Special multifunction filler for wood production and its blending process

A multi-functional, wood-based technology, applied in the field of adhesive fillers, to achieve the effects of improving pre-pressing performance, improving finished product indicators, and improving cold bonding fastness

Inactive Publication Date: 2004-03-03
SHANGHAI YINGXIANG IND
View PDF0 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] b. Significantly improve the pre-pressing performance of plywood, solve the problem of synchronizing the instant viscosity change c

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Special multifunction filler for wood production and its blending process
  • Special multifunction filler for wood production and its blending process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Formula ratio: A material 55; B material 2; C material 32; D material 1; E material 1.5; F material 4; G material 4.5. Take the production of filler 1000Kg as an example, the implementation method is as follows:

[0035] 1. Take 400kg of material A calcium-based bentonite and mix it with 20kg of material B sodium carbonate, grind it for about 30 minutes, store it naturally for more than 3 days, fully carry out ion exchange and sodiumization, and then dry and grind it into artificial sodium carbonate. The degree is above 120 mesh.

[0036] 2. Grind the remaining 150kg of material A to be more than 120 mesh, and the wood flour of material C is passed through a sieving machine to obtain a fine powder of more than 80 mesh.

[0037] 3. Transfer other materials in the formula: 10kg of melamine, 15kg of adipic acid, 40kg of urea, and 45kg of oxalic acid, together with the aforementioned materials, to a high-speed rotary gravity-free mixer, shear and stir for about 20-30 minut...

Embodiment 2

[0041] Formula ratio: A material 65; B material 4; C material 16; D material 3; E material 1; F material 5; G material 6. Taking the production of filler 1000Kg as an example, the implementation mode is similar to that of Example 1, and the process is omitted.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Login to view more

Abstract

A multifunctional filler dedicated for woodworking industry is prepared from Ca-base bentone, sodium carbonate, wood powder or strew-stalk powder, melamine, adipic acid, urea and oxalic acid through mixing 60-80% of Ca-base bentone with sodium carbonate, grinding, laying aside for at least 3 days, drying, grinding by 120 meshes, and mixing with others by high-speed shearing and stirring. Its advantages are high quality of plywood and low cost.

Description

1. Technical field: [0001] The invention relates to an adhesive filler, and in particular discloses a special multifunctional filler for wood industry, which is used in the adhesive of wood-based panel manufacturing—urea-formaldehyde resin glue, as a new generation of functional filler. 2. Background technology: [0002] Urea-formaldehyde resin glue is a thermosetting polymer adhesive material widely used in the man-made plywood manufacturing industry, but it is limited by the synthesis conditions and the storage stability of the produced glue solution. The commercially available resin glue solution is very thin, with a water content of about 50 % up and down, it is more difficult to use directly. Since the advent of urea-formaldehyde resin glue in the domestic and foreign plywood industry in the 1960s, flour processed from agricultural products wheat has been added to the glue as a filler to increase the consistency and initial viscosity, so as to reduce the penetration of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J11/08
Inventor 胡飞
Owner SHANGHAI YINGXIANG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap