Water-based polyurethane and organosilicon, organofluorine copllymerized water-proof air-moisture-permeable antibacterial adhesive coating preparing method

A water-based polyurethane, waterproof and breathable technology, applied in the preparation of organic fluorine copolymer waterproof, breathable, moisture-permeable and antibacterial coating glue, water-based polyurethane and silicone, polyurethane waterproof, breathable and moisture-permeable coating glue, can solve the problem of bacteria in water-based coating glue Infringement and other problems, to achieve the effect of high waterproof, breathable and moisture permeable performance, strong bactericidal effect

Inactive Publication Date: 2007-03-28
江阴市诺科科技有限公司
View PDF0 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But water-based coating adhesive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Add 120g of polyethylene glycol (molecular weight: 1000), 8g of dimethylolsilane, 4g of hydroxyfluorosilicone oil into the flask, vacuum at 100°C for 2 hours, add 8g of dimethylol propionic acid, dissolve it, and cool down to 72°C , add 28g HDI and 6 drops of catalyst DBTDL, keep stirring for 90min, cool down to 63°C, add 7.6g1,4 butanediol, keep stirring for 40min, cool down to 25°C, add 10g of ethylenediamine, and disperse 6g of inorganic silver Add 228 g of silicon oxide water quickly, and stir at high speed for 1 hour to obtain the product. After coating, the antibacterial performance is tested (according to JIS Z2801:2000 standard), and the antibacterial activity value is greater than 4.0.

Embodiment 2

[0022] Add 120g of polypropylene glycol (molecular weight: 1000), 10g of dihydroxyethylsilane, 5g of hydroxyfluorosilicone oil into the flask, vacuumize at 100°C for 2 hours, add 7.8g of dimethylolpropionic acid, dissolve it, and cool down to 75°C. Add 30gIPDI and 6 drops of catalyst DBTDL, keep stirring for 90min. Cool down to 60°C, add 7.5g of 1,4-butanediol, keep stirring for 40min, cool down to 20°C, add 9g of ethylenediamine, quickly add 230g of water dispersed with 6g of inorganic silver-loaded titanium oxide, stir at high speed for 1 hour , get the product. After coating, the antibacterial performance is tested (according to JIS Z2801:2000 standard), and the antibacterial activity value is greater than 4.0.

Embodiment 3

[0024] Add 120g of polyethylene glycol (molecular weight: 800), 9g of dimethylolsilane, 4.5g of hydroxyfluorosilicone oil into the flask, vacuumize at 100°C for 2 hours, add 9g of dimethylolpropionic acid, dissolve, and cool down to 72 ℃, add 28g HDI and 6 drops of catalyst DBTDL, keep stirring for 90min. Cool down to 65°C, add 8.0g of 1,4-butanediol, keep stirring for 40min, cool down to 20°C, add 10g of hexamethylenediamine, quickly add 230g of water dispersed with 8g of inorganic silver-loaded silicon oxide, stir at high speed for 1 hour, get the product. After coating, the antibacterial performance is tested (according to JIS Z2801:2000 standard), and the antibacterial activity value is greater than 4.7.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to aquosity polyurethane, organic silicon, and organic fluorine copolymerization water proof gasper drenching antibiotic coating adhesive preparing method. It includes the following steps: using diisocyanate to react with diatomic alcohol compound, alkyl silicol, hydroxyl group fluoro-silicon oil, dioxy methyl propionic acid to produce performed polymer with -NCO end group, enlarging chain by 1, 4 butylene glycol; using amine to adjust pH value to neutrality; adding de-ionized water contains anti-bacterial agent to stir at high speed; adding water to adjust viscosity. It can be coated at the fabric surface to realize water proof gasper drenching, and kill mold.

Description

technical field [0001] The invention relates to a polyurethane waterproof, breathable, and moisture-permeable coating glue, in particular to a preparation method of a water-based polyurethane, organic silicon, and organic fluorine copolymerized waterproof, breathable, and moisture-permeable antibacterial coating glue. It belongs to the field of organic chemical technology. Background technique [0002] Polyurethane waterproof, breathable and moisture-permeable coating glue is widely used in textile and leather fields, and can endow the coating with special effects of waterproof and moisture permeability. At present, the coating glue of polyurethane is still mainly oily polyurethane, which releases a large amount of harmful organic solvents during production and coating, which is extremely unfriendly to the environment. The new waterborne polyurethane material has great market potential due to the use of non-toxic water as the dispersion medium. But water-based coating adhe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D175/04C09D5/16C09D5/14C08G18/61A01N59/00
Inventor 华明扬
Owner 江阴市诺科科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap