High-efficiency organic-inorganic composite filter material

A filter material and inorganic composite technology, applied in the direction of filtration separation, dispersed particle filtration, conjugated synthetic polymer artificial filament, etc., can solve problems such as poor filtration effect, achieve improved filtration adsorption effect, uniform pore distribution, and improved The effect of the adsorption effect

Inactive Publication Date: 2020-11-20
绍兴市梓昂新材料有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems in the prior art, the present invention provides a high-efficiency organic-inorganic composite filter material, which solves the problem of poor filtering effect in the prior art, and utilizes the insolubility of polyvinyl alcohol to form double-conjugated polymers, supplemented by tourmaline powder The negative ions and the oxygen storage characteristics of activated alumina form a negative oxygen ion system that does not absorb water, which greatly improves the filtration and adsorption effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A high-efficiency organic-inorganic composite filter material is made of negative ion fiber monofilament weaving and pressing.

[0026] The preparation method of described filter material is as follows:

[0027] Step 1, winding three negative ion monofilaments to form woven monofilaments, and weaving the woven monofilaments as warp and weft threads to form a woven net;

[0028] Step 2, put 10 braided nets into a closed environment and let it stand for 30 minutes, then extrude at a constant temperature for 20 minutes to obtain a prefabricated filter plate. The sealed environment is a mixed atmosphere of nitrogen and water vapor, and the volume ratio of nitrogen and water vapor is 5:2, constant temperature extrusion pressure is 3MPa, temperature is 110℃;

[0029] Step 3, hang the prefabricated filter plate in a muffle furnace for sintering at a constant temperature for 2 hours, put it into distilled water and cook for 10 minutes after cooling, take it out and dry it to o...

Embodiment 2

[0037] A high-efficiency organic-inorganic composite filter material is made of negative ion fiber monofilament weaving and pressing.

[0038] The preparation method of described filter material is as follows:

[0039] Step 1, winding 10 negative ion monofilaments to form woven monofilaments, and weaving the woven monofilaments as warp and weft threads to form a woven net;

[0040] Step 2, put 30 woven nets into a closed environment and let it stand for 60 minutes, then extrude at a constant temperature for 40 minutes to obtain a prefabricated filter plate. The sealed environment is a mixed atmosphere of nitrogen and water vapor, and the volume ratio of nitrogen and water vapor is 4:1, constant temperature extrusion pressure is 7MPa, temperature is 120℃;

[0041] Step 3, hang the prefabricated filter plate in a muffle furnace for sintering at a constant temperature for 5 hours, put it in distilled water for 20 minutes after cooling, and dry it to obtain the filter material. ...

Embodiment 3

[0049] A high-efficiency organic-inorganic composite filter material is made of negative ion fiber monofilament weaving and pressing.

[0050] The preparation method of described filter material is as follows:

[0051] Step 1, winding 6 negative ion monofilaments to form woven monofilaments, and weaving the woven monofilaments as warp and weft threads to form a woven net;

[0052] Step 2, put 20 woven nets into a closed environment and let stand for 560 minutes, then extrude at a constant temperature for 30 minutes to obtain a prefabricated filter plate. The sealed environment is a mixed atmosphere of nitrogen and water vapor, and the volume ratio of nitrogen and water vapor is 3:1, constant temperature extrusion pressure is 5MPa, temperature is 115℃;

[0053] Step 3, hang the prefabricated filter plate in a muffle furnace for sintering at a constant temperature for 4 hours, put it into distilled water and cook for 15 minutes after cooling, take it out and dry to obtain the f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of filtration, and relates to the field of air purification, and in particular to a high-efficiency organic-inorganic composite filter material. According to the high-efficiency organic-inorganic composite filter material, aluminum oxide is taken as an inorganic material, polyvinyl alcohol as an organic material and tourmaline as negative ion powder, and a specific preparation method is provided. According to the invention, the problem of poor filtering effect in the prior art is solved, a non-absorbent negative oxygen ion system is formed by utilizing the insolubility of a biconjugated polymer formed by conversion of polyvinyl alcohol and the oxygen storage characteristics of negative ions of tourmaline powder and activated aluminum oxide, and the filtering and adsorbing effects are greatly improved.

Description

technical field [0001] The invention belongs to the field of filtration, relates to the field of air purification, in particular to a high-efficiency organic-inorganic composite filter material. Background technique [0002] At present, the ventilation filter is mainly made of PP, PET and other fiber textiles. It has good acid and alkali resistance, corrosion resistance, low resistance, and can be cleaned repeatedly. The economy is relatively high. In addition, The long and short fibers and dust particles captured by it are easy to clean, the filtration efficiency is not affected by cleaning, and the impact resistance is very good. It is the product of choice for customers. The air conditioning filter has a concave-convex honeycomb structure, which can be widely used in sewage filtration systems and air filtration. It is easy to clean and replace many times, and has a long-lasting effect. Moreover, the air conditioner filter is easy to clean, which is recognized by the majo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01D39/20B01D39/16B01D46/00D01F8/10D01F8/02D01F1/10D01D5/12D04C1/02
CPCB01D39/16B01D39/2082B01D46/0001B01D46/0036D01D5/12D01F1/10D01F8/02D01F8/10D04C1/02
Inventor 朱盼盼蒋选兰王成
Owner 绍兴市梓昂新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com