Injection molding of polymeric material

a polymer material and injection molding technology, applied in the field of polymer structural foam processing, can solve problems such as less than ideal appearan

Inactive Publication Date: 2005-07-28
TREXEL
View PDF69 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0013] According to another aspect of the invention a system is provided having a molding chamber constructed and arranged to contain nucleated polymeric material at an elevated pressure in order to prevent cell growth at the elevated pressure. The pressurized molding chamber can be fluidly or mechanically pressurized in order to contain the nucleated polymeric material at such an elevated pressure. After reduction of the pressure on the pressurized molding chamber, the polymeric material can solidify the shape of a desired microcellular polymeric article as the molding chamber is constructed and arranged to have such an interior shape.

Problems solved by technology

Under other, typically more violent foaming conditions, the cells rupture or become interconnected and an open-cell material results.
While EPS and EPP are useful products for many applications, they can have a less than ideal appearance.
A portion of the extrusion barrel is heated so that as the mixture flows through the barrel, a thermodynamic instability is created, thereby creating sites of nucleation in the molten polymeric material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Injection molding of polymeric material
  • Injection molding of polymeric material
  • Injection molding of polymeric material

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0169] A two stage injection molder (Engel manufacture) was constructed with a 32:1 l / d, 40 mm plasticizing unit which feeds melted polymer into a 40 mm diameter plunger. The plunger and plasticizing units were connected by a spring loaded ball check joiner assembly. The plunger was able to inject into a mold through a typical pneumatically driven shut-off nozzle. Injection of supercritical CO2 was accomplished by placing at approximately 16 to 20 diameters from the feed section an injection system that included one radially positioned port containing 176 orifices of 0.02 inch diameter. The injection system included an actuated control valve to meter a mass flow rate of blowing agent at rates from 0.2 to 12 lbs / hr.

[0170] The plasticator was equipped with a two stage screw including a conventional first stage feed, barrier, transition, and metering section, followed by a multi-flighted mixing section for blowing agent homogenization. The barrel was fitted with heating / cooling bands....

example 2

Injection Molding Microcellular Polystyrene

[0172] The molding machine as described in example 1 was used to mold microcellular polystyrene plaques. Polystyrene pellets (Novacor 2282, 11 M.I.) were fed into the plasticator and, in most cases, mixed with blowing agent to form a single-phase solution, then nucleated by injection into a 5×11×0.050 inch, center gated plaque mold. Injection occurred through a cold sprue. Injection rate was varied to determine the relationship between the processing variables and cell size and weight reduction. Cell size was controlled to under 30 microns and weight reduction as high as 20%. See Tables 1 and 2 and corresponding FIGS. 10-15.

TABLE 1Effect of Injection Speed on Cell Size and Weight ReductionBlowingInjectionAgeWeightSpeedCell SizentReduction(“ / sec)(microns)(%)(%)FIG.11No Cells11.91110510011.9111141011.9191221011.9181313011.912—

[0173]

TABLE 2Effect of Gas Concentration on Cell Size and Weight ReductionMelt temperature = 160° C.Mold Temperatur...

example 3

Injection Molding Microcellular Polyethylene Terephthalate

[0174] The injection molding machine described in example 1 was used to mold PET (Eastman, 0.95 IV) into a 5×11×0.200 inch cavity after drying for four hours at 350 F. The melt temperature was 550 F, the mold temperature was 151 F and was injected with 12% CO2. The melt pressurization pressure was maintained at 3000 psi and the injection speed was 5.0 inches per second.

[0175] The weight reduction was 30% and the cell size was 30 to 40 microns in diameter.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
average cell sizeaaaaaaaaaa
mass flow rateaaaaaaaaaa
mass flow rateaaaaaaaaaa
Login to View More

Abstract

Injection molding systems and methods useful for making microcellular foamed materials are provided as well as microcellular articles. Pressure drop rate and shear rate are important features in some embodiments, and the invention provides systems for controlling these parameters in an injection molding system. Another aspect involves an injection molding system including a nucleator that is upstream of a pressurized mold. Another aspect involves an extrusion system with the reciprocating screw for forming a single phase solution of non-nucleated blowing agent and polymeric material. Another aspect involves very thin walled microcellular material and very thin walled polymeric material. Another aspect provides a method for producing high weight reductions in very thin-walled parts with surfaces that have no noticeable differences from non-foamed parts.

Description

RELATED APPLICATIONS [0001] This application is a divisional of U.S. application Ser. No. 09 / 335,946, filed Jun. 18, 1999, which is a continuation-in-part of U.S. application Ser. No. 09 / 185,987, filed Nov. 4, 1998, which is a continuation-in-part of U.S. application Ser. No. 09 / 008,171, filed Jan. 16, 1998, which claims the benefit under Title 35, U.S.C. § 19(e) of U.S. provisional application Ser. No. 60 / 068,350, filed Dec. 19, 1997, and U.S. provisional application Ser. No. 60 / 035,631, filed Jan. 16, 1997, all of which applications are incorporated herein by reference.FIELD OF THE INVENTION [0002] The present invention relates generally to polymeric structural foam processing, and more particularly to microcellular structural foams and systems and methods of manufacture. BACKGROUND OF THE INVENTION [0003] Structural foamed materials are known, and can be produced by injecting a physical blowing agent into a molten polymeric stream, dispersing the blowing agent in the polymer to f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): B29C44/00B29C44/04B29C44/34B29C48/03B29C48/15B29C48/29B29C48/295B29C48/38B29C48/45B29C48/74
CPCB29C44/00B29K2105/04B29C44/0492B29C44/3446B29C44/3469B29C47/0004B29C47/0009B29C47/004B29C47/0042B29C47/02B29C47/0876B29C47/1063B29C47/368B29C47/44B29C47/74B29C2947/92019B29C2947/92114B29C2947/922B29C2947/92209B29C2947/9238B29C2947/924B29C2947/92409B29C2947/92428B29C2947/92447B29C2947/92657B29K2105/0005B29C44/0461B29C2948/92209B29C2948/924B29C2948/92409B29C48/15B29C48/29B29C48/022B29C48/03B29C48/0011B29C48/0012B29C48/2694B29C48/295B29C48/388B29C48/45B29C48/74B29C2948/92019B29C2948/92114B29C2948/922B29C2948/9238B29C2948/92428B29C2948/92447B29C2948/92657Y10T428/249953
Inventor PIERICK, DAVID E.ANDERSON, JERE R.CHA, SUNG WOONCHEN, LIQINSTEVENSON, JAMES F.LAING, DANA E.
Owner TREXEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com