The core layer is a barrier layer, made of the following raw materials in parts by weight: EVOH 10%, nano-montmorillonite 0.8%, and the balance is polyester chips.
[0029] The present invention also provides a method for preparing the above-mentioned antibacterial barrier BOPET film, which includes the following steps:
[0030] S1. Mix EVOH, nano-montmorillonite, and polyester chips evenly, extrude them through a twin-screw extruder, dry them in ...
Example Embodiment
[0034] Example 2
[0035] An antibacterial barrier BOPET film is composed of an upper surface layer, a core layer and a lower layer; its thickness is 18 μm, and the thickness of the upper and lower layers each account for 13% of the total thickness of the film.
[0036] The upper and lower layers are antibacterial layers, which are made of the following weight percentages of raw materials: 1.1% silver-loaded carbon nanotubes, 0.35% glass beads, and the balance is polyester chips; the average particle size of the glass beads is 1.8μm .
[0037] The core layer is a barrier layer, which is made of the following raw materials in parts by weight: 12% EVOH, 0.6% nano-montmorillonite, and the balance is polyester chips.
[0038] The present invention also provides a method for preparing the above-mentioned antibacterial barrier BOPET film, which includes the following steps:
[0039] S1. Mix EVOH, nano-montmorillonite, and polyester chips uniformly, extrude them through a twin-screw extruder,...
Example Embodiment
[0043] Example 3
[0044] An antibacterial barrier BOPET film is composed of an upper surface layer, a core layer and a lower layer; its thickness is 20 μm, and the thickness of the upper and lower layers each account for 14% of the total thickness of the film.
[0045] The upper and lower layers are antibacterial layers, which are made of the following weight percentages of raw materials: 1.2% silver-loaded carbon nanotubes, 0.4% glass beads, and the balance is polyester chips; the average particle size of the glass beads is 2 μm.
[0046] The core layer is a barrier layer made of the following raw materials in parts by weight: 15% EVOH, 0.5% nano-montmorillonite, and the balance is polyester chips.
[0047] The present invention also provides a method for preparing the above-mentioned antibacterial barrier BOPET film, which includes the following steps:
[0048] S1. Mix EVOH, nano-montmorillonite, and polyester chips evenly, extrude them through a twin-screw extruder, and dry them in ...
PUM
Property | Measurement | Unit |
---|---|---|
The average particle size | aaaaa | aaaaa |
Stretch temperature | aaaaa | aaaaa |
The average particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap