High-hydrophobicity fluorocarbon composition as well as preparation method and application thereof
A composition and hydrophobic technology, applied in antifouling/underwater coatings, coatings, paints containing biocide, etc., to achieve high hydrophobicity and good practical application value
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0051] In a second aspect of the present invention, there is provided a preparation method of the above-mentioned highly hydrophobic fluorocarbon composition. The preparation method includes: adding a dispersant to butyl acetate and stirring uniformly, adding a filler and an inorganic flame retardant to it and dispersing , Prepare filler dispersion;
[0052] Blending and grinding the filler dispersion with the fluorocarbon resin, and the mixture is sieved to obtain coating component A;
[0053] Mix and stir the coating component A with the curing agent.
[0054] Wherein, the mass ratio of the dispersant to butyl acetate is 1:200 to 800, and the stirring treatment time of the dispersant and butyl acetate is 5 to 20 minutes;
[0055] In order to enhance the uniformity of dispersion, after adding reinforcing filler and inorganic flame retardant, the dispersion is carried out by shearing ultrasonic dispersion, and the processing time is 20-60min;
[0056] Blending the filler dispersion wit...
Example Embodiment
[0068] Example 1
[0069] A highly hydrophobic fluorocarbon composition with excellent tracking resistance and flame-retardant properties, consisting of the following parts by weight:
[0070] 60 parts of fluorocarbon resin;
[0071] 20 parts of modified fumed nano-silica with a particle size of 20nm;
[0072] 60 parts of aluminum hydroxide, particle size of 20μm;
[0073] 0.2 parts of dispersant;
[0074] 12 parts of curing agent.
[0075] The use method of the above-mentioned highly hydrophobic fluorocarbon composition is:
[0076] The dispersant was added to 150 parts of butyl acetate, stirred for 10 minutes, and modified fumed nano-silica and aluminum hydroxide were added thereto, followed by shear ultrasonic dispersion for 30 minutes to prepare a filler dispersion. The filler dispersion is poured into a grinder and blended with the fluorocarbon resin for 4 hours, and the resulting mixture is sieved through a 350-mesh sieve to obtain paint component A. Before use, the component A and...
Example Embodiment
[0078] Example 2
[0079] A highly hydrophobic fluorocarbon composition with excellent tracking resistance and flame-retardant properties, consisting of the following parts by weight:
[0080] 60 parts of fluorocarbon resin;
[0081] 10 parts of modified fumed nano-silica with a particle size of 20nm;
[0082] 60 parts of aluminum hydroxide, particle size of 20μm;
[0083] 0.5 part of dispersant BYK163;
[0084] Hardener HDI trimer isocyanate 18 parts.
[0085] The above-mentioned paint usage method is:
[0086] The dispersant was added to 120 parts of butyl acetate, stirred for 10 minutes, and the modified fumed nano-silica and aluminum hydroxide were added, and sheared and ultrasonically dispersed for 50 minutes to prepare a filler dispersion. The filler dispersion was poured into a grinder and blended with the fluorocarbon resin for 5 hours, and the resulting mixture was sieved through a 350-mesh screen to obtain coating component A. Before use, the component A and the curing agent ar...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap