Wound repair spray as well as preparation method and application thereof
A technology of wound repair and spray, which is applied in the field of wound repair spray and its preparation, and can solve the problems of large wound irritation, combined use, and inconvenient use
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0036]A wound repair spray, which is made of the following components: 10wt% bioactive glass, 5wt% zinc hyaluronate, 70.5wt% solvent, 10wt% propellant, 0.3wt% hydroxypropyl methylcellulose, 4wt% % penetration enhancer and 0.2wt% Span 20, the solvent is 70wt% ethanol aqueous solution with pH 6-7, the weight ratio of the bioactive glass to zinc hyaluronate is 2:1, and the propellant consists of Dichlorodifluoromethane and trichlorofluoromethane in a ratio of 1:1, the penetration enhancer is composed of propylene glycol and peppermint oil in a weight ratio of 1:3, and the bioactive glass is composed of Na 2 O, CaO, P 2 o 5 and SiO 2 composition, and the weight percentage is 24.5wt%: 24.5wt%: 6wt%: 45wt%, and the molecular weight of the zinc hyaluronate is 10-15kDa.
Embodiment 2
[0038] A wound repair spray, which is made of the following components: 14wt% bioactive glass, 7wt% zinc hyaluronate, 64.5wt% vehicle, 10wt% propellant, 0.3wt% hydroxypropyl methylcellulose, 4wt% % penetration enhancer and 0.2wt% Span 20, the solvent is 70wt% ethanol aqueous solution with pH 6-7, the weight ratio of the bioactive glass to zinc hyaluronate is 2:1, and the propellant consists of Dichlorodifluoromethane and trichlorofluoromethane in a ratio of 1:1, the penetration enhancer is composed of propylene glycol and peppermint oil in a weight ratio of 1:3, and the bioactive glass is composed of Na 2 O, CaO, P 2 o 5 and SiO 2 composition, and the weight percentage is 24.5wt%: 24.5wt%: 6wt%: 45wt%, and the molecular weight of the zinc hyaluronate is 10-15kDa.
Embodiment 3
[0040] A wound repair spray, which is made of the following components: 14wt% bioactive glass, 7wt% zinc hyaluronate, 64.5wt% vehicle, 10wt% propellant, 0.3wt% ethyl cellulose, 4wt% penetration enhancer agent and 0.2wt% Span 20, the solvent is 70wt% ethanol aqueous solution with pH 6-7, the weight ratio of the bioactive glass to zinc hyaluronate is 2:1, and the propellant consists of a weight ratio of 1 : 1 of dichlorodifluoromethane and trichlorofluoromethane, the penetration enhancer is composed of propylene glycol and peppermint oil with a weight ratio of 1:3, and the bioactive glass is composed of Na 2 O, CaO, P 2 o 5 and SiO 2 composition, and the weight percentage is 24.5wt%: 24.5wt%: 6wt%: 45wt%, and the molecular weight of the zinc hyaluronate is 10-15kDa.
PUM
Property | Measurement | Unit |
---|---|---|
particle diameter | aaaaa | aaaaa |
molecular weight | aaaaa | aaaaa |
particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com