Environment-friendly two-component polyurethane lawn glue with high initial adhesion and easy construction and preparation method thereof

A two-component polyurethane, initial tack technology, used in polyurea/polyurethane adhesives, adhesives, adhesive types, etc. edge shift etc.

Pending Publication Date: 2021-06-08
湖南盛天新材料有限公司
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the deficiencies in the prior art, the present invention provides an environmentally friendly two-component polyurethane lawn adhesive with high initial adhesion and easy construction and a preparation method thereof, which overcomes the toxicity of the existing solvent-based lawn adhesive due to the volatilization and toxicity of the two-component polyurethane Lawn glue has low initial adhesion and is prone to defects such as misalignment and displacement. The two-component polyurethane lawn adhesive has no solvent volatilization, high initial adhesion, and no misalignment and displacement.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An environmentally friendly two-component polyurethane lawn adhesive with high initial adhesion and easy construction, including component A and component B with a mass ratio of 1:4; the component A is a curing agent, which is polymethylene polybenzene The amount of base isocyanate is 25 parts; the B component includes the following components by weight: polytetrahydrofuran ether glycol (PTMEG), its molecular weight is 1000 ± 50, 2000 ± 50 or 3000 ± 50, and the dosage is 5 parts; 2 functional group polyether, its molecular weight is 400, dosage is 20 parts; multifunctional polyether, its molecular weight is 3000, contains 3 functional groups, or its molecular weight is 5000, contains 3 functional groups, dosage is 10 parts; 403 polyether 0.5 part; chain extension 3.5 parts of agent; 10 parts of plasticizer; 35 parts of filler; 10 parts of tackifying resin; 0.5 part of coupling agent; 0.01 part of catalyst;

[0028] The chain extender is a mixture of 1.5 parts of 1,4-but...

Embodiment 2

[0030] An environmentally friendly two-component polyurethane lawn adhesive with high initial adhesion and easy construction, including component A and component B with a mass ratio of 1:4; the component A is a curing agent, which is polymethylene polybenzene The amount of base isocyanate is 25 parts;

[0031] The B component includes the following components in parts by weight: polytetrahydrofuran ether glycol (PTMEG), whose molecular weight is 1000±50, 2000±50 or 3000±50, and the dosage is 13 parts; 2 functional group polyether, whose molecular weight 400, the dosage is 15 parts; multifunctional polyether, its molecular weight is 3000, containing 3 functional groups, or its molecular weight is 5000, containing 3 functional groups, the dosage is 5 parts; 0.2 parts of 403 polyether; 6 parts of chain extender; plasticizer 20 parts; 25 parts of filler; 12 parts of tackifying resin; 0.2 parts of coupling agent; 0.5 parts of catalyst; 0.2 parts of water remover; 1 part of pigment....

Embodiment 3

[0034] An environmentally friendly two-component polyurethane lawn adhesive with high initial adhesion and easy construction, including component A and component B with a mass ratio of 1:4; the component A is a curing agent, which is polymethylene polybenzene The amount of base isocyanate is 25 parts;

[0035] The B component includes the following components in parts by weight: polytetrahydrofuran ether glycol (PTMEG), whose molecular weight is 1000±50, 2000±50 or 3000±50, and the dosage is 5 parts; 2 functional group polyether, whose molecular weight 400, the dosage is 25 parts; multifunctional polyether, its molecular weight is 3000, containing 3 functional groups, or its molecular weight is 5000, containing 3 functional groups, the dosage is 5 parts; 1 part of 403 polyether; 2 parts of chain extender; plasticizer 15 parts; 40 parts of filler; 5 parts of tackifying resin; 1 part of coupling agent; 0.2 part of catalyst; 1 part of water remover; 0.1 part of pigment.

[0036]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides environment-friendly two-component polyurethane lawn glue with high initial adhesion and easy construction. The lawn glue comprises a component A and a component B in a mass ratio of 1:4. The component A is 25 parts of a curing agent; and the component B is prepared from the following components in parts by weight: 3-8 parts of polytetrahydrofuran ether glycol, 15-25 parts of 2-functional group polyether, 5-15 parts of polyfunctional group polyether, 0.2-1 part of 403 polyether, 2-6 parts of a chain extender, 5-15 parts of a plasticizer, 25-40 parts of filler, 5-15 parts of tackifying resin, 0.2-1 part of a coupling agent, 0.01-0.5 part of a catalyst, 0.2-1 part of a dewatering agent, and 0.1-2 parts of a pigment. According to the environment-friendly two-component polyurethane lawn glue with high initial adhesion and easy construction, the influence of solvent volatilization of a solvent type lawn glue on the environment is avoided, and the defects that common two-component polyurethane lawn glue is high in viscosity and difficult to construct, and misalignment and displacement phenomena caused by low initial adhesion are overcome.

Description

technical field [0001] The invention relates to the technical field of artificial turf paving glue, in particular to an environmentally friendly two-component polyurethane lawn glue with high initial adhesion and easy construction and a preparation method thereof. Background technique [0002] Lawn glue is a special adhesive specially used for artificial turf / turf paving and fixing. It is a special-purpose universal glue with special additions and excellent weather resistance and water resistance. [0003] More than 95% of the popular lawn paving adhesives on the market are solvent-based resin adhesives. The organic solvent of solvent-based resin glue volatilizes, releases in the air, or adheres to the artificial turf, causing environmental pollution and seriously endangering human health. meets the. [0004] For this reason, people have developed two-component polyurethane lawn glue, because it does not contain solvents, so the environmental protection performance has bee...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J175/08C08G18/48
CPCC09J175/08C08G18/4808C08G18/4854C08G18/4825
Inventor 张书申文强谢燕平
Owner 湖南盛天新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap