High conductive high strength graphite brick for ultralarge blast furnace, its production technology and application

A high thermal conductivity, graphite brick technology, applied in the field of graphite products, can solve the problems affecting the normal operation of the blast furnace, shorten the service life of the blast furnace, and damage the lining of the blast furnace, and achieve excellent thermal shock resistance, prolong service life, and strong erosion ability. Effect

Inactive Publication Date: 2007-04-18
SINOSTEEL JILIN CARBON +1
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

During the operation of the blast furnace, the above-mentioned areas have been subjected to the impact of heat load in the furnace, temperature fluctuations, etc. for a long time, as well as the erosion and wear of materials and air flow, and the erosion of molten iron and slag, which has damaged the lining of the blast furnace and seriously affected the blast furnace. The normal operation of the blast furnace shortens the service life of the blast furnace

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High conductive high strength graphite brick for ultralarge blast furnace, its production technology and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Add 100kg of pitch coke to 500kg of petroleum coke, and then add 52.2kg of crushed graphite. After crushing, partial grinding, and screening according to a certain particle size, the particle composition and distribution are as follows:

[0038] In mm, 2≤particle size<3 is 6.52kg (1%); 1≤particle size<2 is 71.74kg (11%); 0.5≤particle size<1 is 65.22kg (10%); 0.075≤particle size<0.5 It is 136.95kg (21%); the particle below 0.075 is 371.74kg (57%);

[0039] It can be seen from the drawings that the above-mentioned powders were put into a kneading pot for dry mixing for 30 minutes at a temperature of 105°C. Then add 182.61 kg of medium-temperature coal tar pitch, and carry out wet mixing at the same temperature. The mixing time is 40 minutes, and the temperature of the paste out of the pot is 160 ° C. Then after cooling to about 100°C, put it into the molding machine for molding, the pre-pressing pressure is 16Mpa, the pre-pressing time is 6min, and the volume density of ...

Embodiment 2

[0041] Add 50kg of pitch coke to 250kg of petroleum coke, and then add 22.58kg of crushed graphite. After crushing, partial grinding, and screening according to a certain particle size, the particle composition and distribution are as follows:

[0042] Greater than or equal to 2mm and less than 3mm is 1.61kg (0.5%), greater than or equal to 1mm and less than 2mm is 38.71kg (12%), greater than or equal to 0.5mm and less than 1mm is 35.48kg (11%), greater than or equal to 0.075mm and less than 0.5 mm is 59.68kg (18.5%), and 0.075mm or less is 187.10kg (58%).

[0043] As can be seen from the drawings, the above powders were dry kneaded for 35 minutes at a temperature of 108°C. Then add 93.55 kg of medium-temperature coal tar pitch, carry out wet mixing at the same temperature, the mixing time is 45 minutes, and the temperature of the paste out of the pot is 158°C. Then after cooling to about 100°C, put it into the molding machine for molding, the pre-pressing pressure is 17Mpa, ...

Embodiment 3

[0044] Embodiment 3 (application of high thermal conductivity, high strength small block graphite bricks in super large blast furnace)

[0045] The high thermal conductivity and high strength graphite brick of the present invention is used for the application of the ultra-large blast furnace lining. The dense copper cooling plate + the above-mentioned small pieces of high thermal conductivity and high strength graphite bricks of different specifications are placed in the area above the tuyere of the blast furnace according to the traditional method. Build the furnace lining structure and form a high thermal conductivity layer.

[0046] The blast furnace lining is composed of dense copper cooling plates and the high thermal conductivity and high strength small graphite bricks of the present invention. In this way, the copper cooling plate with high cooling strength (the copper plate cooling layer is cooled with cooling water) and the small graphite bricks together form a high t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a high heat conductivity and high strength graphite brick for super-large blast furnace. It is made up by using (by wt%) 92%-94% of mixed coke formed from petroleum coke and pitch coke and 6%-8% of powdered graphite through the processes of pulverizing, grinding, screening, wet kneading, moulding, roasting and graphitization.

Description

technical field [0001] The invention belongs to the field of graphite products, and relates to a graphite brick, in particular to a high-thermal conductivity and high-strength graphite brick for a super-large blast furnace, a preparation method and an application of the graphite brick. Background technique [0002] "Brick" for blast furnace refers to a kind of refractory material used for the lining of blast furnace. According to its basic physical and chemical properties, it can be divided into different materials and defined as different names. High-alumina bricks mainly made of alumina raw materials, silicon carbide bricks made of silicon carbide raw materials; graphite bricks made of carbonaceous raw materials and formed after high-temperature graphitization. At present, in domestic ironmaking blast furnaces, only large graphite bricks are built at the bottom of the furnace. This kind of graphite brick is obtained by crushing petroleum coke to a c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/52C04B35/66
Inventor 张建华姜华贾文涛王立辉孙权甘菲芳王永淮张济发王建平
Owner SINOSTEEL JILIN CARBON
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap