A special anti-virus slurry for wall covering, wall covering and production method thereof
An anti-virus and anti-viral agent technology, applied in biochemical fiber treatment, textiles and papermaking, and liquid-repellent fibers, etc., can solve the problem of low continuous disinfection effect of disinfectant, large area occupied by wall coverings, and adverse effects of wall coverings To achieve the effect of reducing spraying costs and bacterial growth, preventing bacterial growth, reducing the spread of viruses and cross-infection
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0038] like figure 1 As shown, a wall covering comprises a base material layer 1, a pattern layer 4 and a protective layer 5 which are sequentially compounded, and the protective layer 5 is a waterproof and anti-virus coating, and the waterproof and anti-virus coating is made of a special anti-virus for wall coverings. The slurry is coated on the pattern layer 4 and then dried.
[0039] The wall covering also includes an adhesive layer 2 and a fiber texture layer 3 both disposed between the base material layer 1 and the pattern layer 4. The base material layer 1, the adhesive layer 2, the fiber texture layer 3, and the pattern layer 4 and the protective layer 5 are sequentially compounded.
[0040] The fiber texture layer 3 is a jacquard cloth layer; the base material layer 1 is a non-woven fabric layer.
[0041] The average thickness of the fiber texture layer 3 is 1 mm, the average thickness of the base material layer 1 is 0.5 mm, the average thickness of the pattern layer 4...
Embodiment 2
[0047] The difference between this example and Example 1 is that the antiviral slurry for wall covering includes the following raw materials by weight:
[0048]
[0049] The water-based acrylic resin is ETERWAT 1161-50; the polytetrafluoroethylene modified wax is Clariant 9610F.
[0050] The antibacterial and antiviral agent is ACTICIDE MBS ICB6 and Smart Fix mixed at a weight ratio of 1:1.
[0051] The surfactant is a mixture of fatty alcohol polyoxyethylene ether and cationic surfactant in a weight ratio of 1:2.
[0052] The cationic surfactant is dodecyldimethylbenzylammonium chloride.
[0053] The particle size of the porous calcium silicate is 5 μm, and the particle size of the nano silica is 50 nm.
[0054] The dispersant was DISPERBYK-190; the thickener was Acrysol RM-2020.
[0055] The preparation method of the special antiviral slurry for wall covering comprises the following steps:
[0056] (S1), take water acrylic resin, polytetrafluoroethylene modified wax, ...
Embodiment 3
[0060] The difference between this example and Example 1 is that the antiviral slurry for wall covering includes the following raw materials by weight:
[0061]
[0062] The water-based acrylic resin is ETERSOL 6923; the polytetrafluoroethylene modified wax is Clariant 9322F.
[0063] The antibacterial and antiviral agent is ACTICIDE MBS ICB6.
[0064] The surfactant is a mixture of fatty alcohol polyoxyethylene ether and cationic surfactant in a weight ratio of 1:1.
[0065] The cationic surfactant is tetradecyltrimethylammonium chloride.
[0066] The particle size of the porous calcium silicate is 5 μm, and the particle size of the nano silica is 50 nm.
[0067] The dispersant was DISPERBYK-199; the thickener was Acrysol RM-895.
[0068] The preparation method of the special antiviral slurry for wall covering comprises the following steps:
[0069] (S1), take water acrylic resin, polytetrafluoroethylene modified wax, nano-silica, porous calcium silicate, surfactant, d...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com