Method for obtaining transient liquid phase diffusion bonding of RAFM reliable joint

A technology of diffusion connection and instantaneous liquid phase, which is applied in the direction of welding/welding/cutting items, welding equipment, non-electric welding equipment, etc. It can solve the problems of high surface roughness of the workpiece connection surface, large residual stress of the joint, deformation of the workpiece, etc., to achieve The effect of small pressure, short connection time, and small deformation of the workpiece

Active Publication Date: 2021-02-23
TIANJIN UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the pressure required to connect workpieces using solid phase diffusion bonding technology is very high, resulting in deformation of the workpieces, large residual stress in the joints, and solid phase diffusion bonding has high requirements for the surface roughness of the workpiece connection surface.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for obtaining transient liquid phase diffusion bonding of RAFM reliable joint
  • Method for obtaining transient liquid phase diffusion bonding of RAFM reliable joint
  • Method for obtaining transient liquid phase diffusion bonding of RAFM reliable joint

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Step 1: Cut RAFM steel into The cylinder, and then use a grinder to grind the end face of the cylinder flat and fine.

[0022] Step 2: Cut the Fe-Si-B alloy foil into For the disc, use sandpaper to polish both sides of the foil to 1500#. Step 3: Before connecting, ultrasonically clean the sample and alloy foil in acetone for 20 minutes, dry them, and then ultrasonically clean them in alcohol for 30 minutes, and dry them. Then the surface of the sample was washed with a pickling solution (volume percentage 20% HNO 3 +5%HF+75%H 2 O) wash 3min.

[0023] Step 4: sandwich the Fe-Si-B alloy foil between the surfaces to be connected of two RAFM steel samples. Place the assembled sample in a vacuum furnace and draw a vacuum. When the vacuum reaches 5×10 -3 Start heating at Pa, raise the temperature to 850°C at a heating rate of 5°C / min, hold for 30 minutes, then raise the temperature to 1215°C at a heating rate of 5°C / min, apply a pressure of 1MPa and hold for 3 minute...

Embodiment 2

[0028] Step 1: Cut RAFM steel into The cylinder, and then use a grinder to grind the end face of the cylinder flat and fine.

[0029] Step 2: Cut the Fe-Si-B alloy foil into For the disc, use sandpaper to polish both sides of the foil to 1500#. Step 3: Before connecting, ultrasonically clean the sample and alloy foil in acetone for 20 minutes, dry them, and then ultrasonically clean them in alcohol for 30 minutes, and dry them. Then the surface of the sample was washed with pickling solution (20% HNO 3 +5%HF+75%H 2 O) wash 5min. Step 4: sandwich the Fe-Si-B alloy foil between the surfaces to be connected of two RAFM steel samples. Place the assembled sample in a vacuum furnace and draw a vacuum. When the vacuum reaches 5×10 -3 Start heating at Pa, raise the temperature to 900°C at a heating rate of 10°C / min, keep it for 20 minutes, then raise the temperature to 1200°C at a heating rate of 10°C / min, apply a pressure of 0.8MPa and keep it for 30 minutes, then cool to ro...

Embodiment 3

[0034] Step 1: Cut RAFM steel into The cylinder, and then use a grinder to grind the end face of the cylinder flat and fine.

[0035] Step 2: Cut the Fe-Si-B alloy foil into For the disc, use sandpaper to polish both sides of the foil to 1500#. Step 3: Before connecting, ultrasonically clean the sample and amorphous foil in acetone for 30 minutes, dry them, and then ultrasonically clean them in alcohol for 20 minutes, and dry them. Then the surface of the sample was washed with pickling solution (20% HNO 3 +5%HF+75%H 2 O) wash 3min. Step 4: sandwich the Fe-Si-B alloy foil between the surfaces to be connected of two RAFM steel samples. Place the assembled sample in a vacuum furnace and draw a vacuum. When the vacuum reaches 5×10 -3 Start heating at Pa, raise the temperature to 850°C at a heating rate of 5°C / min, keep it for 30 minutes, then raise the temperature to 1200°C at a heating rate of 5°C / min, apply a pressure of 0.2MPa and keep it for 60 minutes, then cool to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shear strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
shear strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for obtaining transient liquid phase diffusion bonding of a RAFM reliable joint. The method comprises the steps that transient liquid phase diffusion bonding is carried out on a RAFM sample using an iron-based alloy foil Fe-Si-B, the temperature is increased to 800-900 DEG C at the heating rate of 5-20 DEG C / min, the temperature is kept 20-40 minutes, then the temperature is increased to 1185-1215 DEG C at the heating rate of 5-20 DEG C / min, 0.2-2 MPa pressure is applied in the direction perpendicular to a to-be-connected face, the temperature is kept 1-60 minutes, and finally, the temperature is reduced to the room temperature of 20-25 DEG C at the cooling rate of 5-30 DEG C / min. According to the method for obtaining transient liquid phase diffusion bonding of the RAFM reliable joint, an alloy foil intermediate layer is utilized and a thermal cycle process of transient liquid phase diffusion bonding is designed, so that the RAFM reliable joint with uniform structure and good mechanical properties is obtained.

Description

technical field [0001] The invention belongs to a metal material welding technology, and more specifically relates to a method for obtaining instant liquid phase diffusion connection of reliable joints of RAFM steel. Background technique [0002] With the rapid development of economy and society, human energy consumption is increasing day by day. The traditional non-renewable energy is gradually exhausted, so the development and utilization of renewable energy is imminent. As a kind of clean energy, nuclear energy has the advantages of good environmental compatibility, zero carbon emission, and cost-effectiveness. It is the trend of future energy development. Therefore, the continuous development of clean nuclear energy puts forward higher requirements for the safe, reliable and efficient operation of nuclear reactors. Due to the special environment in nuclear reactors, reactor structural materials need to withstand higher radiation doses, more complex corrosion environmen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B23K20/00B23K20/24C22C38/02C22C38/04C22C38/22C22C38/24C22C38/26B23K103/04
CPCB23K20/001B23K20/24C22C38/26C22C38/24C22C38/22C22C38/04C22C38/02B23K2103/04
Inventor 刘晨曦李文超刘永长王祖敏余黎明李会军
Owner TIANJIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com