Manufacturing method of ultrathin anti-aging medical latex gloves

A technique for latex gloves and a manufacturing method, which is applied in the field of gloves, and can solve problems affecting the quality of latex gloves, inability to add reinforcing agents, latex solution pollution, etc., to achieve improved physical cross-linking, excellent mechanical properties, and improved overall deformation resistance Effect

Inactive Publication Date: 2021-01-08
南京润京乳胶制品有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Since latex gloves are thin products, it is impossible to add many reinforcing agents, and the restrictions on anti-aging agents in medical products make the products generally have the disadvantages of not good enough performance, short storage period and easy aging and stickiness. way, the latex solution is often contaminated, greatly affecting the quality of latex gloves

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A method for making ultra-thin aging-resistant medical latex gloves, comprising the steps of:

[0025] The first step is to make latex solution, to nano-SiO 2 Add 2% dispersant to the mixture, add water to form a 10% dispersion, repeat ultrasonic treatment for 3 times, each time for 30 minutes, then age for 20 hours, centrifuge, and take mass fractions of 0.5%, 1.0%, and 2.0% respectively , 4.0% and 8.0% nano-SiO 2 , mixed with concentrated natural rubber latex, and then mixed with 0.5% sulfur, 1% zinc oxide, 0.1% zinc diethyldithiocarbamate, 0.2% zinc ethylphenyldithiocarbamate, 0.1% tetramethyl disulfide The thiuram was subjected to ultrasonic treatment for 30 minutes and heat treatment at 50° C. for 40 minutes to prepare pre-vulcanized modified latex, which was left to stand for 2 hours and then filtered.

[0026] The second step of mold processing and mold washing: use the clear water or detergent of the cleaning equipment to clean the glove molding molds fixed on...

Embodiment 2

[0039] A method for making ultra-thin aging-resistant medical latex gloves, comprising the steps of:

[0040] The first step is to make latex solution, to nano-SiO 2Add a dispersant with a mass fraction of 5%, add water to make a 20% dispersion, repeat the ultrasonic treatment 3 times, each time for 60min, and then age for 30h, centrifuge, and take the mass fractions of 0.5%, 1.0%, and 2.0% respectively , 4.0% and 8.0% nano-SiO 2 , mixed with concentrated natural rubber latex, and then mixed with 2% sulfur, 2% zinc oxide, 1% zinc diethyldithiocarbamate, 1% zinc ethylphenyldithiocarbamate, 0.8% tetramethyl disulfide The thiuram was subjected to ultrasonic treatment for 60 minutes and heat treatment at 50°C for 40 minutes to prepare pre-vulcanized modified latex, which was left to stand for 4 hours and then filtered.

[0041] The second step of mold processing and mold washing: use the clear water or detergent of the cleaning equipment to clean the glove molding molds fixed on...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a manufacturing method of ultrathin anti-aging medical latex gloves. The method comprises the following steps: 1, preparing a latex solution, 2, treating and washing a mold, 3,spraying the latex solution in the step 1 to a dried glove forming mold by using a spray gun, 4, carrying out primary drying on the latex solution on the glove forming mold: carrying out primary drying on the glove forming mold coated with the latex solution through a drying oven, spraying the latex solution to the glove forming mold dried for the first time through a spray gun, and then, drying the glove forming mold for the second time through the drying oven, 5, carrying out vulcanization and anti-sticking release treatment, and 6, carrying out demolding, and carrying out aging for 35-40 hours at the temperature of 110-150 DEG C by adopting hot air. Compared with existing gloves, the gloves manufactured through the method have the advantages that the ageing resistance is obviously improved, and the gloves have excellent mechanical properties; the latex gloves obtained by improving the spray gun have higher mechanical strength than latex gloves manufactured through an existing manufacturing method; and the gloves manufactured on the basis of the method are more stable in quality.

Description

technical field [0001] The invention relates to the field of gloves, in particular to a method for manufacturing ultra-thin anti-aging medical latex gloves. Background technique [0002] Natural latex gloves have good isolation protection and can effectively prevent the hazards of germs and chemicals, so they have been widely used in the 1980s. However, some people have allergic reactions to natural rubber latex, and Because natural latex gloves are not resistant to solvents and chemicals, people have to develop a variety of gloves made of synthetic materials, such as nitrile, neoprene, PVC, polyurethane gloves and so on. Among them, nitrile gloves are very popular because of their comfortable feel, good strength and oil resistance. [0003] Since latex gloves are thin products, it is impossible to add many reinforcing agents, and the restrictions on anti-aging agents in medical products make the products generally have the disadvantages of not good enough performance, shor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08J5/02C08L7/02C08K13/06C08K9/04C08K9/02C08K3/36C08K5/39C08K5/40A41D19/015
CPCC08J5/02A41D19/0055C08J2307/02C08K13/06C08K9/04C08K3/36C08K5/39C08K5/40C08K2201/014C08K2201/011
Inventor 江文养杨晓胜俞静
Owner 南京润京乳胶制品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com