Graphene waterproofing agent for textile use

A graphene, water repellent technology, applied in textiles and papermaking, fiber processing, liquid repellent fibers, etc., can solve the problems of fiber damage and low tensile properties of fabrics

Pending Publication Date: 2021-02-05
NANTONG QIANGSHENG GRAPHENE TECH CO LTD
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a graphene waterproofing agent, which incorporates graphene into the components of the waterproofing agent, which has excellent waterproof performance, and can solve the problems of low tensile properties and fiber damage caused by the waterproofing agent after use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A graphene waterproofing agent for textile, its raw material comprises: modified graphene material, silicon dioxide, resin, surfactant, auxiliary agent and water.

[0027] Preferably, the raw materials of the waterproofing agent include by mass percentage: 0.5% of modified graphene material, 1% of silicon dioxide, 13% of resin, 0.5% of surfactant, 2% of auxiliary agent, and the balance is water.

[0028] Modified graphene materials include graphene prepared by chemical vapor deposition.

[0029] The resin contains silicone resin.

[0030] The surfactant is a cationic surfactant.

[0031] The auxiliary agent contains initiator and thickener; the weight ratio of initiator and thickener is 1:1. Initiators include persulfates. Thickeners include diatomaceous earth.

Embodiment 2

[0033] A graphene waterproofing agent for textile, its raw material comprises: modified graphene material, silicon dioxide, resin, surfactant, auxiliary agent and water.

[0034] Preferably, the raw materials of the waterproofing agent include by mass percentage: 2% of modified graphene material, 3% of silicon dioxide, 25% of resin, 3% of surfactant, 4% of auxiliary agent, and the balance is water.

[0035] The modified graphene material includes exfoliated graphene exfoliated by carbon dioxide supercritical expansion or graphene oxide exfoliated by chemical oxidation.

[0036] The resin contains acrylic resin.

[0037] The surfactant is a cationic surfactant.

[0038] The auxiliary agent includes an initiator and a thickener; the weight ratio of the initiator and the thickener is 2-1.

[0039] Initiators include per-oil-soluble azos. The thickener comprises ammonium polyacrylate.

Embodiment 3

[0041] A graphene waterproofing agent for textile, its raw material comprises: modified graphene material, silicon dioxide, resin, surfactant, auxiliary agent and water.

[0042] Preferably, the raw materials of the waterproofing agent include by mass percentage: 3% of modified graphene material, 4% of silicon dioxide, 36% of resin, 4% of surfactant, 6% of auxiliary agent, and the balance is water.

[0043] The modified graphene material includes graphene oxide modified by a coupling agent.

[0044] The resin includes urethane resin and polyurethane.

[0045] The surfactant is a cationic surfactant.

[0046] The auxiliary agent includes initiator and thickener; the weight ratio of initiator and thickener is 3:2.

[0047] Initiators include persulfates and oil-soluble azos. Thickeners include polyvinyl alcohol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a graphene waterproofing agent for textile use. The graphene waterproofing agent is prepared from the following raw materials: a modified graphene material, silicon dioxide, resin, a surfactant, an auxiliary agent and water. Preferably, the waterproofing agent is prepared from the following raw materials in percentage by mass: 0.5-5% of the modified graphene material, 1-6%of the silicon dioxide, 13-60% of the resin, 0.5-8% of the surfactant, 2-10% of the auxiliary agent and the balance of water. The surfactant is a cationic surfactant. The auxiliary agent comprises aninitiator and a thickener; and the weight ratio of the initiator to the thickener is (1: 1)-(5: 3). The initiator comprises persulfate and / or oil-soluble azo. The thickener comprises any one or more of diatomite, ammonium polyacrylate, polyvinyl alcohol and polyurethane. According to the graphene waterproofing agent, the graphene is blended into each component of the waterproofing agent, so that the obtained waterproofing agent has excellent waterproof performance, and meanwhile, the problems of low tensile property and fiber damage of the fabric after the waterproofing agent is used can be solved.

Description

technical field [0001] The invention relates to a graphene waterproofing agent, in particular to a graphene waterproofing agent for textiles. Background technique [0002] Textile waterproofing agent is a product used for functional finishing of textile fabrics. It has a wide range of applications and involves various fields of textiles. There are also many types of products. The same product can be used for different fabrics, and different products can give fabrics different properties. performance. According to the performance, textile waterproofing agent can be mainly divided into four aspects: waterproof, oil-proof, anti-fouling and easy to decontaminate. After finishing with different textile waterproofing agents, the above four properties can be given to textiles. [0003] Graphene is a single-layer carbon atom material peeled off from graphite. Carbon atoms are tightly packed into a single-layer two-dimensional honeycomb lattice structure. It is the thinnest, hardest...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/74D06M11/79D06M15/643D06M15/263D06M15/285D06M15/564D06M15/333D06M101/10
CPCD06M11/74D06M11/79D06M15/643D06M15/263D06M15/285D06M15/564D06M15/333D06M2200/12D06M2101/10
Inventor 沙嫣沙晓林马立国
Owner NANTONG QIANGSHENG GRAPHENE TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com