Manufacturing process of high-strength round-link chain

A manufacturing process, a technology of circular link chains, applied in the field of circular link chains, can solve problems such as difficult pre-control of balance, poor transmission efficiency, local bending, etc., to improve life and transmission efficiency, increase effective welding area, size and shape standard effect

Pending Publication Date: 2022-07-29
王瑞丰
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the manufacturing process of high-strength round link chains is mostly the same. Usually, the high-strength alloy steel is used to cut the bar to make the bar, and the chain knitting machine is used to bend it into an oblong link composed of two straight arms and two arc-shaped ends. Into the chain, and finally use flash butt welding to weld the joints. In the above-mentioned existing manufacturing process, the chain link is usually bent from a bar to form a single joint structure. During the flash butt welding process The chain link will be shortened longitudinally by the upsetting force, and the two joints will have a certain material loss due to the extrusion of the molten material on the joint surface, and the other straight arm without the joint will be correspondingly deformed by plastic deformation. Shortening, there is no material loss, which leads to the unequal size and shape of the two straight arms of the formed link; at the same time, there is no balance of plastic deformation produced by the straight arms of the joint during the upsetting process It is difficult to pre-control, and there may even be significant uneven deformation such as local bending and local coarseness; in addition, during the upsetting process, the two arc-shaped ends are often compressed to a certain extent and the deformation state is difficult to control; the above factors lead to , the shape of the links of the round link chain produced by the existing technology is not standard and uniform, the force distribution of the links is not balanced during the working process, and the poor matching between the links and between the links and the sprockets is prone to occur. Unfavorable phenomena such as chain skipping, tooth beating, difficulty in tooth removal, etc., the wear rate is high, and eventually the working life of the round link chain is low, the transmission efficiency is poor, and the chain is easy to break during the working process
In addition, when using the existing technology to manufacture high-strength round link chains, it is necessary to drive the overall longitudinal shortening of the link chain during the upsetting link of flash butt welding. On the one hand, the manufacturing cost of the round link chain is increased due to the large material loss; The required upsetting force is relatively large, which increases the power consumption of production equipment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Manufacturing process of high-strength round-link chain
  • Manufacturing process of high-strength round-link chain
  • Manufacturing process of high-strength round-link chain

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The manufacturing process of the high-strength circular chain disclosed in the present invention will be described in detail below with reference to the embodiments.

[0034] 23MnNiMoCr54 alloy steel is a commonly used high-strength chain steel. The high-strength circular chain made of it has the characteristics of good grinding performance, high fatigue times, high strength, strong impact resistance, and large bearing load. The circular chain is made of 23MnNiMoCr54 alloy steel.

[0035] The manufacturing process of the high-strength circular chain disclosed by the present invention comprises the following steps:

[0036] 1. Prefabricated bars and pretreatment

[0037] see Figure 1-3 As shown in the figure, according to the requirements of the type of high-strength circular chain to be produced, select the alloy steel round bar or wire rod of the corresponding specification, carry out the straightening treatment, and use the precision bar shearing machine to cut the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of round-link chains, and particularly discloses a manufacturing process of a high-strength round-link chain, which comprises the following steps of: 1) prefabricating a bar and manufacturing two ends into inclined surface ends, 2) pre-bending the bar into a special-shaped ring body comprising two U-shaped parts, 3) connecting the special-shaped ring body with an adjacent chain ring, twisting the two U-shaped parts to enable the two inclined surface ends to be locally lapped and propped, and 4) manufacturing the high-strength round-link chain. (4) welding the two inclined surface ends by utilizing flash butt welding to enable the two inclined surface ends to be matched and forged together to form a closed long circular chain ring, (5) carrying out surface treatment and heat treatment, and (6) carrying out post-treatment on the round-link chain after forming to obtain the high-strength round-link chain. Chain rings of the round-link chain manufactured through the technology are balanced in stress and low in abrasion efficiency, the effective welding area is increased, the connection strength is improved, finally, the strength, the service life and the transmission efficiency of the round-link chain are remarkably improved, the chain breakage situation is greatly reduced, upsetting allowance is not needed, the material cost of the round-link chain is reduced, and the production cost is reduced. And meanwhile, the power consumption of upsetting equipment is reduced.

Description

technical field [0001] The invention relates to the technical field of circular ring chains, in particular to a manufacturing process of a high-strength circular ring chain. technical background [0002] The circular chain is widely used in mining machinery, ships, lifting equipment and other fields. It is often used as a traction and transmission component of large power equipment. Once the chain is broken during its work, it will cause the equipment to fail to operate and affect the operation of the entire working face. The production process can even lead to safety accidents, so the ring chain has extremely high requirements for strength and safety. At present, the manufacturing process of high-strength circular chain is mostly the same. Usually, high-strength alloy steel is used to produce bar material, and a chain braiding machine is used to bend it into an oblong chain ring composed of two straight arms and two arc ends. It is woven into the chain, and finally the joi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21L3/02B21L19/00
CPCB21L3/02B21L19/00
Inventor 王瑞丰
Owner 王瑞丰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products