Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Formula and preparation method for environment-friendly EVA foamed sole

An environmentally friendly and formulated technology, applied in shoe soles, footwear, applications, etc., can solve problems such as high material cost, poor mold release, and poor performance of shoes, so as to reduce production costs, save production aids, The effect of improving the quality of shoes

Inactive Publication Date: 2021-11-23
中山精美鞋业有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides an environmentally friendly EVA foam sole formula and preparation method, which solves the problems of poor demoulding of the existing EVA sole, high material cost and weak shoe sole friction during use. poor performance issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formula and preparation method for environment-friendly EVA foamed sole
  • Formula and preparation method for environment-friendly EVA foamed sole
  • Formula and preparation method for environment-friendly EVA foamed sole

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039]The embodiment of the present invention provides a kind of environment-friendly EVA foam sole formula, comprises the raw material of following mass parts: EVA raw material 70 parts, POE raw material 15 parts, thermoplastic ethylene propylene rubber 5 parts, polyvinyl cerate 5 parts, octene 2 8 parts of ethylene, 15 parts of high polymer with amide groups, 2 parts of dicumyl peroxide, 0.2 parts of bis-tert-butyl peroxide cumene, 0.4 parts of palmitic acid, 20 parts of silica gel, 5 parts of talcum powder The POE raw material increases the internal cohesion of the EVA material, increases the strength of the sole, and at the same time improves the strength of the sole, making the sole resistant to impact and improving the bending resistance of the sole; thermoplastic ethylene propylene rubber and polyvinyl cerate The addition of EVA foam soles can release the mold well during manufacturing, and the addition of raw materials can improve the mechanical strength of the soles, s...

Embodiment 2

[0061] The embodiment of the present invention provides an environmentally friendly EVA foam sole formula, including the following raw materials in parts by mass: 85 parts of EVA raw materials, 25 parts of POE raw materials, 15 parts of thermoplastic ethylene propylene rubber, 8 parts of polyvinyl cerate, 10 parts of octene 19 parts of ethylene, 26 parts of high polymer with amide groups, 5 parts of dicumyl peroxide, 0.2 parts of di-tert-butyl peroxide cumene, 2 parts of palmitic acid, 30 parts of silica gel, 13 parts of talcum powder share.

[0062] The amide group high polymer is polyamide or polyurethane, and the particle size of talcum powder is 500 mesh.

[0063] A kind of preparation method of environment-friendly EVA foam sole formula, comprises the following steps:

[0064] S1, raw material preheating, use internal mixer to preheat EVA raw material and thermoplastic ethylene propylene rubber;

[0065] S2, raw materials are mixed and melted, and the high polymer of am...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
thicknessaaaaaaaaaa
widthaaaaaaaaaa
Login to View More

Abstract

The invention provides a formula and a preparation method for an environment-friendly EVA foamed sole, and relates to the technical field of shoemaking. The formula for the environment-friendly EVA foamed sole comprises the following raw materials in parts by mass: 70-85 parts of an EVA raw material, 15-25 parts of a POE raw material, 5-15 parts of thermoplastic ethylene propylene rubber, 5-8 parts of polyvinyl acetate, 2-10 parts of octylene, 8-19 parts of ethylene, 15-26 parts of a high polymer of an amide group, 2-5 parts of dicumyl peroxide, 0.2-0.8 part of bis(tert-butylperoxyisopropyl)benzene, 0.4-2 parts of palmitic acid, 20-30 parts of silica gel and 5-13 parts of talcum powder. The sole can be well demolded during shoemaking to ensure that the sole has good quality; the sole is well foamed to save raw material cost; and a shoe has good friction performance through silica gel particles.

Description

technical field [0001] The invention relates to the technical field of shoemaking, in particular to an environmentally friendly EVA foamed shoe sole formula and a preparation method. Background technique [0002] EVA sole is a sole made of EVA material. EVA sole has high resilience, high tensile strength, high toughness, good shock resistance, cushioning performance, excellent heat preservation, cold resistance and low temperature performance. EVA sole is characterized by good softness, rubber General elasticity, good flexibility below 0°C, good transparency and surface gloss, good chemical stability, good aging resistance and ozone resistance, and non-toxic. Good blendability with fillers, good coloring and molding processability. [0003] Now in the production and processing of EVA foam soles, often because of the particularity of EVA materials, the sole materials cannot be released well after injection molding. Therefore, many shoe-making processes will use various metho...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/08C08L23/16C08L31/04C08L77/00C08L75/04C08K5/14C08K3/34C08K5/09C08K3/36C08K13/02C08J9/00A43B13/04
CPCC08J9/0061C08J9/0095C08J9/0066C08J9/0023A43B13/04C08J2323/08C08J2423/08C08J2423/16C08J2431/04C08J2477/00C08J2475/04
Inventor 张聪渊张桓章
Owner 中山精美鞋业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com