Aerogel modified magnesium oxysulfate fireproof insulation board and preparation method thereof
A fire-proof insulation board and aerogel technology are applied in the field of materials to achieve the effects of low density, improved thermal insulation performance and good thermal insulation performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0088] Example 1
[0089] A method for preparing a gas gel modification of a phlioside fire insulation plate, including the following steps:
[0090] 34 kg of industrial seven aqueous magnesium sulfate was added to 22 kg of water, and thoroughly stirred and dissolved, and the magnesium sulfate solution was obtained. Gradually addition to 0.7kgeva rubber powder, 1.2kg citric acid, 10kg gas gel complex powder, mixed powder, high-speed dispersion of 60 min at 300-3000r / min through high speed dispersing machine, and achieve change Magnesium sulfate solution. Then, 19kg lightly magnesium oxide powder (lightly magnesium oxide content is not less than 80%), stirring is stirred at a thorough slurry, and the slurry is sent into the plate machine for template filling, double-sided After the alkali-resistant mesh cloth and the roller are gradually solidified to obtain a wet plate, the wet plate is cut, and the natural maintenance is obtained, that is, the thiragmic oxide sheet is obtained....
Example Embodiment
[0093] Example 2
[0094] A method for preparing a gas gel modification of a phlioside fire insulation plate, including the following steps:
[0095]44 kg of industrial seven aqueous magnesium sulfate was added to 33 kg of water, and thoroughly stirred and dissolved, and the magnesium sulfate solution was obtained. In the mixed powder of 1.0kgeva rubber powder, 1.0kg citric acid, 15kg airgel composite powder, high-speed dispersion is 60 min, resulting in a high speed dispersion of 300-3000r / min, and is modified. Magnesium sulfate solution. Then add 38kg lightly magnesium oxide powder, stir well, form a homogeneous slurry, the slurry is fed into the plate machine, and the double-sided tolerate the alkalib fiber non-woven felt and the rolls, gradually solidify The wet plate, the wet plate is cut, and the natural maintenance is complete, that is, the thiragmic oxide plate, such as figure 2 As shown, Fig. A is a common thiraminated magnesium oxide plate, and Fig. B is a gas gel modi...
Example Embodiment
[0098] Example 3
[0099] A method for preparing a gas gel modification of a phlioside fire insulation plate, including the following steps:
[0100] 39kg industrial seven aqueous magnesium sulfate was added to 33 kg of water, and thoroughly stirred and dissolved, and the magnesium sulfate solution was obtained. Adding a mixed powder from 0.5 kGeva rubber powder, 1.0kg citric acid, 13kg gas gel composite powder, high-speed dispersion 60min by high-speed dispersing machine with a high speed of 300-3000r / min, and modified Magnesium sulfate solution. Then add 38kg of lightly magnesium oxide powder, stirred for 5 min, form a homogeneous slurry, the slurry is fed into the plate machine, and the double-sided to the alkali-resistant glass mesh cloth and the rolls are gradually solidified. The wet plate, the wet plate is cut, and the natural maintenance is obtained, that is, the thio-oxide sheet is obtained.
[0101] In this example, the gel composite powder is torn with a gas gel compo...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Thermal conductivity | aaaaa | aaaaa |
Density | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap