Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A High Strength and Toughness mg-zn-y-nd-ti-zr Cast Magnesium Alloy with Low Hot Cracking Sensitivity

A casting magnesium alloy, sensitive technology, applied in the field of casting magnesium alloy, can solve the problems of high hot cracking tendency and low casting yield, achieve the effects of weakening stress, reducing content, and delaying the time of grain contact

Active Publication Date: 2022-05-06
WEIHAI WANFENG MAGNESIUM IND DEV
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The present invention aims at the deficiencies of the above-mentioned prior art, and provides a kind of Mg-Zn-Y-Nd-Mg-Zn-Y-Nd- Ti-Zr cast magnesium alloy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A high-strength and tough Mg-Zn-Y-Nd-Ti-Zr alloy with low thermal cracking sensitivity contains the components and their nominal mass percentages: 4.5wt.% Zn, 1wt.% Y, 2wt.% Nd , 0.5wt.% Ti and 0.5wt.% Zr, and the rest are Mg and unavoidable impurity elements. The concrete manufacturing method of this alloy is carried out as follows:

[0026] (1) Considering burning loss, according to the following mass percentage content 5wt.%Zn, 1.2wt.%Y, 2.2wt.%Nd, 0.6wt.%Ti and 0.8wt.%Zr and the balance are Mg, weigh Pure Mg, pure Zn, pure Ti (powder or chips), and master alloys Mg-25Y (wt%), Mg-25Nd (wt%), Mg-30Zr (wt%).

[0027] (2) The temperature of the smelting furnace is raised to 750° C., and smelted in an electric furnace under the protection of 99.8% N2 and 0.2% SF6 mixed gas. Blow in argon to stir and remove slag, after standing still for 30-50 minutes, take a sample and use x-ray spectrum to detect its actual composition: 4.7wt.%Zn, 1.1wt.%Y, 1.9wt.%Nd, 0.5wt .%Ti and ...

Embodiment 2

[0032] A high-strength and tough Mg-Zn-Y-Nd-Ti-Zr alloy with low thermal cracking sensitivity contains the components and their nominal mass percentages: 4.5wt.% Zn, 1wt.% Y, 2wt.% Nd , 0.5wt.% Ti and 0.5wt.% Zr, and the rest are Mg and unavoidable impurity elements. The concrete manufacturing method of this alloy is carried out as follows:

[0033] (1) Considering burning loss, according to the following mass percentage content 5wt.%Zn, 1.2wt.%Y, 2.2wt.%Nd, 0.6wt.%Ti and 0.8wt.%Zr and the balance are Mg, weigh Pure Mg, pure Zn, pure Ti (powder or chips), and master alloys Mg-25Y (wt%), Mg-25Nd (wt%), Mg-30Zr (wt%);

[0034] (2) Raise the temperature of the smelting furnace to 750°C, under 99.8%N 2 and 0.2% SF 6 Melted in an electric furnace under the protection of mixed gas. Blow in argon to stir and remove slag, after standing still for 30-50 minutes, take a sample and use x-ray spectrum to detect its actual composition: 4.8wt.%Zn, 0.9wt.%Y, 2.0wt.%Nd, 0.5wt .%Ti and 0....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-strength and tough Mg-Zn-Y-Nd-Ti-Zr cast magnesium alloy with low thermal cracking sensitivity, which belongs to the technical field of cast magnesium alloys. The magnesium alloy is composed of the following components in weight percentage: 4-5wt.% Zn, 1.0-1.2wt.% Y, 1.8-2.2wt.% Nd, 0.3-0.6wt.% Ti, 0.5-0.8wt.% Zr, the rest are Mg and impurity elements, in the present invention Adding rare earth element Nd whose solid solubility limit is much smaller than rare earth element Y to Mg‑4.5Zn‑1Y alloy, and controlling its content, can improve the strength of the alloy more effectively, adding 0.3‑0.6wt.%Ti and 0.5‑ 0.8wt.% Zr further refines the grains of the magnesium alloy, improves the strength and toughness of the alloy, and reduces its hot cracking sensitivity.

Description

technical field [0001] The invention belongs to the technical field of cast magnesium alloys, and in particular relates to a high-strength and tough Mg-Zn-Y-Nd-Ti-Zr cast magnesium alloy with low thermal cracking sensitivity. Background technique [0002] Due to its low density, high specific strength, and high damping performance, magnesium alloys are considered to be an important development direction for lightweight in the fields of automobiles, aerospace, and weaponry. At present, due to the good fluidity of commercial magnesium alloys, they are very suitable for casting and forming, so in the existing magnesium alloy engineering structural parts, casting alloys account for almost more than 90%. On the other hand, compared with wrought magnesium alloys, cast magnesium alloys are affected by as-cast defects and have lower strength and toughness, especially when they are used for forming complex structural parts, they are very prone to hot cracking. Previous studies have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C23/04C22C1/03
CPCC22C23/04C22C1/03
Inventor 朱训明刘旦王志方王建孟祥鋆
Owner WEIHAI WANFENG MAGNESIUM IND DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com