Welding device and welding method for fixed contact assembly of molded case circuit breaker

Abstract

The welding device comprises a support supporting seat, a ceramic pressing rod and two electrodes, the support supporting seat is used for supporting a support, the ceramic pressing rod presses an arc striking angle and a contact to the support, and the two electrodes abut against the two sides, opposite to the arc striking angle and the contact, of the support respectively. By the adoption of the scheme, the welding device and method for the fixed contact assembly of the molded case circuit breaker can complete the high-quality welding process of three parts made of different materials such as a support, a contact and an arc striking angle at a time, welding flux overflows evenly on the appearance of a contact assembly product, the welding brazed rate is larger than or equal to 85%, and the welding quality is improved. And the shear force and metal phase performance indexes are good.

Description

technical field [0001] The invention relates to the field of welding electric contact element processing, in particular to a welding device and a welding method for a static contact assembly of a molded case circuit breaker. Background technique [0002] A circuit breaker is a switching device that can close, carry and break current under normal circuit conditions and can close, carry and break current under abnormal circuit conditions within a specified time. Circuit breakers are divided into high-voltage circuit breakers and low-voltage circuit breakers according to their scope of use. The division of high and low voltage boundaries is relatively vague. Generally, those above 3kV are called high-voltage electrical appliances. [0003] Circuit breakers can be used to distribute electric energy, start asynchronous motors infrequently, protect power lines and motors, and automatically cut off the circuit when they are severely overloaded, short-circuited, or under-voltage. It...

AI Technical Summary

Problems solved by technology

[0005] If induction brazing is used, this process has the characteristics of welding multiple parts at one time, but when the contact and arc striking angle are heated at the same time, since the arc striking angle is made of copper-plated iron and the contact is made of silver graphite, the arc striking angle will heat first To the red state, when the solder reaches a completely melted state, there will be a problem of overburning at the arc striking angle, which will affect the welding appearance of the product and the quality of the electroplating. Close to the bending position of the bracket, first heat the bracket to a red state, melt the solder through the heat conduction of the bracket itself, and then complete the welding between the arc strike angle and the bracket, which will lead to severe annealing of the bracket and a large drop in material hardness. The deformation of the bracket occurs during subsequent transportation, electroplating and other operations, which ultimately affects the performance of the product

[0006] If the traditional metal electrode direct resistance brazing process is used, the welding of the bracket and the contact must be completed first. Usually, in order to ensure the welding strength of the product, there will be obvious solder overflow around it after static contact welding. In the arc angle, there will inevitably be a certain assembly gap between the arc strike angle and the contact, but in order to ensure the performance of the molded case circuit breaker switch product, the customer clearly requires the static contact and arc strike angle in the static component drawing There should be no obvious gap after welding, so it is necessary to polish the solder at

Images