A kind of golf head material and its preparation process and ball head striking surface

A golf head and striking surface technology, applied in golf balls, golf clubs, manufacturing tools, etc., can solve problems such as the inability to meet market demands, and achieve the effects of fewer types of raw materials, improved water corrosion resistance, and enhanced impact toughness

Active Publication Date: 2022-03-08
DONGGUAN YICHENG PRECISION MOLD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although there are many improvement methods for golf head materials in the prior art, they cannot meet the increasing market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of golf head material and its preparation process and ball head striking surface
  • A kind of golf head material and its preparation process and ball head striking surface
  • A kind of golf head material and its preparation process and ball head striking surface

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A golf head material, prepared from the following raw materials, 3% of the raw materials, 8% of the aluminum powder, 8% chromium powder, 3% nickel powder, 0.5% manganese powder, 0.5% iron powder, Titanium powder;

[0049] The preparation method of the golf head material includes the following steps:

[0050] S1 injects the melt wax into the mold and produces a wax mold of a golf ball;

[0051] S2 is applied using a wax mold to form a ceramic housing to form a ceramic housing, then the wax mold is melted, leaving a ceramic housing;

[0052] After S3 sintering the ceramic housing, forming a ceramic shell mold, a smelting of vanadium powder, aluminum powder, chromium powder, nickel powder, manganese powder, iron powder, titanium powder, smelting the furnace in sequch, first according to the rate of 22 ° C / min. After 1,45 min, then heated at a rate of 2 ° C / min to 1700 ° C, after holding 40 min, then heated to 2300 ° C at a rate of 3 ° C / min, after 15min, the liquid raw m...

Embodiment 2

[0054] A golf head material, prepared from the following raw materials, 1%, aluminum powder, 4%, chromium powder, 8%, 0.1%, iron powder, 1.5%, 0.5% iron powder It is titanium powder.

[0055] The preparation method of the golf head material includes the following steps:

[0056] S1 injects the melt wax into the mold and produces a wax mold of a golf ball;

[0057] S2 coat the wax mold to form a ceramic housing to form a ceramic housing, and then melt the wax mold, leaving a ceramic housing;

[0058] After S3 sintering the ceramic housing, forming a ceramic shell mold, a smelting of vanadium powder, aluminum powder, chromium powder, nickel powder, manganese powder, iron powder, titanium powder, first smelting the furnace, first in accordance with the rate of 20 ° C / min. 1000 ° C, after 30 min, then heated to 1600 ° C at a rate of 1 ° C / min, after 30min, then heated to 2200 ° C at a rate of 1 ° C / min, after holding 10 min, to obtain a liquid raw material, and inject liquid raw...

Embodiment 3

[0060] A golf head material, prepared from the following raw materials in accordance with the mass percentage: 5% vanadium powder, 1% of the aluminum powder, 10% chromium powder, 1% nickel powder, 1% manganese powder, 0.1% iron powder, It is titanium powder.

[0061] The preparation method of the golf head material includes the following steps:

[0062] S1 injects the melt wax into the mold and produces a wax mold of a golf ball;

[0063] S2 is applied using a wax mold to form a ceramic housing to form a ceramic housing, then the wax mold is melted, leaving a ceramic housing;

[0064] After S3 sintering the ceramic housing, form a ceramic shell mold, a smelting of vanadium powder, aluminum powder, chromium powder, nickel powder, manganese powder, iron powder, and titanium powder, first smelting the furnace, first by 25 ° C / min. 1200 ° C, holding up 60 min, and then heated to 1800 ° C at a rate of 5 ° C / min, after holding up 60 min, then heated to 2500 ° C at a rate of 5 ° C / ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of golf head preparation, and in particular relates to a golf head material, a preparation process thereof and a ball head striking surface. The golf head material is prepared from the following raw materials: vanadium powder, aluminum powder, chromium powder, nickel powder, manganese powder, iron powder and titanium powder. It has good elastic properties and hardness properties, and also has good tensile properties.

Description

Technical field [0001] The present invention belongs to the technical field of golf ball preparation, and more particularly to a golf head material and a preparation process and a ball strike surface. Background technique [0002] Golf is usually divided into three categories: wooden head, hardcore head and push rod. The design of the golf ball in the competition is used in the design of the size, shape, volume, feature time, inertial force torque, and recovery coefficients, etc. in the design. As the functional requirements continue to increase, the material applied to the golf ball is made from the earliest mountain hull, persimmon wood, gradually evolved into the currently commonly used titanium alloy, stainless steel and iron-based materials. In order to match the market, it is important in material selection. [0003] During the development of the ball material, the solid head of the early persimmon, the strength is low, but the metal materials used today, not only make the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C14/00C22C1/02B22C9/04B23P15/00A63B53/04
CPCC22C14/00C22C1/02B22C9/04B23P15/00A63B53/04
Inventor 朱明洲游佳谦
Owner DONGGUAN YICHENG PRECISION MOLD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More