Process for preparing SBS aqueous emulsion
The technology of water emulsion and emulsifier is applied in the field of preparation of SBS water emulsion to achieve the effect of soft hand feeling, good compatibility and good calendering effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] In a 10L stainless steel reactor with stirring, add 20 parts of SBSM solution (in terms of SBSM mass), start stirring, first stir at a low speed, and slowly add 80 parts of water (containing 1.0 wt% sodium dodecylbenzenesulfonate in water) , 0.25wt% polyoxyethylene octylphenol ether with an ethylene oxide addition number of 10, 0.25wt% potassium chloride, and 0.2wt% defoamer CRA), at a temperature of 30-60°C, stirring at a high speed for 30min, and then At 60°C, the organic solvent was removed in vacuo. The mechanical stability of the obtained emulsion was measured by the SH / T1151-92 method, and the coagulum content was 3%.
Embodiment 2
[0027] In a 10L stainless steel reactor with stirring, add 30 parts of SBSM solution (in terms of SBSM mass), start stirring, stir at a low speed first, and slowly add 70 parts of water (water contains 0.8 wt% of ammonium oleate, ethylene oxide 0.25wt% of polyoxyethylene octylphenol ether with an addition number of 10, 0.25wt% of potassium chloride, and 0.2wt% of defoaming agent CRA), at a temperature of 30-60°C, high-speed stirring for 30min, at 60°C, pumping The organic solvent was removed in vacuo. The mechanical stability of the obtained emulsion was measured by the SH / T1151-92 method, and the coagulum content was 3%.
Embodiment 3
[0029] In a 10L stainless steel reactor with stirring, add 60 parts of SBSM solution (in terms of SBSM mass), start stirring, first stir at a low speed, and slowly add 40 parts of water (containing 2.5 wt% sodium dodecylbenzenesulfonate in water) , polyoxyethylene octylphenol ether with an ethylene oxide addition number of 10 1.0wt%, potassium chloride 0.8wt%, defoamer CRA 0.5wt%), temperature at 30-60°C, high-speed stirring for 30min, in At 60°C, the organic solvent was removed by vacuum. The mechanical stability of the obtained emulsion was measured by the SH / T1151-92 method, and the coagulum content was 4%.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com