A kind of two-dimensional ni-ir porous nanosheet and its preparation method and application

A nanosheet, ni-ir technology, applied in nanotechnology, electrolysis components, electrodes, etc., can solve the problems of difficulty in obtaining high-purity hydrogen, hindering large-scale commercial applications, and limiting the large-scale application of hydrogen energy, achieving excellent The effect of electrocatalytic activity, structural stability, and many active sites

Active Publication Date: 2021-12-21
NANJING NORMAL UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, hydrogen is mainly separated from fossil fuels such as natural gas and coalbed methane. It is difficult to obtain high-purity hydrogen, which greatly limits the large-scale application of hydrogen energy.
The water-splitting reaction consisting of hydrogen evolution and oxygen evolution half-reaction serves as a sustainable source of hydrogen, an attractive energy carrier that can be used to generate clean electricity in fuel cells, whereas the oxygen evolution half-reaction is electrolytic The rate-determining step of water reaction, its large overpotential seriously hinders large-scale commercial application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of two-dimensional ni-ir porous nanosheet and its preparation method and application
  • A kind of two-dimensional ni-ir porous nanosheet and its preparation method and application
  • A kind of two-dimensional ni-ir porous nanosheet and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A preparation method of two-dimensional Ni-Ir porous nanosheets, comprising the following steps:

[0043] 1) Preparation of Hoffman-type complex precursors with two-dimensional layered structure

[0044] Use nickel potassium cyanide and iridium chloride as precursors, heat in an oil bath at 70°C, and keep the reaction at this temperature for 30 minutes. After the reaction system is centrifuged, the solid is washed 3 times with water to obtain a two-dimensional layered structure. The precursor of the Hoffman type complex;

[0045] 2) Preparation of two-dimensional Ni-Ir porous nanosheets

[0046] The dried two-dimensional layered Hoffman-type complex precursor was placed in a tube furnace, and the temperature was programmed to rise to 250 °C for calcination and oxidation for 2 h; after cooling to room temperature, the obtained material was loaded on carbon cloth and passed through a specific Two-dimensional Ni-Ir porous nanosheets were obtained by reduction under the e...

Embodiment 2

[0049] A preparation method of two-dimensional Ni-Ir porous nanosheets, comprising the following steps:

[0050] 1) Preparation of Hoffman-type complex precursors with two-dimensional layered structure

[0051] Use nickel potassium cyanide and iridium chloride as precursors, heat in an oil bath at 80°C, and keep the reaction at this temperature for 30 minutes. After the reaction system is centrifuged, the solid is washed several times with water to obtain a two-dimensional layered structure. The precursor of the Hoffman type complex;

[0052] 2) Preparation of two-dimensional Ni-Ir porous nanosheets

[0053] The dried two-dimensional layered Hoffman-type complex precursor was placed in a tube furnace, and the temperature was programmed to rise to 250 °C for calcination and oxidation for 2 h; after cooling to room temperature, the obtained material was loaded on carbon cloth and passed through a specific Two-dimensional Ni-Ir porous nanosheets were obtained by reduction under...

Embodiment 3

[0056] A preparation method of two-dimensional Ni-Ir porous nanosheets, comprising the following steps:

[0057] 1) Preparation of Hoffman-type complex precursors with two-dimensional layered structure

[0058] Use nickel potassium cyanide and iridium chloride as precursors, heat the oil bath at 90°C, and keep the reaction at this temperature for 30 minutes. After the reaction system is centrifuged, the solid is washed several times with water to obtain a two-dimensional layered structure. The precursor of the Hoffman type complex;

[0059] 2) Preparation of two-dimensional Ni-Ir porous nanosheets

[0060] The dried two-dimensional layered Hoffman-type complex precursor was placed in a tube furnace, and the temperature was programmed to rise to 250 °C for calcination and oxidation for 2 h; after cooling to room temperature, the obtained material was supported on carbon cloth and passed through Two-dimensional Ni-Ir porous nanosheets were obtained by reduction under a specifi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a two-dimensional Ni-Ir porous nanosheet and its preparation method and application, using nickel cyanide and iridium salt as precursors, and preparing a two-dimensional layered structure Hoffman type complex precursor through oil bath heating , and after high-temperature calcination and oxidation, a two-dimensional Ni‑Ir porous nanosheet was obtained by reduction under a specific electrochemical window. Compared with the traditional preparation method, the method of the present invention has simple process operation, can remove the miscellaneous ions in the solution by using deionized water, does not release greenhouse gas during the calcination oxidation process, and the electrochemical reduction process is clean, environment-friendly and pollution-free. The two-dimensional Ni-Ir porous nanosheet prepared by the method of the present invention has extremely high purity, has the advantages of large specific surface area, many active sites, good electronic conductivity, stable structure, etc., and exhibits excellent electrocatalytic activity for oxygen evolution.

Description

technical field [0001] The invention relates to a two-dimensional Ni-Ir porous nanosheet and its preparation method and application, belonging to the technical field of Ni-Ir porous sheet nanoflowers. Background technique [0002] Environmental pollution and energy crisis are becoming more and more serious, and the remarkable advantages of high energy efficiency and low emission of fuel cell technology have attracted widespread attention. At present, hydrogen is mainly separated from fossil fuels such as natural gas and coalbed methane. It is difficult to obtain high-purity hydrogen, which greatly limits the large-scale application of hydrogen energy. The water-splitting reaction consisting of hydrogen evolution and oxygen evolution half-reaction serves as a sustainable source of hydrogen, an attractive energy carrier that can be used to generate clean electricity in fuel cells, whereas the oxygen evolution half-reaction is electrolytic The rate-determining step of water re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25B11/093C25B1/04B82Y40/00
CPCC25B11/04C25B1/04Y02E60/36
Inventor 唐亚文刘启成刘嘉琪周心怡徐林孙冬梅邱晓雨
Owner NANJING NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com