Mortar and preparation method thereof

A mortar and steel slag powder technology, applied in sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of insufficient cement consumption, poor water retention, strong cement dependence, etc. Uniform stability, high strength effect

Active Publication Date: 2020-12-18
唐山中陶纪元工程设计有限公司
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The mortar in the prior art is mostly prepared with cement as the cementitious material. The strength of the mortar mainly depends on the cement grade and the amount of cement. If the grade of cement is too high, the insufficient amount of cement will lead to poor water retention, so the dependence on cement is strong.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mortar and preparation method thereof
  • Mortar and preparation method thereof
  • Mortar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of masonry mortar, comprises the raw material of following parts by weight:

[0036] 8 parts of steel slag powder, 2 parts of aggregate forming agent and 1.5 parts of water;

[0037] The steel slag powder comprises 4 parts by weight of 1mm steel slag powder, 2.67 parts of 150 μm steel slag powder and 1.33 parts of 100 μm steel slag powder;

[0038] The aggregate forming agent comprises the following components by weight:

[0039] 15 parts of alkali residue,

[0040] 35 parts of steel slag,

[0041] 3 parts of waste plaster mold,

[0042] 30 parts of cement clinker.

[0043] The preparation method of above-mentioned masonry mortar, comprises the following steps:

[0044] (1) get steel slag, grind, sort, obtain steel slag powder;

[0045] (2) Preparation of aggregate forming agent: get alkali slag, steel slag, waste gypsum mold, cementitious material respectively, pulverize, grind, sieve, obtain alkali slag powder, steel slag powder, waste gypsum mold powder ...

Embodiment 2

[0048] A kind of masonry mortar, comprises the raw material of following parts by weight:

[0049] 10 parts of steel slag powder, 5 parts of aggregate forming agent and 6 parts of water;

[0050] The steel slag powder comprises 5 parts by weight of 1mm steel slag powder, 3.33 parts of 150 μm steel slag powder and 1.67 parts of 100 μm steel slag powder;

[0051] The aggregate forming agent comprises the following components by weight:

[0052] 25 parts of alkali residue,

[0053] 45 parts of steel slag,

[0054] 6 parts of waste plaster mold,

[0055] 35 parts of gelling material,

[0056] 1.5 parts of additives;

[0057] The cementitious material is clinker cement,

[0058] The additives are enhancers.

[0059] The preparation method of above-mentioned masonry mortar, comprises the following steps:

[0060] (1) get steel slag, grind, sort, obtain steel slag powder;

[0061] (2) Preparation of aggregate forming agent: get alkali slag, steel slag, waste gypsum mold, cem...

Embodiment 3

[0064] A kind of masonry mortar, comprises the raw material of following parts by weight:

[0065] 10 parts of steel slag powder, 3 parts of aggregate forming agent and 2 parts of water;

[0066] The steel slag powder comprises 5 parts by weight of 1mm steel slag powder, 3.33 parts of 150 μm steel slag powder and 1.67 parts of 100 μm steel slag powder;

[0067] The aggregate forming agent comprises the following components by weight:

[0068] 20 parts of alkali residue,

[0069] 40 parts of steel slag,

[0070] 5 parts of waste plaster mold,

[0071] 34 parts of gelling material,

[0072] Additive 1 part;

[0073] The cementitious material is cement clinker;

[0074] The additive is a grinding aid.

[0075] The preparation method of above-mentioned masonry mortar, comprises the following steps:

[0076] (1) get steel slag, grind, sort, obtain steel slag powder;

[0077] (2) Preparation of aggregate forming agent: get alkali slag, steel slag, waste gypsum mold, cementiti...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a mortar. The mortar takes industrial solid waste steel slag powder with different particle sizes and an aggregate forming agent composed of industrial solid wastes as main rawmaterials, and steel slag with the particle size of about 1 mm can play a skeleton role, so that the strength of the mortar is improved, the heat resistance of the mortar is improved, the mortar is ensured to have relatively high strength in a using process, various stress effects can be borne, and cracks are avoided; gaps of 1 mm steel slag can be filled with the steel slag with the particle sizeof 150 [mu]m, so that the density of the mortar is increased, and the strength of the mortar is further enhanced; and the steel slag with the particle size of 100 [mu]m improves the uniform stabilityof the mortar. The mortar provided by the invention does not contain cement, the dependence of the mortar on the cement is reduced, meanwhile, the burden of industrial solid wastes on the environmentis solved, and the obtained mortar has the characteristics of uniformity and stability, small layering degree, high bonding strength, excellent frost resistance and low shrinkage value.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a mortar and a preparation method thereof. Background technique [0002] Mortar is a bonding substance used in building bricks. It is composed of a certain proportion of sand and cementing materials such as cement, lime paste, clay, etc. and water. Commonly used mortars are cement mortar, mixed mortar, lime mortar and clay mortar. Mortar is used for masonry and plastering projects, and can be divided into masonry mortar and plastering mortar. The former is used for masonry and component installation of bricks, stones, blocks, etc.; the latter is used for walls, floors, roofs and Plastering on the surface of beam and column structures to meet protection and decoration requirements. Some of the ordinary mortar materials are gypsum, lime plaster or clay mixed with fibrous reinforcing materials and water to prepare a paste, which is called ash, paste, mud or ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B18/14C04B22/10C04B20/00C04B111/20C04B103/12
CPCC04B28/00C04B18/141C04B40/0039C04B2201/50C04B2111/29C04B2103/12C04B20/0076C04B22/146C04B18/0481C04B2103/0068C04B2103/52C04B24/383C04B22/06C04B22/10Y02W30/91
Inventor 董华忠陈勇魏越任晓花王雪王刚
Owner 唐山中陶纪元工程设计有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap