UV solidified intaglio printing decorative ink

A gravure printing and decorative technology, applied in the field of gravure printing decorative ink, to achieve the effect of high scattering, good consistency and improved curing speed

Inactive Publication Date: 2002-11-20
潘治平
View PDF2 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to create and utilize the printing speed to be fast, and the consistency of printed products is good, and the thick gravure printing method of ink layer comes printing decorative pattern (patent applicatio...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0022] Ink composition:

[0023] Oligomer CN140 Sartomer 25 kg

[0024] CN965 Sartomer 25kg

[0025] Thinner EOTMPTA Sartomer 20 kg

[0026] TPGDA Sartomer 16 kg

[0027] Photoinitiator 819 produced by Ciba 4 kg

[0028] 2959 Ciba 4 kg

[0029] Forming agent nano SO 2 East China University of Science and Technology Institute of Superfine Materials 5 kg

[0030] Polymerization inhibitor resistance-1 produced by Shanghai Wenhua Technology and Trade Co., Ltd. 0.01 kg

[0031] Auxiliary BYK-077 (defoamer) produced by BYK company 0.5 kg

[0032] BYK-301 (slip agent) produced by BYK company 0.5 kg

[0033] Dissolve photoinitiator 819 and 2959 with TPGDA and ETMPTA first, then add other components and stir evenly. Obtain milky white more viscous UV gravure decorative ink.

[0034] Shanghai Yuncheng Plate Making Co., Ltd. uses laser engraving to make gravure printing plates. The plates co...

example 2

[0036] Ink composition

[0037] Oligomer EB616 UCB 15kg

[0038] EB205 UCB company produced 10 kg

[0039] EB830 UCB 13.5 kg

[0040] Diluent POTPGDA UCB company produced 15 kg

[0041] Produced by PONPGDA UCB Company 15kg

[0042] Photoinitiator ITX INTERNATIONAL INC. 3kg

[0043] Produced by EPD INTERNATIONAL INC. 3 kg

[0044] Shaped body TiO 2 (Nano) Shanghai Wei'an New Material Research

[0045] Center Limited 10kg

[0046] PE commercially available 10kg

[0047] Polymerization inhibitor resistance-1 produced by Shanghai Wenhua Technology and Trade Co., Ltd. 0.5 kg

[0048] Auxiliary Rad2500 (smoothing agent) produced by TEGO Company 1 kg

[0049] BENTONE SD-3 RHEOX 4 kg

[0050] First of all, the powdered polyethylene (PE) purchased from the market must be cryogenically cooled with liquid nitroge...

example 3

[0052] Oligomer CN965 produced by Sartomer 10 kg

[0053] Thinner DDA Sartomer 20 kg

[0054] POTMPTA Sartomer 20 kg

[0055] Photoinitiator 1800 produced by Ciba Company 3 kg

[0056] Formed body Talc powder (5 microns) Changxing Jinshi superfine

[0057] Powder Limited 46 kg

[0058] Inhibitor MEHQ commercially available 1 kg

[0059] Ink preparation and printing are the same as in Example 2. The printing speed is 3000 sheets / hour (about 70M / min). Printed on silver cardboard, the ink is slightly sticky after printing, and can produce patterns such as emaciated sand and refraction, but the effect is better except for coral, and the other patterns are not as good as Example 2. As in 200g / M 2 First print the light green bottom layer on the white cardboard, and then use this ink to print the coral pattern by gravure printing. It is very elegant and can be used for packaging such as tea. It starts to harden after one da...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a decorative printing ink for gravure printing, its composition is formed from (wt%) 10-50% of oligomer, 10-40% of active diluent, 3-8% of photoinitiator, 0-46% of forming agent whose fineness is less than 10 micrometer, 0.01-1% of retarder and 0-5% of adjuvant. Said UV gravure printing decorative ink possesses reduced oxyinhibition and its solidifying speed is greatly raised, for example, UV light source is 80W/CMX3, at 150M/min. it can be well solidified, and can make cross-hatch with different effects, can print various patterns of imitation metal etching (corning), dioptric, buckle, ice flower and coral form, and its storage stability is good. Said ivnented product is a colorless one, the pigment or colour ink can be added, and the colour pattern can be printed.

Description

technical field [0001] The invention relates to an ink, especially an ink used for gravure printing, which can produce various decorative patterns such as imitation metal etching (sand), refraction, wrinkles, ice flowers, coral, etc. and a strong three-dimensional effect. Patterned UV curable gravure decorative inks. Background technique [0002] At present, the decorative printing of imitation metal etching etc. all adopts the screen printing method, which I have described in detail in the article "UV Screen Printing Decorative Ink" of "Screen Printing" 2000, 6, P26-28. They have been widely used in the packaging of cigarettes, alcohol, cosmetics, and health care products. There are many kinds of UV screen printing decorative inks with single performance, some are troublesome to use, and the production capacity is low. For example, imitation metal etching ink can only be used to print patterns with a sandy surface effect, and there are many types of inks in thick, medium,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/101
Inventor 潘治平
Owner 潘治平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap