Finishing method for nano antibiotic fabric

A kind of antibacterial fabric and fabric technology, which is applied in the treatment of textile materials, spray/jet textile material treatment, liquid/gas/steam textile material treatment, etc., can solve the problems of uneven distribution of antibacterial agents, pollution, high production costs, etc., to achieve Increased bonding fastness, excellent antibacterial ability, and the effect of solving discoloration

Inactive Publication Date: 2006-11-08
DONGHUA UNIV
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a finishing method for nano-antibacterial fabrics to solve the d

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Cotton yarn card (20 s ×16 s , 128 × 60) in 4% water glass aqueous solution, two dipping and two rolling, pressure 0.3MPa, liquid carrying rate 70%, drying in a blast oven at 75°C, then washing and drying; use PG-350 of KUMAS company Spray 10% ammonium sulfate aqueous solution onto the fabric finished by the former with an electric sprayer, dry in a blast oven at 70°C, wash with water, and bake at 70°C for 3 minutes; the fabric has a bath ratio of 40:1 and a concentration of 0.050%. After soaking in the silver nitrate aqueous solution for 30 minutes, it was taken out, baked at 80°C for 3 minutes, washed with water, and finally the finished fabric was dried in an air blast oven at 80°C.

Embodiment 2

[0038] Cotton yarn card (20 s ×16 s , 128 × 60) in 4% water glass aqueous solution, two dipping and two rolling, pressure 0.4MPa, liquid carrying rate 60%, drying in 60 ℃ blast oven, then washing and drying; use PG-350 of KUMAS company Spray 10% ammonium sulfate aqueous solution onto the fabric finished by the former with an electric sprayer, dry it in an air blast oven at 80°C, wash it with water, and bake it at 80°C for 3 minutes; Dip and roll in the silver nitrate aqueous solution, the pressure is 0.3MPa, the liquid-carrying rate is 60%, then rolled up and stacked for 30 minutes, baked at 70°C for 3 minutes, washed with water, and finally dried the finished fabric in a 60°C blast oven Dry.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses finishing method for nanometer antibiotic fabric. By means of sol-gel technology, silica gel is prepared on fabric with water glass of different modulus as precursor and ammonium salt as catalyst and used in padding fabric to introduce silver antibiotic and endow fabric with excellent lasting antibiotic performance. The fabric may have its 99 % over of colibacillus and Staphylococcus aureus killing rate maintained after being washed for 50 times. The finishing process has few influence on the hand feeling, whitenes and physical and mechanical performance of the fabric, uses no adhesive and dispersant, and has less pollution and low cost.

Description

technical field [0001] The invention relates to a finishing method of nano antibacterial fabrics, in particular to a finishing method of nano antibacterial fabrics without using any binder and dispersant. Background technique [0002] Antibacterial materials can be divided into three categories: organic, inorganic metal ion type and semiconductor photocatalytic type. Organic antibacterial materials have great application limitations due to problems such as poor heat resistance and insufficient durability; photocatalytic antibacterial materials are developing rapidly, but they need to further solve their problems such as ultraviolet light dependence and light utilization rate, and are still in the early stage of industrial application; Metal ion antibacterial materials have excellent heat resistance, spectrum antibacterial properties, safety, light resistance and chemical stability, and have a long antibacterial time, which is the mainstream product in the current antibacteri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06B3/18D06B1/02
Inventor 邢彦军戴瑾瑾杨晓君张安秋
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap