High-performance water-resistant antifouling stone-like coating

A high-performance technology of real stone paint, applied in the field of coatings, can solve the problems of peeling off, the surface of real stone paint is easy to be polluted, and reduce the water and antifouling performance and water resistance of real stone paint, so as to achieve the effect of strong antifouling ability and colorful appearance

Inactive Publication Date: 2020-10-30
江苏晨光涂料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Traditional real stone paint uses cellulose-based thickeners. A large number of hydroxyl functional groups on the surface of the thickener greatly reduce the water and antifouling performance and water resistance of real stone paint (Guo Qingquan, Li Yongjin, Chen Huanqin. Stain resistance and Influencing factors[J]. Green Building, 2003, 19(5):15-18.), making the surface of real stone paint easily polluted and easy to fall off from the outer wall cavity in a humid environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] High-performance water-resistant and anti-fouling real stone paint, in parts by weight, includes the following components:

[0031] Silicone acrylic emulsion 30 parts

[0032] Natural colored sand 80 parts

[0033] Rock slices 3 servings

[0034] Coalescing aid 0.5 parts

[0035] Thickener 0.1 parts

[0036] Surfactant 0.05 part

[0037] Multi-functional additive 0.1 part

[0038] Antifouling agent 2 parts

[0039] 0.2 parts of defoamer

[0040] Hydrophobic agent 0.2 parts

[0041] 10 parts of water;

[0042] In the film-forming auxiliary agent, the mass ratio of diethylene glycol monobutyl ether to diethyl butyl ether acetate is 1:1;

[0043] Mix the above-mentioned raw materials, stir at room temperature at a speed of 600 rpm for 20 minutes, and mix evenly to obtain the real stone paint coating of the present invention.

[0044] Spray the real stone paint coating of the present invention on the mortar block, the spray pressure is 0.8Pa / cm 2 , the spray gun d...

Embodiment 2

[0051] High-performance water-resistant and anti-fouling real stone paint, in parts by weight, includes the following components:

[0052] Silicone acrylic emulsion 35 parts

[0053] Natural colored sand 100 parts

[0054] Rock slices 4 parts

[0055] Coalescing aid 1 part

[0056] Thickener 0.2 parts

[0057] Surfactant 0.1 parts

[0058] 0.2 parts of multifunctional additive

[0059] Antifouling agent 3 parts

[0060] 0.3 parts of defoamer

[0061] Hydrophobic agent 0.3 part

[0062] 13 parts of water;

[0063] In the film-forming auxiliary agent, the mass ratio of diethylene glycol monobutyl ether to diethyl butyl ether acetate is 1:2;

[0064] Mix the above-mentioned raw materials, stir at room temperature at a speed of 600 rpm for 20 minutes, and mix evenly to obtain the real stone paint coating of the present invention.

[0065] Spray the real stone paint coating of the present invention on the mortar block, the spray pressure is 0.8Pa / cm 2 , the spray gun diam...

Embodiment 3

[0072] High-performance water-resistant and anti-fouling real stone paint, in parts by weight, includes the following components:

[0073] Silicone acrylic emulsion 40 parts

[0074] Natural colored sand 120 parts

[0075] Rock slices 5 parts

[0076] Coalescing aid 1 part

[0077] Thickener 0.2 parts

[0078]Surfactant 0.1 parts

[0079] 0.2 parts of multifunctional additive

[0080] Antifouling agent 3 parts

[0081] 0.3 parts of defoamer

[0082] Hydrophobic agent 0.3 part

[0083] 15 parts of water;

[0084] In the film-forming auxiliary agent, the mass ratio of diethylene glycol monobutyl ether to diethyl butyl ether acetate is 1:1.5;

[0085] Mix the above-mentioned raw materials, stir at room temperature at a speed of 600 rpm for 20 minutes, and mix evenly to obtain the real stone paint coating of the present invention.

[0086] Spray the real stone paint coating of the present invention on the mortar block, and the spraying pressure is at 0.8Pa / cm 2 , the ca...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of coatings, in particular to a high-performance water-resistant antifouling stone-like coating. The traditional stone-like coating adopts a cellulose thickener, and a large number of hydroxyl functional groups on the surface of the thickener greatly reduce the water resistance, antifouling property and water resistance of the stone-like coating. In order to solve the problem, the invention provides the high-performance water-resistant antifouling stone-like coating, An added coalescing agent is a compound of diethylene glycol monomethyl ether and diethylene glycol butyl ether acetate, and the mass ratio of the diethylene glycol monobutyl ether to the diethylene glycol butyl ether acetate is 1: (1-2); an added multifunctional auxiliary agent isa mixture of 2-butylaminoethanol and 2-N-dibutylaminoethanol, and the mass ratio of the 2-butylaminoethanol to the 2-N-dibutylaminoethanol is 1: 1.5. Compared with the traditional stone-like coating,the high-performance water-resistant antifouling stone-like coating prepared by the method has better antifouling and water-resistant properties.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a high-performance water-resistant and anti-fouling real stone paint. Background technique [0002] At present, in order to achieve the effect of natural stone materials in buildings, natural stone materials are commonly used, but natural stone materials are limited by natural ore, and the color and pattern after decoration are not uniform, and they cannot be refurbished. It is difficult to mine and process, and the price is expensive; The load on the wall is heavy, so it is not suitable for the decoration of light buildings. In addition, the construction is difficult, especially the corners need special processing, the gaps between the stones need to be filled with sealant, and the overall waxing is required after the construction is completed. [0003] The spraying effect of real stone paint is solemn and elegant, which can fully show the rich texture of natural stone. The use...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/32C04B14/06C04B111/27
CPCC04B26/32C04B14/068C04B2111/00008C04B2111/27C04B2111/00155C04B2201/50
Inventor 薛亚波陈斌许红涛缪丽锋
Owner 江苏晨光涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap