Gum dipping glove free of latex components
A glove and rubber-dipping technology, which is applied in the field of latex-free rubber-dipped gloves, can solve the problems of low friction of rubber-dipped gloves, and achieve the effects of increasing service life, avoiding air bubbles, and improving quality
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0031] An embodiment of the present invention provides a latex-free rubber-dipped glove, which includes a glove fabric layer, a rubber-dipped layer, and a non-slip rubber particle layer.
[0032] The glove fabric layer is knitted from 30-50% cotton yarn, 30-50% nylon thread, and 10-20% low elastic yarn. The material of the dipping layer is an aqueous solution composed of isoprene rubber, sulfur, dispersant and accelerator. The ingredients in the dipping layer are calculated by weight as follows: 120 parts, 1-3 parts, 2-4 parts, 2-3 parts, the dispersant uses polyethylene wax, the accelerator uses triethylenediamine, and the anti-skid rubber particles The diameter is 0.2 ~ 0.5mm. The dispersant is a kind of surfactant with two opposite properties of lipophilicity and hydrophilicity in the molecule. It can uniformly disperse the solid and liquid particles of inorganic and organic pigments that are difficult to dissolve in liquid. , At the same time, it can also prevent the sedim...
Embodiment 2
[0034] Embodiments of the present invention provide a production process for latex-free rubber-dipped gloves, comprising the following steps:
[0035] S1 set of molds
[0036] Put the glove fabric layer on the hand mold, and the hand mold is cleaned in advance;
[0037] S2 dipping coagulant
[0038] Dip the glove fabric layer into the coagulant, drain it, and dry it at a low temperature at a temperature of 40-50°C for 30 minutes, then dry it at a high temperature at a temperature of 60-70°C until the glove fabric layer is completely dry ;
[0039] S3 Dip Latex
[0040] Immerse the dried glove fabric layer in S2 into latex, control the dipping time for another 5-10s, and drain, then perform drying treatment, the temperature is controlled at 20-30°C, and the dipping layer is viscous, stop dry;
[0041] S4 Adhesion of non-slip rubber particles
[0042] Spray the anti-slip rubber particles to the palm of the glove fabric layer and the fingers on the same side, control 15-30 ...
Embodiment 3
[0047] Embodiments of the present invention provide a production process for latex-free rubber-dipped gloves, comprising the following steps:
[0048] S1 set of molds
[0049] Put the glove fabric layer on the hand mold, and the hand mold is cleaned in advance;
[0050] S2 dipping coagulant
[0051] Dip the glove fabric layer into the coagulant, drain it, and dry it at a low temperature at a temperature of 40-50°C for 30 minutes, then dry it at a high temperature at a temperature of 60-70°C until the glove fabric layer is completely dry ;
[0052] S3 Dip Latex
[0053] Immerse the dried glove fabric layer in S2 into latex, control the dipping time for another 5-10s, and drain, then perform drying treatment, the temperature is controlled at 20-30°C, and the dipping layer is viscous, stop dry;
[0054] S4 Adhesion of non-slip rubber particles
[0055] Spray anti-slip rubber particles to the palm of the glove fabric layer and fingers on the same side, control 15-30 particle...