Cleaning agent for pretreatment of cold-rolling galvanization

A cleaning agent and defoaming agent technology, applied in the field of cleaning agents, can solve problems such as weak buffer capacity, lower quality of cold-rolled galvanized products, short service life of cleaning agents, etc., and achieve wide use temperature range, good cleaning effect, The effect of long service life

Inactive Publication Date: 2006-07-19
武钢集团有限公司
View PDF2 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Its shortcomings: one is that the buffering ability of the alkaline compound and the chelating agent in the formula to the pH value is not strong, resulting in a short service life of the cleaning agent, and when the replacement is not timely, it is easy to cause oil stains to remain on the cold-rolled steel plate; Prevent the formation of iron soap, which may easily cause iron soap to remain on cold-rolled steel sheets, reducing the quality of cold-rolled galvanized products
Its disadvantage: because its formula contains silicate, if the cleaning agent is used before cold-rolled galvanizing, silicon will easily remain on the cold-rolled steel plate after cleaning the cold-rolled steel plate, reducing the quality of cold-rolled galvanized products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Embodiment 1: get sodium hydroxide 40% by weight percentage; Sodium carbonate 22%; Polysodium phosphate 15%; Gluconate 15%; Composite alkyl phosphate surfactant 7%; Polyether type defoamer 1% . After uniformly mixing these raw materials, it can be prepared with tap water, the concentration is 3%, and the cleaning temperature is 70°C. The cleaning agent prepared according to this weight percentage has excellent defoaming performance, and the residual foam height after 10 minutes is ≤1mm; it has good rust resistance and is non-corrosive; it has no flocs and precipitates in hard water; and the water-insoluble matter is less than 1.0 %; no visible residue after rinsing; surface tension ≤ 35mN / m; immersion or spray cleaning of oiled cold-rolled steel sheets, the cleaning efficiency can reach more than 99%.

Embodiment 2

[0028] Embodiment 2: get sodium hydroxide 30% by weight percentage; Sodium carbonate 29%; Polysodium phosphate 28%; Gluconate 5%; Composite alkyl phosphate surfactant 6%; Polyether type defoamer 2% . After uniformly mixing these raw materials, it can be prepared with tap water, the concentration is 2.5%, and the cleaning temperature is 60°C. The cleaning agent prepared according to this weight percentage has excellent defoaming performance, and the residual foam height after 10 minutes is ≤1mm; it has good rust resistance and is non-corrosive; it has no flocs and precipitates in hard water; and the water-insoluble matter is less than 1.0 %; no visible residue after rinsing; surface tension ≤ 35mN / m; immersion or spray cleaning of oiled cold-rolled steel sheets, the cleaning efficiency can reach more than 99%.

Embodiment 3

[0029] Embodiment 3: get sodium hydroxide 40% by weight percentage; Sodium carbonate 20%; Polymeric sodium phosphate 5%; Gluconate 28%; Composite alkyl phosphate surfactant 1%; Polyether type defoamer 6% After uniformly mixing these raw materials, it can be prepared with tap water, the concentration is 3%, and the cleaning temperature is 65°C. The cleaning agent prepared according to this weight percentage has excellent defoaming performance, and the residual foam height after 10 minutes is ≤1mm; it has good rust resistance and is non-corrosive; it has no flocs and precipitates in hard water; and the water-insoluble matter is less than 1.0 %; no visible residue after rinsing; surface tension ≤ 35mN / m; immersion or spray cleaning of oiled cold-rolled steel sheets, the cleaning efficiency can reach more than 99%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
surface tensionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a cleaning agent for cold rolling galvanizing pretreatment, which comprises the following constituents (by weight percentage): sodium-hydroxide 10-50%, sodium carbonate 10-40%, sodium tripolyphosphate 5-30%, glucoheptonates 5-30%, composite alkyl phosphate ester surface active agent 1-7%, and polyether type defoaming agent 1-7%.

Description

technical field [0001] The invention relates to a cleaning agent, in particular to a cleaning agent used for pre-treatment of cold-rolled galvanizing. Background technique [0002] Degreasing and cleaning is an important part of the pre-treatment of cold-rolled galvanizing. Before galvanizing, cold-rolled steel sheets must undergo a surface cleaning process to remove oil particles and other surface residues on the metal surface. Bringing into the cold-rolled galvanizing process will affect the quality of cold-rolled galvanized products. At present, the main cleaning method of the cold-rolled galvanizing production line is alkaline cleaning at a temperature of 70-80°C. Before the present invention, publication number is that CN1548582A " special cleaning agent for cold-rolled steel plate " discloses a kind of cleaning agent that is liquid state. Its shortcomings: one is that the buffering ability of the alkaline compound and the chelating agent in the formula to the pH valu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C23G1/14C23G1/18C23G1/19
Inventor 黄先球卢鹰涂元强石争鸣张万灵刘建容
Owner 武钢集团有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com