An anti-static fabric and wear-resistant technology, which is applied in the direction of wear-resistant fibers, textiles, fabrics, etc., can solve the problems of reducing the comfort of fabrics, fabric hand feeling, etc., to achieve faster dissipation rate, eliminate static electricity, and reduce surface resistance Effect

Inactive Publication Date: 2021-12-10
深圳市流遇实业有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides an anti-static fabric with strong wear resistance and its preparation method, which solves the problem that the hand feeling of the fabric after finishing with the antistatic agent PEE will decrease and the comfort of the fabric will be reduced. The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] An anti-static fabric with strong wear resistance, comprising the following raw materials in parts by weight: 60 parts of wool fiber, 40 parts of bamboo charcoal polyester fiber, and 3 parts of composite finishing agent;

[0034] The antistatic fabric with strong abrasion resistance is prepared by the following steps:

[0035] Step 1. Add the composite finishing agent into purified water, adjust the concentration of the composite finishing agent to 12g / L, then adjust the pH value of the composite finishing agent to 4, and set aside;

[0036] Step 2: Pour the treated composite finishing agent into a baking container, then pre-baking the wool fiber and bamboo charcoal polyester fiber, the pre-baking treatment temperature of the wool fiber and bamboo charcoal polyester fiber is 350 ° C, and then the wool fiber Bamboo charcoal polyester fibers are subjected to two dipping and two rolling treatments in the composite finishing agent, the baking temperature is set to 140°C, an...

Embodiment 2

[0045] An anti-static fabric with strong wear resistance, comprising the following raw materials in parts by weight: 70 parts of wool fiber, 50 parts of bamboo charcoal polyester fiber, and 5 parts of composite finishing agent;

[0046] The antistatic fabric with strong abrasion resistance is prepared by the following steps:

[0047] Step 1. Add the composite finishing agent into purified water, adjust the concentration of the composite finishing agent to 13g / L, then adjust the pH value of the composite finishing agent to 5, and set aside;

[0048] Step 2: Pour the treated composite finishing agent into a baking container, then pre-baking the wool fiber and bamboo charcoal polyester fiber, the pre-baking treatment temperature of the wool fiber and bamboo charcoal polyester fiber is 350 ° C, and then the wool fiber Bamboo charcoal polyester fibers are subjected to two dipping and two rolling treatments in the composite finishing agent, the baking temperature is set to 140°C, an...

Embodiment 3

[0057] A preparation method of an anti-static fabric with strong wear resistance, comprising the following steps:

[0058] Step 1. Add the composite finishing agent into purified water, adjust the concentration of the composite finishing agent to 13g / L, then adjust the pH value of the composite finishing agent to 4, and set aside;

[0059] Step 2. Pour the treated composite finishing agent into a baking container, then pre-baking the wool fiber and bamboo charcoal polyester fiber, and then perform double dipping and two rolling treatments on the wool fiber and bamboo charcoal polyester fiber in the composite finishing agent. Set the baking temperature to 150°C and the baking time to 90s to complete the surface treatment of wool fibers and bamboo charcoal polyester fibers;

[0060] Step 3. Blending the surface-treated wool fiber and bamboo charcoal polyester fiber to obtain warp and weft yarns, put the warp and weft yarns into the singeing machine for singeing treatment, put th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-wear-resistance antistatic fabric and a preparation method thereof. The high-wear-resistance antistatic fabric comprises the following raw materials in parts by weight of 60-70 parts of wool fibers, 40-50 parts of bamboo charcoal polyester fibers and 3-5 parts of a composite finishing agent. According to the high-wear-resistance antistatic fabric, the fibers are subjected to high-temperature finishing by using the composite finishing agent, hydrophobic groups in a product a are combined to or close to the surfaces of the hydrophobic fibers under a high-temperature condition, and hydrophilic groups-polyether components are arranged towards one side of air, so that directional arrangement is formed on an interface of the air and the fibers; the hydrophilic groups can absorb moisture in the air and form a layer of water film with relatively good conductivity on the surface of the fiber, so that the dissipation rate of surface charge of the fabric is increased, the surface resistance of the fiber is reduced, and the effect of eliminating static electricity is achieved; and in addition,a fatty long chain is added into the composite finishing agent, so that polyester chain segments and polyester molecules are subjected to a co-melting and eutectic effect, and the antistatic effect of the fabric is effectively improved.

Description

technical field [0001] The invention relates to the technical field of fabrics, in particular to an antistatic fabric with strong wear resistance and a preparation method thereof. Background technique [0002] Fabric is the material used to make clothing. As one of the three elements of clothing, fabrics can not only interpret the style and characteristics of clothing, but also directly affect the color and shape of clothing. Common clothing fabrics include cotton, linen, silk, woolen, chemical fiber, blended, and modal. [0003] Usually, in the process of friction between different fabrics, the surface of the fabric will generate static charges, especially for various acrylic fabrics, when the clothes made of this kind of fabrics are taken off, they will rub against the inner layer of clothing, which will easily generate high-voltage charges , and break down the air between the inner and outer layers of clothing to form static electricity, which will frighten and harm the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityApplications(China)
IPC IPC(8): D06M15/11D06M15/09D06M15/507D06M15/53D06M15/643D06M15/03D06M13/463D06M13/148D03D15/58D03D15/533D03D15/47D03D15/283D03D15/233D06M101/12D06M101/32
CPCD06M15/11D06M15/09D06M15/03D06M13/148D06M15/507D06M15/53D06M15/6436D06M13/463D03D15/47D03D15/233D03D15/283D03D15/533D03D15/58D06M2101/12D06M2101/32D06M2200/35D10B2211/02D10B2331/04
Inventor罗欣玲
Owner深圳市流遇实业有限公司