Transfer sheet for transferring protective layer for photographic emulsion face and photomask with protective layer

A photographic emulsion and protective layer technology, applied in the field of photomasks, can solve the problems of difficulty in practical use, damage to the emulsion surface, difficulty in controlling film thickness, etc.

Inactive Publication Date: 2005-10-12
NIPPON PAPER IND CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, with this method, since 18 to 72 hours of heating etching is required, there is a possibility of damaging the emulsion surface, and in the coating process (undried coating process), it is difficult to control the film thickness, which is difficult for practical use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transfer sheet for transferring protective layer for photographic emulsion face and photomask with protective layer
  • Transfer sheet for transferring protective layer for photographic emulsion face and photomask with protective layer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] ① Preparation of support

[0057] On the surface of a polyethylene terephthalate (hereinafter referred to as PET) film with a thickness of 50 μm stretched biaxially, the following peeling layer forming liquid is coated with a roll coater, and dried for 1 minute at 130° C. Thus, a peeling layer having a thickness of 2 μm was formed.

[0058]

[0059] (a) Acrylamide copolymer (Tesfine 322: trade name manufactured by Hitachi Chemical Polymer Co., Ltd.): 1.8 parts

[0060] (b) Epoxy-melamine copolymer (SP-DRC No.153N: trade name manufactured by Dainippon Ink Chemical Industry Co., Ltd.): 41 parts

[0061] (c) p-toluenesulfonic acid (Dryer 900: trade name manufactured by Nippon Kasei Polymer Co., Ltd.): 0.2 parts

[0062] (d) Solvent: 46 parts of ethyl acetate

[0063] Butanone 11 parts

[0064] ②Preparation of uncured photographic emulsion surface protective layer

[0065]Apply the uncured photographic emulsion surface protective layer forming solution on the support...

Embodiment 2

[0079] A transfer film was prepared in the same manner as in Example 1, except that the uncured photographic emulsion surface protective layer-forming liquid in Example 1 was changed to the state described below. At this point, the cure index of the uncured photographic emulsion topcoat was 150.

[0080]

[0081] (Ionizing radiation curable resin composition)

[0082] (a) Trifunctional acrylate: (Aronix M-309: Toagosei Co., Ltd.): 12 parts

[0083] (b) COOH group-containing monofunctional acrylate (Aronix M-5400: trade name manufactured by Toagosei Co., Ltd.): 9 parts

[0084] (c) Polyamine (acrylic graft copolymer: L-40M trade name manufactured by Soken Chemical Co., Ltd.): 9 parts

[0085] (d) Reaction initiator: Lucirin TPO (trade name manufactured by BASF Japan Co., Ltd.): 0.1 part

[0086] (e) Diluent: ethyl acetate: 17.2 parts, butanone: 17.2 parts, ethyl cellosolve: 8.5 parts

[0087] In the same manner as in Example 1, a photomask with a protective layer was prep...

Embodiment 3

[0089] A transfer film and a photomask with a protective layer were prepared in the same manner as in Example 1, except that the uncured photographic emulsion surface protective layer forming liquid in Example 1 was changed to the state described below. At this time, the cure index of the uncured photographic emulsion topcoat was 130.

[0090]

[0091] (Ionizing radiation curable resin composition)

[0092] (a) Trifunctional acrylate: (Aronix M-309: trade name manufactured by Toagosei Co., Ltd.): 9 parts

[0093] (b) COOH group-containing monofunctional acrylate (Aronix M-5400: trade name manufactured by Toagosei Co., Ltd.): 12 parts

[0094] (c) Polyamine (acrylic graft copolymer: L-40M trade name manufactured by Soken Chemical Co., Ltd.): 9 parts

[0095] (d) Reaction initiator: Lucirin TPO (trade name manufactured by BASF Japan Co., Ltd.): 0.1 part

[0096] (e) Diluent: ethyl acetate: 17.2 parts, butanone: 17.2 parts, ethyl cellosolve: 8.5 parts

[0097] In the same m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The present invention is an invention providing a photographic emulsion surface protective layer transfer sheet, characterized by having on one surface of a releasable support a photographic emulsion surface protective layer which is adhesive and in an uncured state, and characterized in that the photographic emulsion surface protective layer in an uncured state comprises an ionized radiation-curable resin composition containing a hydrophilic group-containing monofunctional (meth)acrylate and a polyfunctional (meth)acrylate. This transfer sheet can have an adhesive layer excellent in scratch resistance, close adhesion to an emulsion surface and solvent resistance. Therefore, when this transfer sheet is used particularly for forming a protective layer on the emulsion surface of a photomask, the photomask capable of long-term consistent use is obtained.

Description

technical field [0001] The present invention relates to a transfer film used for transferring a protective layer to a photomask used for pattern formation of a printed circuit board or a display panel, and to an emulsion surface of a photomask for plate making, and to protecting the emulsion surface by the protective layer photomask. Background technique [0002] The surface protection methods of various materials are known so far. There is a method of attaching a protective layer provided with an adhesive layer on the surface of a film such as a polyester film to the surface of an object, and a protective layer is provided on a peelable film. layer, through adhesives or adhesives, the method of transferring the protective layer to the surface of the object, etc. When the protective layer is transferred to the surface of the object by such an adhesive or adhesive, although there is an advantage that a thin protective layer can be provided, the strength of the adhesive layer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G03F1/00G03F1/54
CPCG03F1/54G03F1/144G03F1/14G03F1/48B41M5/00
Inventor 高田俊彦佐久间真永岛和夫大村知伸
Owner NIPPON PAPER IND CO LTD