Preparation method of macroporous active alumina dry glue with high peptizing index

A technology of activated alumina and alumina, applied in the preparation of alkali metal aluminate/alumina/aluminum hydroxide, chemical instruments and methods, inorganic chemistry, etc., can solve the problem of unstable performance of peptized activated alumina, Problems such as poor peptization and low pore structure

Active Publication Date: 2021-07-02
天津凯文特科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the currently used peptized activated alumina has unstable performance and cannot exert stable performance in ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of macroporous active alumina dry glue with high peptizing index
  • Preparation method of macroporous active alumina dry glue with high peptizing index
  • Preparation method of macroporous active alumina dry glue with high peptizing index

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The technical solutions of the present invention will be further described below through specific examples.

[0025] 1. Preparation

[0026] A kind of preparation method of the macroporous activated alumina dry glue of high peptization index, comprises the steps:

[0027] Step 1, using aluminum sulfate solution and sodium metaaluminate solution to carry out neutralization and gelation in a co-current manner; the concentration of aluminum oxide in the aluminum sulfate solution in the step 1 is 50-150g / L, and its acid The alkali ratio is 1.4-1.7; preferably, the concentration of aluminum oxide in the aluminum sulfate solution in the step 1 is 100g / L, and the acid-base ratio is 1.55.

[0028] The concentration of aluminum oxide in the sodium metaaluminate solution in the step 1 is 150-250 g / L, and its acid-base ratio is 1.2-1.4. Preferably, the concentration of aluminum oxide in the sodium metaaluminate solution in the step 1 is 200g / L, and its acid-base ratio is 1.28. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Pore volumeaaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of macroporous active alumina dry glue with a high peptizing index. The preparation method comprises the following steps: step 1, neutralizing an aluminum sulfate solution and a sodium metaaluminate solution in a parallel flow manner to gelatinize; and step 2, aging, water-washing, drying and crushing the finished product gelatinized in the step 1 to obtain the activated aluminum oxide. The preparation method has the beneficial effects that the active aluminum oxide product with high peptizing index, large pore volume and large specific surface area can be obtained by controlling the gelatinizing process, raw material indexes and the like.

Description

technical field [0001] The invention relates to the field of preparation of macroporous activated alumina dry glue, in particular to a preparation method of macroporous activated alumina dry glue with high peptization index. Background technique [0002] Activated alumina is a pseudo-boehmite, a white, odorless, non-toxic powder with incomplete composition, low crystallinity, and spatial network structure. Activated alumina has physical properties such as high specific surface area and suitable pore structure. It can be peptized under acidic conditions as a binder for catalytic cracking and hydrogenation catalysts, which is an important application in the petrochemical industry. Peptized activated alumina as a binder can increase the mechanical strength and pore structure of the catalyst to a certain extent, and improve the catalytic performance of the catalyst. Therefore, the peptization performance of activated alumina is directly related to the selectivity, stability and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C01F7/14
CPCC01F7/141C01P2006/12C01P2006/14
Inventor 郝德彪周广增李卫东
Owner 天津凯文特科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap