Electromagnetic casting method for aluminium-1% silicon fine wire masterbatch for integrated circuit linkage

An integrated circuit and electromagnetic casting technology, which is used in the field of preparation of metal and alloy bonding wire masterbatches, can solve the problems of coarse internal structure grains, low wire elongation, wire breakage, etc. High elongation and smooth surface

Inactive Publication Date: 2003-01-22
黄国兴
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the past, conventional vacuum melting, horizontal continuous casting, continuous casting and rolling or hot top semi-continuous casting (DC method) were mostly used. These methods not only have rough surface and many hidden dangers of cracks, but also have serious component segregation, coarse gr

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] The grade of the prepared alloy is aluminum-1% silicon, the diameter of the alloy ingot is required to be 60 mm, and the weight of the charge is 25 kg. Its electromagnetic continuous casting process is:

[0008] 1. The inductor is made. The induction coil is wound with a φ6mm hollow copper tube with an inner diameter of φ65mm and a height of 65mm, and the number of turns is 8 turns.

[0009] 2. Turn on the 2500Hz, 40-100V power supply, adjust the power, so that the electromagnetic intensity in the sensor is 25mT-100mT. (When a stirring coil is added, adjust the electromagnetic strength of the stirring induction coil to 10-80mT, and this example program does not add a stirring sensor)

[0010] 3. Melt the aluminum alloy and put it into the tundish for refining, degassing and impurity removal for later use.

[0011] 4. Connect to the cooling water channel.

[0012] 5. Adjust the dummy base to the lower end of the crystallizer. Operating procedures:

[0013] Turn on t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Current intensityaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The present invention relates to MF and HF continuous elecromagnetic casting and LF electromagnetic stirring process for preparing aluminum -1% silicon fine wire masterbatch for IC linkage. Into one special 6-120 mm inner diameter induction crystallizer, current of 1000-100000 Hz and current of 5-100 Hz are separately fed to generate electromagnetic field, so that liquid metal is suspended insidethe crystallizer. Under the action of strong electromagnetic stirring and strong water spraying cooling, liquid metal is oriented and solidified fast to realize continuous casting. The features includes excellent surface quality, homogeneous element components without segregation, compact and fine crystal structure, good ventilation, less pinhole and less oxide inclusion.

Description

Technical field [0001] The invention relates to a method for preparing an integrated circuit bonding wire masterbatch and other metal and alloy bonding wire masterbatches. Background technique [0002] Bonding wires for integrated circuits mainly refer to gold wire, silver and its alloy wire, aluminum-silicon, aluminum-magnesium, copper and its alloy, nickel, palladium alloy, etc. Because the above-mentioned metal matrix composite materials are composed of various metal elements with different melting points and different specific gravity. In the past, conventional vacuum melting, horizontal continuous casting, continuous casting and rolling or hot top semi-continuous casting (DC method) were mostly used. These methods not only have rough surface and many hidden dangers of cracks, but also have serious component segregation, coarse grains in the internal structure, pinholes, inclusions, etc. Seriously, the wire elongation is low. In the production process, wire breakage is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22D11/049
Inventor 黄国兴赵伟旦
Owner 黄国兴
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap