Baking-free slag brick and method of making same
A production method and waste residue technology are applied in the field of non-burning waste residue bricks and their production, which can solve the problems of complex production equipment, difficult popularization and high cost, and achieve the effects of good hydration, easy release and high yield.
Inactive Publication Date: 2005-01-19
张庆军 +1
View PDF3 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Chinese patent application 87108093.1 "Manufacturing method of slag bricks for construction" uses construction waste as the main raw material, but after the bricks are formed, they still need high-pressure steam curing, which consumes a lot of energy, costs high, and the production equipment is complicated, so it is difficult to popularize
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0014] Raw material weight ratio is as follows:
[0015] 36-43% of construction waste, 44-51% of inferior rock, 12-20% of cement; 1-2% of its weight water reducer is added to the cement.
Embodiment 2
[0017] Raw material weight ratio is as follows:
[0018] Construction waste 36-43%, inferior rock 44-51%, cement 7-13%, fly ash 5-8%.
Embodiment 3
[0020] The weight ratio of raw materials is as follows: 36-43% of construction waste, 44-51% of inferior rock, 5-10% of cement, 3-6% of fly ash, and 3-6% of lime.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| compressive strength | aaaaa | aaaaa |
Login to View More
Abstract
The baking-free slag brick is produced with building slag, inferior stone, cement with water-reducing agent in 1-2 % added, flash and lime. The production process includes the steps of: crushing and grinding material, mixing, pressure molding at the pressure of 170-200 kg / sq cm to form adobe, and curing of the adobe at temperature over 0 deg.c for over 15 days. The utilization of building slag can reduce pollution and lower cost.
Description
(1) Technical field [0001] The invention relates to a building block and a manufacturing method thereof, in particular to a burning-free waste slag brick and a manufacturing method thereof. (2) Technical background [0002] Traditional clay bricks use a large amount of clay for firing, which consumes a lot of energy, destroys fields and occupies land, and is not conducive to environmental protection. The general cement bricks are formed by mixing gravel, sand, cement and chemical additives with water and vibrating. Although it is non-burning, it not only has high cost, but also has a rough surface and poor compactness, which affects its use. [0003] There are many kinds of waste slag bricks with cinder or slag as raw materials, such as Chinese patent application 02100218.5 "unfired hollow brick", which uses quicklime, burned coal gangue, slag, cement clinker, clay and boiler slag as raw materials; 01102954.4 "a Process method for rapid production of fly ash blocks or fly ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): B28B3/00C04B18/08C04B18/16C04B28/02E04C1/00
CPCY02W30/91
Inventor 张庆军
Owner 张庆军