Unlock instant, AI-driven research and patent intelligence for your innovation.
Anti-corrosion and anti-rust wax and preparation method and preparation device thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology for anti-corrosion and anti-rust and preparation equipment, which is applied in the direction of anti-corrosion coatings, chemical instruments and methods, mixers with rotating stirring devices, etc., which can solve problems such as unfavorable construction and poor construction performance of anti-corrosion and anti-rust wax, so as to facilitate subsequent production Effect
Inactive Publication Date: 2021-05-04
NANJING TIANSHI NEW MATERIAL TECH
View PDF9 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] In order to solve the problem in the prior art that the anti-corrosion and anti-rust wax has poor construction performance and is not conducive to construction at normal temperature, the present invention proposes an anti-corrosion and anti-rust wax, a preparation method and a preparation device thereof
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0027] The present invention also proposes a preparation method of the above-mentioned anti-corrosion and anti-rust wax, comprising the following steps:
[0031] S104: adding the oxidized polyethylene wax micropowder and the petroleum resin micropowder in parts by weight into the reaction kettle and stirring to obtain the anti-corrosion and anti-rust wax.
[0034] Further, the duration of the heat preservation and stirring is 0.5-1 h.
Embodiment 1
[0036] Embodiment 1 provides a kind of antirust wax. The preparation raw materials of the antirust wax, in parts by weight, include the following components: 25 parts of modified linseed oil, 10 parts of oxidized polyethylene wax micropowder, and 2 parts of petroleum resin micropowder , 5 parts of bariumpetroleum sulfonate, 1 part of lanolinmagnesium, 5 parts of white oil, 0.2 part of antioxidant.
[0037] Prepare as follows:
[0038] Put the modified linseed oil, barium petroleum sulfonate, magnesium lanolin, white oil and antioxidant in parts by weight into the reaction kettle, and heat to 80°C while stirring;
[0039] Then keep stirring for 30min;
[0040] Turn on the cooling water of the reactor and cool it down to 30°C;
[0041] Add the oxidized polyethylene wax micro-powder and petroleum resin micro-powder in parts by weight, and stir for 15 minutes to prepare. Specific embodiment 2:
Embodiment 2
[0042] Embodiment 2 provides a kind of antirust wax. The preparation raw materials of the antirust wax, in parts by weight, include the following components: 30 parts of modified linseed oil, 15 parts of oxidized polyethylene wax micropowder, and 5 parts of petroleum resin micropowder , 10 parts of barium petroleum sulfonate, 2 parts of lanolin magnesium, 10 parts of white oil, 0.3 parts of antioxidant.
[0043] Prepare as follows:
[0044] Put the modified linseed oil, barium petroleum sulfonate, magnesium lanolin, white oil and antioxidant in parts by weight into the reaction kettle, and heat to 80°C while stirring;
[0045] Then keep stirring for 30min;
[0046] Turn on the cooling water of the reactor and cool it down to 30°C;
[0047] Add the oxidized polyethylene wax micro-powder and petroleum resin micro-powder in parts by weight, and stir for 15 minutes to prepare. Specific embodiment 3:
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses anti-corrosion and anti-rustwax and a preparation method and a preparation device thereof. The anti-corrosion and anti-rustwax is prepared from, by weight, 25-45 parts of modified linseed oil, 10-25 parts of oxidized polyethlene wax micro powder, 2-15 parts of petroleum resin micro powder, 5-15 parts of bariumpetroleumsulfonate, 1-5 parts of lanolinmagnesium, 5-15 parts of white oil and 0.2-1 part of antioxidants. The preparation method comprises the following steps: weighting materials; carrying out heat preserving and stirring; performing cooling to a cooling temperature; and adding the materials and performing stirring to prepare the anti-corrosion and anti-rust wax. The preparation device comprises a kettle body, a cooling assembly, a stirring assembly, a cleaning assembly and a heating assembly, wherein the cleaning assembly comprises a cleaning scraping plate, a threaded plate and a rotary connection support. The anti-corrosion and anti-rust wax, the preparation method and the preparation device thereof are provided on the basis of the prior art; the composition of the anti-corrosion and anti-rust wax is improved, and the anti-rust wax is kept in a liquid state, so that the prepared anti-corrosion and anti-rust wax has better construction performance; and the preparation device is improved, and the anti-corrosion and anti-rust wax adhered to the kettle body is effectively cleaned by using the cleaning scraper, so that subsequent production is facilitated.
Description
technical field [0001] The invention relates to the technical field of anti-corrosion and anti-rust, in particular to an anti-corrosion and anti-rust wax, a preparation method and a preparation device thereof. Background technique [0002] The anti-corrosion and anti-rust wax has excellent anti-corrosion and anti-rust functions, and is widely used in the field of metal anti-rust and anti-corrosion. However, the existing anti-corrosion and anti-rust wax has the problems of high VOC content, high product viscosity and poor construction performance at room temperature. SUMMARY OF THE INVENTION [0003] In order to solve the problem in the prior art that the anti-corrosion and anti-rust wax has poor construction performance and is unfavorable for construction at normal temperature, the present invention proposes an anti-corrosion and anti-rust wax, a preparation method and a preparation device thereof. [0004] An anti-corrosion and anti-rust wax, by weight, is composed of the...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More