Iron tailing unfired water permeable brick and preparation method thereof
A technology of iron tailings and permeable bricks, applied in ceramic products, other household appliances, sustainable waste treatment, etc., to achieve the effects of environmental protection, durability and wear resistance, and low energy consumption
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] Example 1 (Performance indicators must be added after each example: non-fired permeable bricks with good water permeability, the prepared unfired permeable bricks have a compressive strength of 30.5~35.5MPa, and a water permeability coefficient of 1.0×10 -2 ~4.5×10 -2 cm / s,)
[0021] An iron tailings unfired permeable brick, including the following raw materials:
[0022] 150kg of PO42.5R grade cement (134 parts), 500kg of iron tailings (446 parts), 300kg of 3-8mm grade gravel (268 parts), 50kg of desulfurized ash and 120kg of water (107 parts).
[0023] The production process of the above-mentioned permeable bricks includes the following steps:
[0024] S1. Raw material batching; import iron tailings, crushed stones, cement and desulfurized ash into the mixer according to 150kg of cement, 500kg of iron tailings, 300kg of crushed stones and 50kg of desulfurized ash, stir for 1min-5min under dry conditions, and then Slowly add 120kg of water under agitation, and the p...
Embodiment 2
[0033] A permeable brick comprising raw materials by weight of:
[0034] 200kg of PO42.5R grade cement, 500kg of iron tailings, 250kg of 3-8mm grade gravel, 50kg of desulfurized ash and 120kg of water.
[0035] The production process of the above-mentioned permeable bricks includes the following steps:
[0036] (1) Prepare various materials;
[0037] (2) Stirring of raw materials: import iron tailings, crushed stones, cement, and desulfurized ash into the agitator, stir for 2 minutes under dry conditions, and then slowly add water under agitation to ensure that no agglomeration occurs during the stirring process of the materials. Add water and stir for 5 minutes;
[0038] (3) Filling and molding: Calculate the weight of the required material, put it into the mold, and quickly pressurize it through the press, with a pressure of 10KN, so as to avoid vibration and slurry extraction during this process;
[0039] (4) Natural maintenance molding.
[0040] The prepared fire-free ...
Embodiment 3
[0042] A permeable brick comprising raw materials by weight of:
[0043] 150kg of PO42.5R grade cement, 550kg of iron tailings, 250kg of 3-8mm grade gravel, 50kg of desulfurized ash and 120kg of water.
[0044] The production process of the above-mentioned permeable bricks includes the following steps:
[0045] (1) Prepare various materials;
[0046] (2) Stirring of raw materials: import iron tailings, crushed stones, cement, and desulfurized ash into the agitator, stir for 2 minutes under dry conditions, and then slowly add water under agitation to ensure that no agglomeration occurs during the stirring process of the materials. Add water and stir for 5 minutes;
[0047] (3) Filling and molding: calculate the required material weight according to the bulk density, put it into the mold, and quickly pressurize it through the press, with a pressure of 10KN, to avoid vibration and extraction during this process;
[0048] (4) Natural maintenance molding.
[0049] The prepared ...
PUM
Property | Measurement | Unit |
---|---|---|
compressive strength | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
compressive strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap