Easily degreased coated steel plate, preparation method thereof and painted steel plate

A technology of coating steel plate and coating, applied in coating, hot dipping process, solid diffusion coating, etc., can solve problems such as ineffective degreasing

Pending Publication Date: 2022-02-18
SHOUGANG CORPORATION
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The application provides an easy degreasing coated steel plate and its preparation method and application to solve the technical problem that the zinc-aluminum-magnesium coated steel plate cannot be effectively degreased in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Easily degreased coated steel plate, preparation method thereof and painted steel plate
  • Easily degreased coated steel plate, preparation method thereof and painted steel plate
  • Easily degreased coated steel plate, preparation method thereof and painted steel plate

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] Such as figure 2 , In one embodiment of the present application, there is provided an easy method for preparing defatted plated steel sheet, the method comprising:

[0035] . S1 obtain a bath containing the chemical composition of the magnesium aluminum coating and preheated to afford preheating bath;

[0036] As an alternative embodiment, the preheating temperature of the bath was 400 ℃ -500 ℃, the preheating temperature of the steel substrate of 400 ℃ -500 ℃;

[0037]In the present application, it is an object of controlling the temperature of 400 ° C to 500 ° C in the preheating plating solution to prevent too low of the plating solution; when the temperature range is too large, since the steel sheet is at a higher temperature. In the plating solution, the Fe element in the steel sheet will quickly react rapidly in the plating solution, forming a coarse-containing compound particulate matter containing Si and Mg, and deteriorating the toughness of the plating layer, resu...

Embodiment 1

[0048] The chemical composition of zinc aluminum magnesium plating is: mg: 1%, Al: 1%, margin is Zn and inevitable impurity elements;

[0049] The porosity of the porous oxide film is 20%, and the hole depth accounts for 100% of the thickness of the porous oxide film layer. The thickness of the porous oxide film is 100 nm, and the aperture depth is 100 nm;

[0050] The mass fraction of oxygen in the oxidative atmosphere is 0.3%, and the heating temperature in the controlled oxidizing atmosphere is 100 ° C, and the heating time is 10 s in the oxidizing atmosphere;

[0051] The preheating plating solution has a temperature of 480 ° C, and the temperature of the preheating steel matrix is ​​480 ° C.

Embodiment 2

[0053] The chemical ingredient of zinc aluminum magnesium plating is: mg: 1.2%, Al: 2%, margin is Zn and inevitable impurity elements;

[0054] The porosity of the porous oxide film is 25%, the hole depth accounts for 97% of the thickness of the porous oxide film layer, and the thickness of the porous oxide film is 100 nm, and the aperture depth is 97 nm;

[0055] The mass fraction of oxygen in the oxidation atmosphere is 0.8%, and the heating temperature in the oxidizing atmosphere is 120 ° C, and the heating time is 20 s in the oxidizing atmosphere;

[0056] The temperature of the preheating plating solution was 400 ° C, and the temperature of the preheating steel matrix was 430 ° C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of steel hot dipping treatment, and particularly relates to an easily degreased coated steel sheet, a preparation method thereof and the application thereof.The coated steel sheet comprises a steel substrate and a coating, the coating comprises a zinc-aluminum-magnesium coating and a porous oxidation film, the innermost layer of the coating is the zinc-aluminum-magnesium coating, and the outermost layer of the coating is the porous oxidation film layer; the porous oxidation film layer is an oxidation film layer of the zinc-aluminum-magnesium coating; the method comprises the steps that a plating solution containing chemical components of the zinc-magnesium-aluminum coating is obtained and preheated, and a preheated plating solution is obtained; a preheated steel base body is obtained; the preheated steel base body is placed in the preheated plating solution to be subjected to hot dipping treatment, and a first steel plate is obtained; the first steel plate is heated in an oxidizing atmosphere and then cooled to the room temperature, and a plated steel plate is obtained; according to the application, the coated steel plate is applied to production of vehicle parts and household appliances needing to be painted. By controlling the components of the zinc-aluminum-magnesium coating and the process conditions of the oxidizing atmosphere, the coated steel plate with good degreasing effect and high corrosion resistance can be obtained.

Description

Technical field [0001] The present application belongs to hot-dip steel processing technology, and in particular relates to an easily skimmed plated steel sheet and painted steel and its preparation method. Background technique [0002] Zinc hot dipping treatment is molten zinc and alloys steel substrate reaction, thereby forming a strong metallurgical bonding coating; Zinc hot dip coating steel, having a strong bonding force, good corrosion resistance, a long life is simple, the manufacturing process, the product low price, demand in many different industries such as the automotive industry, electrical industry and the construction industry is increasing. [0003] The most commonly used hot-dip zinc plating process of aluminum-magnesium plated zinc, magnesium, and zinc-magnesium and aluminum-plated surface is easy to form a dense oxide film fine air environment, very polar polarity oxide thin film adsorbable oil molecules, difficult to remove, remove the skim coated steel diffic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C2/06C23C2/26C23C2/40C23C8/10C22C18/00C22C18/04
CPCC23C2/06C23C2/40C23C2/26C23C8/10C22C18/04C22C18/00
Inventor 蒋光锐刘广会李研王海全商婷滕华湘
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap