Low temperature decrease steel ladle pouring method

A ladle pouring and low temperature technology, which is applied in the direction of casting molten material containers, manufacturing tools, metal processing equipment, etc., can solve the problems of steel performance degradation, high superheat of molten steel in the tundish, etc., and achieve the effect of reducing the consumption of refractory materials

Inactive Publication Date: 2005-07-20
SHOUGANG CORPORATION
View PDF0 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

After the method is implemented, the molten steel in the ladle and the lining can be heated and kept warm during the steel pouring process of the casting machine, the temperature drop of the molten steel and the ladle during the steel pouring process can be reduced, and the superheat degree can be stabilized in the early and late stages of a furnace of molten steel pouring, reaching The purpose of low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low temperature decrease steel ladle pouring method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The invention will be further described below in conjunction with the accompanying drawings

[0023] 1. Install the cantilever crane

[0024] A cantilever crane is installed near the turret of the continuous casting ladle, and the function of the cantilever crane is to lift the ladle cover with the burner. When the cantilever is hoisted to a high position, ensure that there is a free space of 500mm between the ladle cover and the upper edge of the ladle sitting on the high position of the turntable of the casting machine. After the cantilever crane is lowered, the ladle cover can be covered on the ladle.

[0025] 2. Make the heating bag cover

[0026] The heating burner is installed in the center of the cover. The high-efficiency burner is used to improve the heating efficiency of the flame and ensure the effective heating of the molten steel after the liquid level is lowered. The cover is lined with light-weight refractory materials to reduce the weight of the cover ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a two temperature drop ladle pouring method. It is characterized by that in the ladel pouring process said invention utilizes gas to heat molten steel by means of high-effective nozzle mounted on the ladel cover, and utilizes bottom blowing argon to stir the molten steel. Said method can stabilize pouring basket temperature and can implement stable low overheat molten steel pouring operation.

Description

[0001] Field: [0002] The invention relates to a low-temperature drop ladle pouring method, which is mainly applicable to steelmaking plants in the metallurgical industry. Background technique: [0003] Nowadays, most metallurgical enterprises have realized full continuous casting. During the casting process of the continuous casting machine, the molten steel stays in the ladle for a long time, and the temperature drop of the molten steel in the ladle and the ladle itself is relatively large during the pouring process. The continuous casting process itself requires stable temperature of molten steel and stable superheat of molten steel in the tundish. Only when the superheat of molten steel is stable can the casting machine operate smoothly. [0004] The pouring time of continuous casting ladle is generally more than 30 minutes. The difference between the highest superheat and the lowest superheat of a furnace of steel in the pouring process is generally 6-13 degrees, that is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22D1/00B22D41/01B22D41/58
Inventor 李树森罗伯钢
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap