Method for preparing nanometer silver solution and nanometer silver powder by using high polymer as stabilizer

A technology of nano-silver and stabilizer is applied in the field of broad-spectrum antibacterial nano-silver solution and nano-silver powder preparation to achieve the effects of strong antibacterial ability, strong broad-spectrum antibacterial property and good stability

Inactive Publication Date: 2005-08-17
ZHEJIANG UNIV
View PDF2 Cites 80 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above patents all use porous materials as carriers to prepare nano-silver powders, and do not in

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing nanometer silver solution and nanometer silver powder by using high polymer as stabilizer
  • Method for preparing nanometer silver solution and nanometer silver powder by using high polymer as stabilizer

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Preparation method of nano-silver solution using high polymer as stabilizer: Dissolve 5g of chitosan in 95ml of water, add 1.69g of silver nitrate, and slowly add 5ml of aqueous solution containing 3.5g of ascorbic acid under vigorous stirring. Stirring was continued for 5-6 hours. That is, a stable nano-silver solution is obtained.

[0018] The results of transmission electron microscopy show that the average size of nano-silver particles is 100nm.

Embodiment 2

[0020] Preparation method of nano-silver solution with high polymer as stabilizer: Dissolve 0.1g of methylcellulose in 95ml of water, add 34mg of silver nitrate, and slowly add 5ml of aqueous solution containing 9mg of formaldehyde under vigorous stirring. Stirring was continued for 5-6 hours. That is, a stable nano-silver solution is obtained.

[0021] The results of transmission electron microscopy show that the particle size distribution of nano-silver particles is 80-100nm, with an average of 90nm.

Embodiment 3

[0023] Preparation method of nano-silver solution with high polymer as stabilizer: Dissolve 1g of polyvinylpyrrolidone in 95ml of water, add 16mg of silver nitrate, and slowly add 5ml of aqueous solution containing 40mg of sodium borohydride under vigorous stirring. Stirring was continued for 12-15 hours. That is, a stable nano-silver solution is obtained.

[0024] The results of transmission electron microscopy showed that the particle size distribution of nano-silver particles was 20-30nm, with an average of 27nm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to view more

Abstract

The present invention discloses the preparation process of nanometer silver solution and nanometer silver powder with polymer as stabilizer. Water soluble polymer as stabilizer in solution of 0.001-0.05 g/ml solution and silver nitrate in solution of 0.001-0.1 mol/L are compounded and reduced with water soluble reductant in solution of 0.001-0.2 mol/L to obtain nanometer silver particle of 5-100 nm size. The nanometer silver particle in solution may be further deposited and washed with sodium hydroxide solution, dried and crushed to obtain nanometer silver particle of 5-100 nm size. The prepared solution may be used in medical article, and prepared nanometer silver powder may be used widely in household appliance, plastic product, paint, etc. The present invention is environment friendly, low in cost and simple in operation, and the prepared nanometer silver particle has extremely powerful antibiotic capacity and wide antibiotic spectrum.

Description

technical field [0001] The invention relates to a preparation method of a broad-spectrum antibacterial nano-silver solution and a nano-silver powder, in particular to a preparation method of a nano-silver solution and a nano-silver powder with a high polymer as a stabilizer. Background technique [0002] At present, most of the antibacterial materials used in the market are organic antibacterial agents, but organic antibacterial agents generally have poor antibacterial effects, and only have a strong anti-mold effect, and there are few organic antibacterial agents that have excellent inhibition on both. Moreover, organic antibacterial agents have poor heat resistance and stability, and their decomposition products and volatiles may be harmful to the human body; thus, inorganic antibacterial agents with strong inhibitory effects on bacteria, especially silver-based antibacterial agents, stand out. Compared with organic antibacterial agents, inorganic antibacterial materials h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): A01N25/10A01N59/16
Inventor 计剑付金红沈家骢
Owner ZHEJIANG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap