Water-soluble cushion of internal container in thermos

A water-soluble, bile pad technology, applied in the field of thermos bottle bile pad, can solve the problems of poor heat preservation effect of thermos, piercing into the cavity wall of the respiratory tract, and inflammation of the respiratory tract of operators, and achieves sufficient supply, asbestos material saving, and rich materials. Effect

Inactive Publication Date: 2004-03-17
王荣生
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, asbestos is the main ingredient used in thermos bottle liner pads, and its material form is fiber and powder. The disadvantage is that in the production process of preparation, molding and drying, its material form is fiber and powdery asbestos. In the air, it is inhaled into the respiratory tract by the operator, causing inflammation of the operator's respiratory tract, and even fibrous asbestos penetrates into the cavity wall of the respiratory tract, causing the operator to suffer from respiratory tract cancer. The water-soluble liner pad is used as the inner and outer bottle of the thermos The support body of the liner is still retained when the inner and outer liner are silver-plated, so that the liner pad and its surroundings cannot be plated with silver, making the insulation effect of the thermos bottle poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The present invention will be described in further detail below in conjunction with embodiment:

[0021] Press the prescription composition weight ratio (%) of thermos bottle liner pad, the weight of each composition of following table, respectively prepare 100 gram materials and make bottle liner pad.

[0022] Components Embodiment one (grams) Embodiment two (grams) Embodiment three (grams)

[0023] Meerschaum 10 5 15

[0024] Light calcium carbonate 20 15 10

[0025] Calcium carbonate 50 70 60

[0026] Bentonite 2 2 2

[0027] Silica 10 5 5

[0028] Clay 2 2 2

[0029] Water-soluble natural gum 6 1 6

[0030] Each material in the table, its purity is industrial use, and its each embodiment formula can all meet the requirement of liner liner.

[0031] The role and function of each component are as follows:

[0032] Light calcium carbonate can adjust the softness and hardness of the liner pad of the thermos bottle.

[0033] Natural rubber is an adhesive, and th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A water-soluble pad for the internal container of thermos is prepared from sepiolite (5-15 wt%), calcium bicarbonate (10-20), triple superphosphate (50-70), bentonite (2), powdered stone (5-15), pottery clay (2) and natural colloid (1-6) through mixing them with ionized water, die-pressing into sheet, and baking. Its advantages include high insulating effect, no damage to human body and no environmental pollution.

Description

technical field [0001] The invention relates to a thermos liner pad, in particular to a formula for a water-soluble thermos liner pad. The bottle liner pad made of this group of materials is used as the bottle liner pad for the inner and outer bottle liners of the thermos bottle. Compared with bottle liner pads made of other materials, the heat preservation effect is better, and its production and production process are harmless to human body and have no pollution to the environment. Background technique [0002] At present, asbestos is the main ingredient used in thermos bottle liner pads, and its material form is fiber and powder. The disadvantage is that in the production process of preparation, molding and drying, its material form is fiber and powdery asbestos. In the air, it is inhaled into the respiratory tract by the operator, causing inflammation of the operator's respiratory tract, and even fibrous asbestos penetrates into the cavity wall of the respiratory tract,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A47J41/02C03B9/00
Inventor 王荣生钟会生
Owner 王荣生