Production of ultra-fine crystal hot-rolled ribbed reinforcing rob

A technology of hot-rolled ribbed steel bar and manufacturing method, applied in metal rolling, manufacturing tools, metal rolling and other directions, can solve the problems of unreachable tensile strength, difficult to achieve, difficult to control, etc., and achieve production cost The effect of reducing and promoting the ferrite phase deformation nucleus and satisfying the welding performance

Inactive Publication Date: 2006-03-15
ANYANG IRON & STEEL GRP
View PDF0 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the shortcomings of its research on ultra-fine-grained steel bars are that the research has strict requirements on its deformation temperature, deformation amount, deformation rate, and cooling rate after deformation, which is relatively easy to control for laboratories, but for industrialized large-scale In terms of production, it will be very difficult to control, and it is not easy to achieve
And according to the results of mechanical properties, its performance is only the yield strength of 400Mpa, and the tensile strength is far from the requirements of HRB400 steel bars.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0018] Adopt the method of the present invention to produce ultra-fine-grained reinforced steel technological process: 100 ton converter (electric furnace)——LF refining furnace——150mm continuous casting billet——walking beam type heating furnace—high speed twist-free rolling mill——Stai The Holmore line controls the cooling line. The chemical composition (weight %) of the steel is: C: 0.20%, Si: 0.32%, Mn: 1.49%, Nb: 0.022%. Rolling includes two parts: low temperature controlled rolling and post-rolling controlled cooling. Rolling heating temperature: 1030°C, rolling start temperature: 950-980°C, sizing inlet temperature: 860-880°C; spinning temperature 860-890°C; rolling specification φ8mm, rolling pass 26 passes. After rolling, air cooling is used at the entrance section of the Stelmo line to make the steel undergo rapid phase transformation. The cooling rate is 4.5°C / S. After reaching the phase transformation temperature point, it is then air-cooled, and coils are collected a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

A technology for thermally rolling the superfine-crystal coiled ribbed steel bar used as building material includes such steps as controlled rolling by heating to 980-1100 Deg C., beginning to roll at 930-980 Deg C. and discharging at 860-890 Deg C. and controlled air cooling. Said ribbed steel bar contains C (0.17-0.25 Wt%), Si (0.25-0.80), Mn (1.2-1.6), Nb (0.01-0.025), P (0-0.04), S (0-0.04) and Fe (rest).

Description

technical field [0001] The invention relates to a method for producing hot-rolled ribbed steel wire rod with ultra-fine grain (4-6 μm) above 400Mpa in large-scale industrial production, and belongs to the field of low-alloy steel for construction. Background technique [0002] Grain refinement is one of the most effective ways to improve the strength and toughness of steel materials. On-line control and formation of ultra-fine structures has always been the dream goal of material science and technology workers. The future development direction of steel materials is based on high cleanliness and high uniformity. and ultrafine tissue as the target. In the literature Vol.36.No.8August.2001, Yang Zhongmin and others published the paper "Research on Ultra-fine Grain Critical Austenite Controlled Rolling Process of Ordinary Carbon Steel", through the simulation experiment on the Gleeble-2000 thermal deformation simulator, The effect of process parameters on low-carbon steel Q235 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B21B1/18B21B45/02C22C38/12
Inventor 王子亮李利剑李子林赵自义韦弦范银平曹树卫马志军
Owner ANYANG IRON & STEEL GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap